RESUMEN
OBJECTIVE: Membrane sterility is very necessary considering its function as an implant material. Therefore, this research aims to determine the dose of gamma-ray irradiation for the sterilization of polyvinyl alcohol (PVA)-collagen-chitosan composite membranes used as regenerative surgery materials. MATERIALS AND METHODS: A total of 100 pieces of the composite membranes were prepared in a size of 2.0 × 1.5 cm by mixing 7.5% PVA, 3% collagen, and 2% chitosan using the film casting method in three batches. Furthermore, the bioburden test was performed to determine the initial microbial count in the sample by following ISO 11737-1. The results were used to ascertain the dose of gamma-ray irradiation on the sample according to ISO 11137-2. The dose verification test was then performed at the sterility assurance level 10-6. RESULTS: The average result of the bioburden test from three batches was 6.6 colony forming unit; hence, the verification dose was 4.8 kGy. In the verification dose test, since there was only one contaminated sample, the sterility dose test was continued. CONCLUSION: The sterile gamma-ray irradiation dose for PVA-collagen-chitosan composite membrane was 17.1 kGy.
RESUMEN
Dental implant is a material used in replacing missing teeth. The osseointegration process of dental implants will be affected by the macrodesign of the fixtures. This study aimed to review the dental implant macrodesign in the past 10 years. This study was conducted in a systematic review method using two electronic databases (PUBMED and Science Direct). Only randomized controlled trials (RCTs) published in the last 10 years were used for this review. All the search results were filtered using Preferred Reporting Items for Systematic Reviews And Meta-Analyses and should fulfill some predefined inclusion criteria. The last step was to assess the methodological quality of the studies using the JBI Checklist for RCT. The search identified 357 studies with only 23 that going through full-text analysis, resulting in 14 articles included in the review. In total, 19 different implant brands were used in 12 different countries. Dental implant macrodesigns were divided into collar design, implant shape, thread geometry, and platform design. The macrodesign features of the implant were mostly developed in the variation of thread geometry and collar design.
RESUMEN
OBJECTIVE: The aim of this study was to evaluate the effect of gamma-ray irradiation on the physical, mechanical, and morphological characteristics of the polyvinyl alcohol (PVA)-collagen-chitosan membranes as a guided tissue regeneration membrane material. MATERIAL AND METHOD: The membrane was fabricated by mixing PVA, collagen, and chitosan using the film casting method. PVA-collagen-chitosan membranes were irradiated with various radiation dose (0, 15, and 25 kGy). Furthermore, it is characterized using Fourier-transform infrared (FTIR) for functional group identification, morphological test was performed using scanning electron microscopy (SEM), and mechanical properties (i.e., tensile strength and elongation) were evaluated using universal testing machine and swelling studies. STATISTICAL ANALYSIS: Statistical analysis was performed based on analysis of variance and post hoc with p-value < 0.05. RESULT: The FTIR spectrum shows various peaks of functional groups from the PVA-collagen-chitosan membrane. The result of the statistical analysis show changes in tensile strength (p = 0.0004) and membrane elongation (p = 0.000451) at different radiation doses of 0, 15, and 25 kGy. The membrane absorption obtains p-value of 0.0193, while the SEM results show that the PVA-collagen-chitosan membrane homogeneously mixed. CONCLUSION: There is an effect of gamma-ray irradiation on tensile strength, elongation, and water absorption of the membranes. Increasing the radiation dose increases the value of tensile strength, while elongation and absorption of the membrane decrease. The PVA-collagen-chitosan membrane has the potential to develop as an alternative membrane for guided tissue regeneration.
RESUMEN
Aim: This study aims to evaluate the clinical assessment results of periimplant soft tissue with morse taper (internal abutment connection). Methods: The study was conducted using a rapid review by searching the articles from PubMed NCBI and Cochrane by using keywords. All articles were selected by the year, duplication, title, abstract, full-text, and finally, all selected articles were processed for final review. Following clinical parameters were included; Periimplant Probing Pocket Depth (PPD), Plaque Score (PS), modified Plaque Index (mPI), Mucosal Thickness (MTh), Gingival Height (GH), periimplant mucosal zenith, Pink Esthetic Score (PES), Bleeding On Probing (BOP), Sulcus Bleeding Index (SBI), and modified Gingival Index (mGI). Results: 9 selected articles were obtained from the initial literature searching count of 70 articles. The overall samples included 326 morse taper implants. Based on the evaluation, 3 out of 4 articles reported pocket depth < 4 mm, no bleeding was reported in 2 out of 4 articles. 4 out of 4 articles reported low plaque accumulation, low soft tissue recession was reported in 3 out of 3 articles, and 4 out of 4 articles reported acceptable PES values. Conclusion: The evaluations indicate that the morse taper (internal abutment connection) has favorable assessment results based on various clinical parameters