This paper reports on the preparation and the characterization of structural, electrical and thermoelectric properties of nanocomposite films formed from three-dimensional networks of polycrystalline bismuth (Bi) nanowires (NWs). The samples were fabricated by electrodeposition within polycarbonate (PC) templates with crossed cylindrical nanopores, yielding self-supported networks of Bi crossed nanowires (CNWs) with mean diameter values ranging from 23 nm to 230 nm. Temperature changes in electrical resistance and thermopower were studied by considering electric and thermal currents flowing in the plane of the films. While the values of the Seebeck coefficient are close to those of polycrystalline Bi for diameters greater than 100 nm, a progressive decrease in thermopower appears at smaller diameters, due to an increasing contribution of surface charge carriers as the diameter decreases. Transverse thermoelectricity based on the Nernst effect was also demonstrated on a network of Bi CNWs 230 nm in diameter. Such hierarchical architectures based on Bi CNWs are extremely robust, offering a reliable solution for the next generation of flexible thermoelectric devices.
RESUMEN
Thermoelectric energy conversion based on flexible materials has great potential for applications in the fields of low-power heat harvesting and solid-state cooling. Here, we show that three-dimensional networks of interconnected ferromagnetic metal nanowires embedded in a polymer film are effective flexible materials as active Peltier coolers. Thermocouples based on Co-Fe nanowires exhibit much higher power factors and thermal conductivities near room temperature than other existing flexible thermoelectric systems, with a power factor for Co-Fe nanowire-based thermocouples of about 4.7 mW/K2m at room temperature. The effective thermal conductance of our device can be strongly and rapidly increased by active Peltier-induced heat flow, especially for small temperature differences. Our investigation represents a significant advance in the fabrication of lightweight flexible thermoelectric devices, and it offers great potential for the dynamic thermal management of hot spots on complex surfaces.
RESUMEN
Results of measurements on the thermoelectric power of 45 nm diameter interconnected nanowire networks consisting of pure Fe, dilute FeCu and FeCr alloys and Fe/Cu multilayers are presented. The thermopower values of Fe nanowires are very close to those found in bulk materials, at all temperatures studied between 70 and 320 K. For pure Fe, the diffusion thermopower at room temperature, estimated to be around - 15 [Formula: see text]V/K from our data, is largely supplanted by the estimated positive magnon-drag contribution, close to 30 [Formula: see text]V/K. In dilute FeCu and FeCr alloys, the magnon-drag thermopower is found to decrease with increasing impurity concentration to about 10 [Formula: see text]V/K at 10[Formula: see text] impurity content. While the diffusion thermopower is almost unchanged in FeCu nanowire networks compared to pure Fe, it is strongly reduced in FeCr nanowires due to pronounced changes in the density of states of the majority spin electrons. Measurements performed on Fe(7 nm)/Cu(10 nm) multilayer nanowires indicate a dominant contribution of charge carrier diffusion to the thermopower, as previously found in other magnetic multilayers, and a cancellation of the magnon-drag effect. The magneto-resistance and magneto-Seebeck effects measured on Fe/Cu multilayer nanowires allow the estimation of the spin-dependent Seebeck coefficient in Fe, which is about - 7.6 [Formula: see text]V/K at ambient temperature.
RESUMEN
A network of silver nanowires (Ag-NWs) is grown by electrodeposition in a nanoporous membrane with interconnected nanopores. This bottom-up approach fabrication method gives a conducting network with a 3D architecture and a high density of Ag-NWs. The network is then functionalized during the etching process, which leads to a high initial resistance as well as memristive behavior. The latter is expected to arise from the creation and the destruction of conducting silver filaments in the functionalized Ag-NW network. Moreover, after several cycles of measurement, the resistance of the network switches from a high-resistance regime in the GΩ range with tunnel conduction to a low-resistance regime presenting negative differential resistance in the kΩ range.
