Dielectric Analysis of Blended Polysulfone/Polyethylenimine Membrane Contactors for CO2 Capture.

Polysulfone membranes, used as contactors for CO2 capture, are blended with two different hyperbranched polyethyleneimines modified with benzoyl chloride (Additive 1) and phenyl isocyanate (Additive 2) in different percentages. Fourier-transformed infrared spectra evidence the presence of urea and amide groups, whereas the field emission scanning electron microscopy images show differences in the microstructure of the blended membranes. Dielectric spectra determine the motions of the side and backbone chains, which can facilitate the diffusion of CO2 . The spectra consist of six dielectric processes; three of them are due to the polysulfone (γPSf , ßPSf , and αPSf ), whereas the rest are characteristic of the additive (γHPEI , ßHPEI , and αHPEI ). The benzoyl chloride and phenyl isocyanate functional groups introduce variations in molecular mobility and modify the relaxations associated with the hyperbranched polyethyleneimine (HPEI). The additives also increase the conductivity of the blended membranes, which can compromise the performance of the membranes, specifically in the case of Additive 1. Ion hopping is found to be the prevailing charge transport mechanism while both relaxations, αHPEI and αPSf , are actives. These results, together with the final morphology of the membranes, may explain the greater absorption capacity of the membranes prepared with the hyperbranched polyethyleneimine modified with Additive 2.

Membranes for Cation Transport Based on Dendronized Poly(epichlorohydrin-co-ethylene oxide). Part 1: The Effect of Dendron Amount and Column Orientation on Copolymer Mobility.

Dendronized polyethers give rise to columnar LC structures which can successfully act as cation transport materials. Therefore, we prepared two different materials, based on Poly(epichlorohydrin-co-ethylene oxide) (PECH-co-EO) grafted with methyl 3,4,5-tris[4-(n-dodecan-1-yloxy)benzyloxy] benzoate, containing 20% or 40% modified units, respectively. The obtained polymers were characterized by differential scanning calorimetry (DSC), X-ray diffraction and optical microscopy between crossed polars (POM) and compared to the unmodified PECH-co-EO. In order to reach efficient transport properties, homeotropically oriented membranes were prepared by a fine-tuned thermal annealing treatment and were subsequently investigated by dynamic mechanical thermal analysis (DMTA) and dielectric thermal analysis (DETA). We found that the presence of the dendrons induces a main chain partial crystallization of the polyether chain and coherently increases the polymer Tg. This effect is more evident in the oriented membranes. As for copolymer orientation upon annealing, the cooling rate and the annealing temperature were the most crucial factors. DMTA and DETA confirmed that grafting with the dendron strongly hinders copolymer motions, but did not show great differences between unoriented and oriented membranes, regardless of the amount of dendrons.