Fabrication of S and O-incorporated graphitic carbon nitride linked poly(1,3,4-thiadiazole-2,5-dithiol) film for selective sensing of Hg2+ ions in water, fish, and crab samples.

Screen-printed carbon electrodes (SPCE) were modified with sulfur and oxygen-incorporated graphitic carbon nitride (S, O-GCN) linked poly(1,3,4-thiadiazole-2,5-dithiol) film (PTD) through thioester linkage. The promising interaction between the Hg2+ and modified materials containing sulfur as well as oxygen through strong affinity was studied. This study was utilized for the electrochemical selective sensing of Hg2+ ions by differential pulse anodic stripping voltammetry (DPASV). After, optimizing the different experimental parameters, S, O-GCN@PTD-SPCE was used to improve the electrochemical signal of Hg2+ ions and achieved a concentration range of 0.05-390 nM with a detection limit of 13 pM. The real-world application of the electrode was studied in different water, fish, and crab samples and their obtained results were confirmed with Inductive Coupled Plasma - Optical Emission Spectroscopy (ICP-OES) studies. Additionally, this work established a facile and consistent technique for enhancing the electrochemical sensing of Hg2+ ions and discusses various promising applications in water and food quality analysis.

Electrochemical behavior of polypyrrole/chitosan composite coating on Ti metal for biomedical applications.

In the present work, the corrosion resistance performance and biocompatibility of polypyrrole/chitosan (PPy/CHI) composite coated Ti was studied. The deposition of composite coating was carried out by electropolymerization method. The deposited PPy/CHI composite coatings were different in morphology, structural, surface roughness and wettability compared PPy coated Ti. The presence of composite coating was confirmed by solid 13C NMR. The PPy/CHI composite coating showed enhanced microhardness and adhesion strength compared to the PPy coating. The corrosion protection ability of PPy/CHI composite coatings at various applied potentials was analyzed by dynamic electrochemical impedance spectroscopy (DEIS), exhibited higher impedance in all the potentials compared to uncoated and PPy coated Ti. The lower corrosion current density obtained for PPy/CHI-2 composite coating from polarization studies revealed increased corrosion protection ability in SBF solution. The stability of composite coating was confirmed by immersion studies. PPy/CHI-2 composite coating immersed in SBF solution enhances hydroxyapatite (HAp) formation.