RESUMEN
The versatility of the template-assisted electrodeposition technique to fabricate complex three-dimensional networks made of interconnected nanowires allows one to easily stack ferromagnetic and non-magnetic metallic layers along the nanowire axis. This leads to the fabrication of unique multilayered nanowire network films showing giant magnetoresistance effect in the current-perpendicular-to-plane configuration that can be reliably measured along the macroscopic in-plane direction of the films. Moreover, the system also enables reliable measurements of the analogous magneto-thermoelectric properties of the multilayered nanowire networks. Here, three-dimensional interconnected NixFe1-x/Cu multilayered nanowire networks (with 0.60≤x≤0.97) are fabricated and characterized, leading to large magnetoresistance and magneto-thermopower ratios up to 17% and -25% in Ni80Fe20/Cu, respectively. A strong contrast is observed between the amplitudes of magnetoresistance and magneto-thermoelectric effects depending on the Ni content of the NiFe alloys. In particular, for the highest Ni concentrations, a strong increase in the magneto-thermoelectric effect is observed, more than a factor of 7 larger than the magnetoresistive effect for Ni97Fe3/Cu multilayers. This sharp increase is mainly due to an increase in the spin-dependent Seebeck coefficient from -7 µV/K for the Ni60Fe40/Cu and Ni70Fe30/Cu nanowire arrays to -21 µV/K for the Ni97Fe3/Cu nanowire array. The enhancement of the magneto-thermoelectric effect for multilayered nanowire networks based on dilute Ni alloys is promising for obtaining a flexible magnetic switch for thermoelectric generation for potential applications in heat management or logic devices using thermal energy.
RESUMEN
Electrochemical deposition of interconnected nanowires and nanotubes made of ferromagnetic metals into track-etched polycarbonate templates with crossed nanochannels has been revealed suitable for the fabrication of mechanically stable three-dimensional magnetic nanostructures with large surface area. These 3D networks embedded into flexible polymer membranes are also planar and lightweight. This fabrication technique allows for the control of the geometric characteristics and material composition of interconnected magnetic nanowire or nanotube networks, which can be used to fine-tune their magnetic and magneto-transport properties. The magnetostatic contribution to the magnetic anisotropy of crossed nanowire networks can be easily controlled using the diameter, packing density, or angle distribution characteristics. Furthermore, the fabrication of Co and Co-rich NiCo alloy crossed nanowires with textured hcp phases leads to an additional significant magnetocrystalline contribution to the magnetic anisotropy that can either compete or add to the magnetostatic contribution. The fabrication of an interconnected nanotube network has also been demonstrated, where the hollow core and the control over the tube wall thickness add another degree of freedom to control the magnetic properties and magnetization reversal mechanisms. Finally, three-dimensional networks made of interconnected multilayered nanowire with a succession of ferromagnetic and non-magnetic layers have been successfully fabricated, leading to giant magnetoresistance responses measured in the current-perpendicular-to-plane configuration. These interconnected nanowire networks have high potential as integrated, reliable, and stable magnetic field sensors; magnetic devices for memory and logic operations; or neuromorphic computing.
RESUMEN
Recently, interconnected nanowire networks have been found suitable as flexible macroscopic spin caloritronic devices. The 3D nanowire networks are fabricated by direct electrodeposition in track-etched polymer templates with crossed nano-channels. This technique allows the fabrication of crossed nanowires consisting of both homogeneous ferromagnetic metals and multilayer stack with successive layers of ferromagnetic and non-magnetic metals, with controlled morphology and material composition. The networks exhibit extremely high, magnetically modulated thermoelectric power factors. Moreover, large spin-dependent Seebeck coefficients were directly extracted from experimental measurements on multilayer nanowire networks. This work provides a simple and cost-effective way to fabricate large-scale flexible and shapeable thermoelectric devices exploiting the spin degree of freedom.
RESUMEN
NiFe alloy and NiFe/Cu multilayered nanowire (NW) networks were grown using a template-assisted electrochemical synthesis method. The NiFe alloy NW networks exhibit large thermopower, which is largely preserved in the current perpendicular-to-plane geometry of the multilayered NW structure. Giant magneto-thermopower (MTP) effects have been demonstrated in multilayered NiFe/Cu NWs with a value of 25% at 300 K and reaching 60% around 100 K. A large spin-dependent Seebeck coefficient of -12.3 µV/K was obtained at room temperature. The large MTP effects demonstrate a magnetic approach to control thermoelectric properties of flexible devices based on NW networks.