RESUMEN
Despite the fact that GeTe is known to be a very interesting material for applications in thermoelectrics and for phase-change memories, the knowledge on its low-temperature transport properties is only limited. We report on phase-coherent phenomena in the magnetotransport of GeTe nanowires. From universal conductance fluctuations measured on GeTe nanowires with Au contacts, a phase-coherence length of about 280 nm at 0.5 K is determined. The distinct phase-coherence is confirmed by the observation of Aharonov-Bohm type oscillations for parallel magnetic fields. We interpret the occurrence of these magnetic flux-periodic oscillations by the formation of a tubular hole accumulation layer. For Nb/GeTe-nanowire/Nb Josephson junctions we obtained a critical current of 0.2 µA at 0.4 K. By applying a perpendicular magnetic field the critical current decreases monotonously with increasing field, whereas in a parallel field the critical current oscillates with a period of the magnetic flux quantum confirming the presence of a tubular hole channel.
RESUMEN
Scaling information bits to ever smaller dimensions is a dominant drive for information technology (IT). Nanostructured phase change material emerges as a key player in the current green-IT endeavor with low power consumption, functional modularity, and promising scalability. In this work, we present the demonstration of microwave AC voltage induced phase change phenomenon at â¼3 GHz in single Sb2Te3 nanowires. The resistance change by a total of 6-7 orders of magnitude is evidenced by a transition from the crystalline metallic to the amorphous semiconducting phase, which is cross-examined by temperature dependent transport measurement and high-resolution electron microscopy analysis. This discovery could potentially tailor multistate information bit encoding and electrical addressability along a single nanowire, rendering technology advancement for neuro-inspired computing devices.
RESUMEN
We report on low-temperature transport and electronic band structure of p-type Sb2Te3 nanowires, grown by chemical vapor deposition. Magnetoresistance measurements unravel quantum interference phenomena, which depend on the cross-sectional dimensions of the nanowires. The observation of periodic Aharonov-Bohm-type oscillations is attributed to transport in topologically protected surface states in the Sb2Te3 nanowires. The study of universal conductance fluctuations demonstrates coherent transport along the Aharonov-Bohm paths encircling the rectangular cross-section of the nanowires. We use nanoscale angle-resolved photoemission spectroscopy on single nanowires (nano-ARPES) to provide direct experimental evidence on the nontrivial topological character of those surface states. The compiled study of the bandstructure and the magnetotransport response unambiguosly points out the presence of topologically protected surface states in the nanowires and their substantial contribution to the quantum transport effects, as well as the hole doping and Fermi velocity among other key issues. The results are consistent with the theoretical description of quantum transport in intrinsically doped quasi-one-dimensional topological insulator nanowires.
RESUMEN
Single crystalline p-type CdTe:Sb nanobelts were fabricated using an Au-catalyzed chemical vapor deposition method. Low carrier concentration and low mobility even at high Sb incorporation manifest compensation in the system. From cross examination of temperature-dependent charge transport and photoluminescence measurements, two major acceptor levels induced by Sb doping are determined: a shallow level attributed to substitutional Sb dopants without lattice relaxation and an associated deeper level resulted from large lattice relaxation-AX centers. Persistent photoconductivity and hysteresis photoconductance under the thermal cycle elucidate the nature of AX centers. This comprehensive investigation of the impurity levels in the material system is essential for the design and development of nanoelectronic devices based on the CdTe nanostructures.
RESUMEN
High-quality CdS nanowires with uniform Sn doping were synthesized using a Sn-catalyzed chemical vapor deposition method. X-ray diffraction and transmission electron microscopy demonstrate the single crystalline wurtzite structure of the CdS/Sn nanowires. Both donor and acceptor levels, which originate from the amphoteric nature of Sn in II-VI semiconductors, are identified using low-temperature microphotoluminescence. This self-compensation effect was cross examined by gate modulation and temperature-dependent electrical transport measurement. They show an overall n-type behavior with relatively low carrier concentration and low carrier mobilities. Moreover, two different donor levels due to intrinsic and extrinsic doping could be distinguished. They agree well with both the electrical and optical data.
RESUMEN
Tin-doped cadmium sulfide nanowires reveal donor-acceptor pair transitions at low-temperature photoluminescence and furthermore exhibit ideal resonator morphology appropriate for lasing at continuous wave pumping. The continuous wave lasing mode is proven by the evolution of the emitted power and spectrum with increasing pump intensity. The high temperature stability up to 120 K at given pumping power is determined by the decreasing optical gain necessary for lasing in an electron-hole plasma.
RESUMEN
We have fabricated indium-doped ZnO (IZO) nanowires (NWs) and carried out four-probe electrical-transport measurements on two individual NWs with geometric diameters of ≈70 and ≈90 nm in a wide temperature T interval of 1-70 K. The NWs reveal overall charge conduction behavior characteristic of disordered metals. In addition to the T dependence of resistance R, we have measured the magnetoresistance (MR) in magnetic fields applied either perpendicular or parallel to the NW axis. Our R(T) and MR data in different T intervals are consistent with the theoretical predictions of the one- (1D), two- (2D) or three-dimensional (3D) weak-localization (WL) and the electron-electron interaction (EEI) effects. In particular, a few dimensionality crossovers in the two effects are observed. These crossover phenomena are consistent with the model of a 'core-shell-like structure' in individual IZO NWs, where an outer shell of thickness t (~15-17 nm) is responsible for the quantum-interference transport. In the WL effect, as the electron dephasing length Lφ gradually decreases with increasing T from the lowest measurement temperatures, a 1D-to-2D dimensionality crossover takes place around a characteristic temperature where Lφ approximately equals d, an effective NW diameter which is slightly smaller than the geometric diameter. As T further increases, a 2D-to-3D dimensionality crossover occurs around another characteristic temperature where Lφ approximately equals t (
RESUMEN
We have measured the intrinsic electrical resistivities, rho(T), of three individual single-crystalline ZnO nanowires (NWs) from 320 down to 1.3 K. The NWs were synthesized via carbon thermal chemical vapor deposition and the four-probe Pt contacting electrodes were made by the focused-ion-beam technique. Analysis of the overall temperature behavior of rho(T) confirms that the charge transport processes in natively doped ZnO NWs are due to a combination of the thermal activation conduction and the nearest-neighbor hopping conduction processes, as proposed and explained in a recent work (Chiu et al 2009 Nanotechnology 20 015203) where the ZnO NWs were grown by a different thermal evaporation method and the four-probe electrodes were made by the electron-beam lithography technique. Taken together, the observations of these two complementary studies firmly establish that the electrical conduction mechanisms in natively doped ZnO NWs are unique and now satisfactorily understood.