Biphenyl-rGO composite room temperature gas sensor for enhanced amine sensing.

Amines, which are classified as volatile organic compounds (VOCs), serve a variety of purposes in the fields of environmental monitoring, food safety, and healthcare diagnosis. The present technique for detecting amine levels involves sophisticated setups and bulky equipment. Here. In this study, a chemoresistive gas sensor is developed that is cost-effective and easy to operate at room temperature (RT). The sensor is designed specifically for the detection of Ammonia, dimethylamine (DMA), trimethylamine (TMA), and total volatile basic nitrogen (TVB-N). Using biphenyl-reduced graphene oxide (B-rGO) composite gas sensors effectively addresses the issues of low sensitivity-selectivity and long-term instability commonly observed in conventional amine sensors. B-rGO sensor produced sensitivity of ∼3500 and selectivity above 30 for TVB-N sensing. The sensor is stable for temperature fluctuations below 50 °C and shows stable sensing response for period of over 3 months. A Chemoresistive B-rGO sensor was developed using an ultrasonic spray deposition system with optimized flow rate of 50 mL/h. Rapid evaporation of solvent using hot plate has resulted in unique morphology for B-rGO film sensors. The highest sensitivity, ∼836, is obtained for 100 ppm of ammonia with ammonia > DMA > TMA as a sensitivity order. B-rGO showed almost seven times higher amine sensitivity than rGO which highlights the importance of biphenyl in the B-rGO composite. Sensor calibration curve has been presented in the study to understand change in the sensitivity of sensor with increasing analyte gas concentration. The calibration curve has an average R-squared value of 0.98.

Polyethylene glycol embedded reduced graphene oxide supramolecular assemblies for enhanced room-temperature gas sensors.

Herein, we present the gas-dependent electrical properties of a reduced graphene oxide nanocomposite. The reduced graphene oxide (rGO) was synthesized by reducing GO with sodium borohydride (NaBH4). As-synthesized rGO was dispersed in DI water containing 1, 2, 3, 4, and 5 wt% polyethylene glycol (PEG) to prepare PEG-rGO supramolecular assemblies. The successful preparation of supramolecular assemblies was verified by their characterization using XRD, FESEM, EDS, TEM, FTIR, and Raman spectroscopy. At room temperature, the gas-dependent electrical properties of these supramolecular assemblies were investigated. The results showed that sensors composed of PEG-rGO supramolecular assemblies performed better against benzene and methanol at 3% and 4% PEG, respectively. However, high selectivity and a wide range of activation energies (∼1.64-1.91 eV) were observed for H2 gas for 4% PEG-modified supramolecular assemblies. The PEG-rGO supramolecular assemblies may be an excellent candidate for constructing ultrahigh-performance gas sensors for a variety of applications due to their high sensitivity and selectivity.

A NiS2/C composite as an innovative anode material for sodium-ion batteries: ex situ XANES and EXAFS studies to investigate the sodium storage mechanism.

The successful deployment of sodium-ion batteries (SIBs) requires high-performance sustainable and cost-effective anode materials having a high current density. In this regard, sodium disulphide (NiS2) has been prepared as a composite with activated carbon (C) using a facile hydrothermal synthesis route in the past. The X-ray diffraction pattern of the as-prepared NiS2/C composite material shows well-defined diffraction peaks of NiS2. Most carbonaceous materials are amorphous, and the Brunauer-Emmett-Teller (BET) study shows that the surface area is close to 148 m2 g-1. At a current density of 50 mA g-1, the NiS2/C composite exhibits a high capacity of 480 mA h g-1 during the initial cycle, which subsequently decreases to 333 mA h g-1 after the completion of the 100th cycle. The NiS2/C composite electrode provides an exceptional rate capability by delivering a capacity of 270 mA h g-1 at a high current density of 2000 mA g-1, suggesting the suitability of the NiS2/C composite for SIBs. Ex situ X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) analyses at the Ni K-edge have been used to examine the type of chemical bonding present in the anode and also how it changes during electrochemical redox cycling. The understanding of the sodium storage mechanism is improved by the favorable results, which also offer insights for developing high-performance electrode materials for rechargeable SIBs.

Polyvinylpyrrolidone-Capped Silver Nanoparticles for Highly Sensitive and Selective Optical Fiber-Based Ammonium Sensor.

Herein, aqueous ammonium sensing characteristics of polyvinylpyrrolidone (PVP) capped silver nanoparticles (Ag-NPs) coated optical fiber-based sensors are presented. The PVP-capped Ag-NPs were prepared using cold and modified polyol synthesis methods. Aqueous ammonium detection was carried out by the surface plasmon resonance (SPR) effect observed in the Ag-NPs coated optical fiber system. The effect of cold and modified polyol synthesis methods on optical sensing performance was studied. The optical fiber cladding was modified with PVP-capped Ag-NPs according to the standard protocol for sensing investigation. The probe sensing response was analyzed for varying concentrations of ammonium ions on red, green, and blue LEDs. The sensor characteristics, viz., sensing response, repeatability, calibration curve, and ambient light effect, were investigated for PVP capped Ag-NPs coated optical fiber-based sensor. The PVP capped Ag-NPs synthesized via the polyol synthesis method showed a detection limit of 48.9 mM, 1.33 mV/M sensitivity, and an excellent linear relationship (R2 = 0.9992) between voltage and ammonium ion concentration in the range of 0.054-13.4 M concentration. On the other hand, PVP capped Ag-NPs synthesized using the cold synthesis method showed a detection limit of 159.4 mM, a sensitivity of 0.06 mV/M, and a poor linear relationship (R2 = 0.4588) between voltage and ammonium ion concentration in the range of 0.054-13.4 M concentration. The results indicate that the PVP-capped Ag-NPs synthesized using the polyol synthesis method exhibit enhanced ammonium ion sensing compared to the cold synthesis method.