Effects of Mg and Sb Substitution on the Magnetic Properties of Magnetic Field Annealed MnBi Alloys.

Rare-earth-free permanent magnets have attracted considerable attention due to their favorable properties and applicability for cost-effective, high-efficiency, and sustainable energy devices. However, the magnetic field annealing process, which enhances the performance of permanent magnets, needs to be optimized for different magnetic fields and phases. Therefore, we investigated the effect of composition on the crystallization of amorphous MnBi to the ferromagnetic low-temperature phase (LTP). The optimal compositions and conditions were applied to magnetic field annealing under 2.5 T for elemental Mg- and Sb/Mg pair-substituted MnBi. The optimum MnBi composition for the highest purity LTP was determined to be Mn56Bi44, and its maximum energy product, (BH)max, was 5.62 MGOe. The Mg-substituted MnBi exhibited enhanced squareness (Mr/Ms), coercivity (Hc), and (BH)max values up to 0.8, 9659 Oe, and 5.64 MGOe, respectively, whereas the same values for the Sb/Mg pair-substituted MnBi were 0.76, 7038 Oe, and 5.60 MGOe, respectively. The substitution effects were also investigated using first-principles calculations. The density of states and total magnetic moments of Mn16Bi15Mg and Mn16Bi15Sb were similar to those of pure Mn16Bi16. Conversely, the Sb-substituted MnBi resulted in a dramatic enhancement in the anisotropy constant (K) from a small negative value (-0.85 MJ/m3) to a large positive value (6.042 MJ/m3).

Beating Thermal Deterioration of Magnetization with Mn4C and Exchange Bias in Mn⁻C Nanoparticles.

The magnetization of most materials decreases with increasing temperature due to thermal deterioration of magnetic ordering. Here, we show that Mn4C phase can compensate the magnetization loss due to thermal agitation. The Mn⁻C nanoparticles containing ferrimagnetic Mn4C and other Mn⁻C/Mn-O phases were prepared by using the traditional arc-discharge method. A positive temperature coefficient of magnetization (~0.0026 Am² kg-1 K-1) and an exchange bias up to 0.05 T were observed in the samples. We ascribe the exchange bias to the co-existence of ferrimagnetic Mn4C/Mn3O4 and antiferromagnetic α-Mn(C)/MnO phases. The positive temperature coefficient of magnetization of the samples was ascribed to the presence of Mn4C phase, which is considered as a Néel's P-type ferrimagnet.

In situ Observation of Phase Transformation in MnAl(C) Magnetic Materials.

The phase transformation in two modes, including both displacive and massive growth of τ-phase from ε-MnAl(C), was observed by in situ transmission electron microscopy. The exact temperature range for different phase transformation modes was determined by magnetic measurements. The displacive growth of ε→τ in Mn54Al46 (or Mn54Al46C2.44) occurs at temperatures below 650 K (or 766 K), above which both modes coexist. One-third or less of the ε-phase can be transformed into τ-phase via displacive mode while the remaining two-thirds or more via massive mode. In bulk τ-phase, most τ-nanocrystals formed via displacive mode are distributed in the matrix of large τ-grains that formed via massive mode. The typical massive growth rate of the τ-phase is 8-60 nm/s, while the displacive growth rate is low. A more complete understanding of the ε→τ phase transformations in the MnAl-based magnets was provided in this work, based on which the annealing process for ε→τ was optimized and thus high purity τ-phase with high saturation magnetization was obtained.