RESUMEN
High-speed melt spinning of a cyclo-olefin polymer (COP) and a copolyamide (CoPA) have been performed. Differential scanning calorimetry curves of the resulting monofilaments show that they remain in an amorphous state even after hot drawing. Wide angle x-ray diffraction patterns of undrawn and drawn COP filaments show that although the material remains in an amorphous state, a degree of orientation is induced in the polymer after drawing. The amorphous filaments show an enhanced bending recovery with respect to different semi-crystalline monofilaments commercially available. However, single fiber axial compressive testing indicates that the amorphous filaments exhibit a compressive modulus value which is 50% lower than what is observed for a reference semi-crystalline PET filament. Analysis of the compressive strains applied by the bending recovery test indicates that while the maximum applied strains remain well within the region of elastic deformation of the amorphous materials, the threshold between elastic and plastic deformation is reached for the semi-crystalline materials.
RESUMEN
A synchrotron study is presented in which the concept of one-dimensional tomographic reconstruction of small-angle X-ray scattering patterns is applied to investigate polyamide 6 monofilaments, dip-coated with alumina particles. The filaments are scanned with a focused synchrotron beam and the resulting scattering patterns are recorded with a PILATUS 2M detector. The reconstructed sequence of SAXS images reflects the local nanostructure variation along the filament radius. In particular, the influence of coating process parameters on the polyamide 6 is investigated.