RESUMEN
Single wall carbon nanotubes (SWCNTs) were grown on either sized or desized carbon fabric in a self-designed reactor by Pulsed Laser Deposition (PLD). The uniqueness of the PLD system lies, among other things, in the ability to keep the substrate at a low temperature, compared to the 1100 °C needed for the SWCNTs synthesis, thus, rendering it undamaged. Samples were placed at different positions on a cold finger (CF), where a temperature gradient develops, in the range 25-565 °C. The chemical composition and morphology of desized and surface treatments, as well as SWCNTs grown on carbon fibres, were verified by Scanning Electron Microscopy (SEM) equipped with Energy Dispersive X-Ray Spectroscopy (EDX), while the quality of SWCNTs was proven by confocal micro-Raman Spectroscopy and High-Resolution Scanning Transmission Electron Microscopy (HR-STEM). Fibres covered with SWCNTs by PLD were characterized using contact angle and the surface free energy was calculated. A micro-droplet pull-out test was used to evaluate the effect of SWCNTs over interfacial properties of a carbon-epoxy composite. A 20% increase in interfacial shear strength (IFSS) was observed by deposition at 290 °C, compared to the commercial carbon fibre sizing. The carbon fibres kept their tensile properties due to the low deposition temperatures.
RESUMEN
WS2 inorganic nanotubes (WS2-NT) have been incorporated into Polylactic Acid (PLA) by melt mixing to create a bio-degradable, mechanically reinforced nanocomposite filament. The filament was then processed by Fused Filament Fabrication (FFF) 3D-printer, and the morphology and characteristics before and after printing were compared. We found that addition of WS2-NT to PLA by extrusion mixing increases the elastic modulus, yield strength and strain-at-failure by 20%, 23% and 35%, respectively. Moreover, we found that the printing process itself improves the dispersion of WS2-NT within the PLA filament, and does not require changing of the printing parameters compared to pure PLA. The results demonstrate the advantage of WS2-NT as reinforcement specifically in 3D-printable polymers, over more traditional nano-reinforcements such as graphene and carbon nanotubes. WS2-NT based 3D-printable nanocomposites can be used for variety of applications from custom-made biodegradable scaffold of soft implants such as cartilage-based organs and biodegradable soft stents to the more general easy-to-apply nano-reinforced polymers.
RESUMEN
Impregnation of expandable graphite (EG) after thermal treatment with an epoxy resin containing surface-active agents (SAAs) enhanced the intercalation of epoxy monomer between EG layers and led to further exfoliation of the graphite, resulting in stacks of few graphene layers, so-called "stacked" graphene (SG). This process enabled electrical conductivity of cured epoxy/SG composites at lower percolation thresholds, and improved thermo-mechanical properties were measured with either Kevlar, carbon or glass-fiber-reinforced composites. Several compositions with SAA-modified SG led to higher dynamic moduli especially at high temperatures, reflecting the better wetting ability of the modified nanoparticles. The hydrophilic/hydrophobic nature of the SAA dictates the surface energy balance. More hydrophilic SAAs promoted localization of the SG at the Kevlar/epoxy interface, and morphology seems to be driven by thermodynamics, rather than the kinetic effect of viscosity. This effect was less obvious with carbon or glass fibers, due to the lower surface energy of the carbon fibers or some incompatibility with the glass-fiber sizing. Proper choice of the surfactant and fine-tuning of the crosslink density at the interphase may provide further enhancements in thermo-mechanical behavior.