Photoelectrocatalytic degradation of benzoic acid using Au doped TiO2 thin films.

Highly transparent pure and Au doped TiO2 thin films are successfully deposited by using simple chemical spray pyrolysis technique. The effect of Au doping onto the structural and physicochemical properties has been investigated. The PEC study shows that, both short circuit current (Isc) and open circuit voltage (Voc) are (Isc=1.81mA and Voc=890mV) relatively higher at 3at.% Au doping percentage. XRD study shows that the films are nanocrystalline in nature with tetragonal crystal structure. FESEM images show that the film surface covered with a smooth, uniform, compact and rice shaped nanoparticles. The Au doped thin films exhibit indirect band gap, decreases from 3.23 to 3.09eV with increase in Au doping. The chemical composition and valence states of pure and Au doped TiO2 films are studied by using X-ray photoelectron spectroscopy. The photocatalytic degradation effect is 49% higher in case 3at.% Au doped TiO2 than the pure TiO2 thin film photoelectrodes in the degradation of benzoic acid. It is revealed that Au doped TiO2 can be reused for five cycles of experiments without a requirement of post-treatment while the degradation efficiency was retained.

Visible light catalysis of rhodamine B using nanostructured Fe(2)O(3), TiO(2) and TiO(2)/Fe(2)O(3) thin films.

The Fe(2)O(3), TiO(2) and TiO(2)/Fe(2)O(3) composite films are deposited using spray pyrolysis method onto glass and FTO coated substrates. The structural, morphological, optical and photocatalytic properties of Fe(2)O(3), TiO(2) and TiO(2)/Fe(2)O(3) thin films are studied. XRD analysis confirms that films are polycrystalline with rhombohedral and tetragonal crystal structures for Fe2O3 and TiO(2) respectively. The photocatalytic activity was tested for the degradation of Rhrodamine B (Rh B) in aqueous medium. The rate constant (-k) was evaluated as a function of the initial concentration of species. Substantial reduction in concentrations of organic species was observed from COD and TOC analysis. Photocatalytic degradation effect is relatively higher in case of the TiO(2)/Fe(2)O(3) than TiO(2) and Fe(2)O(3) thin film photoelectrodes in the degradation of Rh B and 98% removal efficiency of Rh B is obtained after 20min. The photocatalytic experimental results indicate that TiO(2)/α-Fe(2)O(3) photoelectrode is promising material for removing of water pollutants.

Photoelectrocatalytic decolorization and degradation of textile effluent using ZnO thin films.

Zinc oxide (ZnO) thin films have been successfully deposited onto fluorine doped tin oxide coated glass at substrate temperature of 400 °C and used as electrode in photoelectrocatalytic reactor. The untreated textile effluent was circulated through photoelectrocatalytic reactor under UVA illumination for the decolorization and degradation. Textile effluent was decolorized by 93% within 3h at room temperature with significant reduction in COD (69%). High performance liquid chromatography (HPLC) and Fourier transform infrared spectroscopy (FTIR) analysis of samples before and after decolorization confirmed the degradation of dyes molecules from textile effluent into simpler oxidizable products. Phytotoxicity study revealed reduction in toxic nature of textile effluent after treatment.