RESUMEN
This work establishes the first direct mechanocatalytic reaction protocol within an extruder, focusing on the Suzuki-Miyaura reaction. Through the coating of either the extruder screws or barrel with Pd, we executed the cross-coupling reaction without the reliance on molecular catalyst compounds or powders, and solvents continuously. We identified the influence and interplay of crucial reaction parameters such as temperature, mechanical energy input, residence time, rheology, and catalyst contact time and finally obtained 36 % and 75 % of the reaction product after one and four reactor passes respectively.
RESUMEN
We have utilized carbon sources as milling additives to enable a direct mechanochemical one-pot synthesis of Fe3Co3Ni3S8/carbon (Pn/C) materials using elemental reaction mixtures. The obtained Pn/C materials are thoroughly characterized and their carbon content could be adjusted up to 50 wt%. In addition to carbon black (CB) as an additive, Pn/C materials were produced using graphite, reduced graphene oxide (rGO), and carbon nanotubes (CNTs), which allows the overall physicochemical properties of materials for energy storage applications to be adjusted. By employing the Pn/C materials as electrocatalysts for the HER in a zero-gap proton exchange membrane (PEM) electrolyzer, we were able to reach a current density of 1 A cm-2 at a cell potential as low as 2.12 V using Pn, which was synthesized with 25 wt% CB. Furthermore, electrolysis at an applied current density of 1 A cm-2 for 100 h displays a stable performance, thus providing a sustainable synthesis procedure for potential future energy storage applications. Herein, we show that catalyst supports play an important role in the overall performance.
RESUMEN
Herein, the first mechanochemical Fries rearrangement for the industrially important synthesis of para-hydroxyacetophenone, inside a ball mill and a twin-screw extruder, is presented. Our approach leads to a yield of 62 % in as little as 90â minutes while liquid-assisted grinding can shift the isomer ratio resulting in an excess of the desired para-product. The multigram scale-up by extrusion leads to 61 % yield in only three minutes while completely avoiding solvents. The extrusion temperature can even further be reduced by combining extrusion with a subsequent ageing step.
RESUMEN
The mechanochemical synthesis of nitrogen-rich nanoporous carbon materials has been scaled up using an extruder. Lignin, urea, and K2 CO3 were extruded under heat and pressure to yield nanoporous carbons with up to 3500â m2 g-1 specific surface area after pyrolysis. The route was further broadened by applying different nitrogen sources as well as sawdust as a low-cost renewable feedstock to receive carbons with a C/N ratio of up to 15â depending on nitrogen source and extrusion parameters. The texture of obtained carbons was investigated by scanning electron microscopy as well as argon and nitrogen physisorption, while the chemical structure was analyzed by X-ray photoelectron spectroscopy. The received carbon was tested as a supercapacitor electrode, showing comparable performance to similar ball-mill-synthesized materials. Lastly, the space-time yield was applied to justify the use of a continuous reactor versus the ball mill.
Asunto(s)
Carbono , Nanoporos , Carbono/química , Electrodos , Nitrógeno/química , SolventesRESUMEN
Polyimides were obtained in 99 % yield in under 1â h through the "beat and heat" approach, involving solvent-free vibrational ball milling and a thermal treatment step. The influence of a plethora of additives was explored, such as Lewis acids, Lewis bases, and dehydrating agents, and the mechanochemical reaction was identified to run via a polyamic acid intermediate. The protocol was adopted to a range of substrates inaccessible through solution-based processes, including perylene tetracarboxylic acid dianhydride and melamine. Furthermore, quantum chemical calculations were conducted to identify the water removal as the crucial step in the reaction mechanism. The presented method is substantially faster and more versatile than the solution-based process.
Asunto(s)
Perileno , SolventesRESUMEN
The synthesis of porous electrode materials is often linked with the generation of waste that results from extensive purification steps and low mass yield. In contrast to porous carbons, covalent triazine frameworks (CTFs) display modular properties on a molecular basis through appropriate choice of the monomer. Herein, the synthesis of a new pyridine-based CTF material is showcased. The porosity and nitrogen-doping are tuned by a careful choice of the reaction temperature. An in-depth structural characterization by using Ar physisorption, X-ray photoelectron spectroscopy, and Raman spectroscopy was conducted to give a rational explanation of the material properties. Without any purification, the samples were applied as symmetrical supercapacitors and showed a specific capacitance of 141â F g-1 . Residual ZnCl2 , which acted formerly as the porogen, was used directly as the electrolyte salt. Upon the addition of water, ZnCl2 was dissolved to form the aqueous electrolyte inâ situ. Thereby, extensive and time-consuming washing steps could be circumvented.