Bacterial reservoir in deeper skin is a potential source for surgical site and biomaterial-associated infections.

BACKGROUND: The origin of surgical site and biomaterial-associated infection is still elusive. Micro-organisms contaminating the wound may come from the air in the operating theatre, the surgical team or the skin of the patient. The skin of patients is disinfected prior to surgery, but bacteria deeper in the skin (e.g. in sweat glands or sebaceous glands) may not be reached. METHODS: A preliminary cohort study was performed to study the origin of surgical site and biomaterial-associated infection between May 2020 and February 2021. In order to investigate whether cutaneous microbiota colonize the wound when released from the skin upon cutting, aerobic and anaerobic bacteria were isolated, quantified and identified from the skin of 99 patients undergoing trauma surgery, before and after skin disinfection, from knife blades and from the wound directly after the first cut. RESULTS: Ninety-nine percent of the patients were culture-positive before disinfection with chlorhexidine. Of these, 40% were still culture-positive after disinfection. Of these, 54% had a positive culture of the wound after cutting the skin. Twenty percent of the patients with a negative culture after disinfection had a positive wound culture after cutting the skin. Staphylococcus epidermidis and Cutibacterium acnes were the most commonly cultured bacterial species. In 9% of cases, more than 100 bacterial colonies were cultured from the wound; this may cause biomaterial-associated infection. CONCLUSION: Bacteria residing in the skin and not eradicated by disinfection may enter the surgical wound upon cutting, resulting in contamination which may cause biomaterial-associated infection.

Current osteomyelitis mouse models, a systematic review.

Osteomyelitis is an inflammatory bone disease caused by an infecting microorganism leading to a gradual bone loss. Due to the difficulty in studying osteomyelitis directly in patients, animal models allow researchers to investigate the pathogenesis of the infection and the development of novel prophylactic, anti-inflammatory and antimicrobial treatment strategies. This review is specifically focused on the in vivo mouse osteomyelitis studies available in literature. Thus, a systematic search on Web of Science and PubMed was conducted using the query "(infection) AND (mice OR mouse OR murine) AND (model OR models) AND (arthroplasty OR fracture OR (internal fixator) OR (internal fixation OR prosthesis OR implant OR osteomyelitis)". After critical assessment of the studies according to the inclusion and exclusion criteria, 135 studies were included in the detailed analysis. Based on the model characteristics, the studies were classified into five subject groups: haematogenous osteomyelitis, post-traumatic osteomyelitis, bone-implant-related infection, peri-prosthetic joint infection, fracture-related infection. In addition, the characteristics of the mice used, such as inbred strain, age or gender, the characteristics of the pathogens used, the inoculation methods, the type of anaesthesia and analgesia used during surgery and the procedures for evaluating the pathogenicity of the infecting micro-organism were described. Overall, the mouse is an excellent first step in vivo model to study the pathogenesis, inflammation and healing process of osteomyelitis and to evaluate novel prophylaxis and treatment strategies.

A murine Staphylococcus aureus fracture-related infection model characterised by fracture non-union, staphylococcal abscess communities and myeloid-derived suppressor cells.

A fracture-related infection (FRI) is a serious complication that can occur after surgical fixation of bone fractures. Affected patients may encounter delayed healing and functional limitations. Although it is well established that Staphylococcus aureus (S. aureus) is the main causative pathogen of an FRI, the pathophysiology of an S. aureus-induced FRI is not well characterised over time. Therefore, an experimental study in mice comparing S. aureus-inoculated and non-inoculated groups was performed that particularly focused on staphylococcal abscess communities (SACs) and host cellular response. C57Bl/6N female mice received a double osteotomy of the femur, which was stabilised using a titanium 6-hole MouseFix locking plate and four screws. Animals were either S. aureus-inoculated or non-inoculated and euthanised between 1 and 28 d post-surgery. Histopathological evaluation showed normal bone healing for non-inoculated mice, whereas inoculated mice had no fracture consolidation and severe osteolysis. Within the bone marrow of inoculated mice, SACs were observed from 7 d, which increased in size and number over time. A fibrin pseudocapsule enclosed the SACs, which were surrounded by many Ly6G+ neutrophils with some Ly6C+ monocytes and F4/80+ macrophages, the majority of which were viable. The abscesses were encapsulated by fibrin(ogen), collagen and myofibroblasts, with regulatory T cells and M2 macrophages at the periphery. Only bone marrow monocytes and neutrophils of inoculated mice displayed functional suppression of T cells, indicative of myeloid-derived suppressor cells. The present study revealed that an FRI in mice is persistent over time and associated with osteolysis, SAC formation and an immunosuppressive environment.

Effects of sterilization on the mechanical properties of poly(methyl methacrylate) based personalized medical devices.

BACKGROUND: Nowadays, personalized medical devices are frequently used for patients. Due to the manufacturing procedure sterilization is required. How different sterilization methods affect the mechanical behavior of these devices is largely unknown. MATERIALS AND METHODS: Three poly(methyl methacrylate) (PMMA) based materials (Vertex Self-Curing, Palacos R+G, and NextDent C&B MFH) were sterilized with different sterilization methods: ethylene oxide, hydrogen peroxide gas plasma, autoclavation, and γ-irradiation. Mechanical properties were determined by testing the flexural strength, flexural modulus, fracture toughness, and impact strength. RESULTS: The flexural strength of all materials was significantly higher after γ-irradiation compared to the control and other sterilization methods, as tested in a wet environment. NextDent C&B MFH showed the highest flexural and impact strength, Palacos R+G showed the highest maximum stress intensity factor and total fracture work. CONCLUSION: Autoclave sterilization is not suitable for the sterilization of PMMA-based materials. Ethylene oxide, hydrogen peroxide gas plasma, and γ-irradiation appear to be suitable techniques to sterilize PMMA-based personalized medical devices.

A chlorhexidine-releasing epoxy-based coating on titanium implants prevents Staphylococcus aureus experimental biomaterial-associated infection.

Prevention of biomaterial-associated infections (BAI) remains a challenging problem, in particular due to the increased risk of resistance development with the current antibiotic-based strategies. Metallic orthopaedic devices, such as non-cemented implants, are often inserted under high mechanical stress. These non-cemented implants cannot be protected by e.g. antibioticreleasing bone cement or other antimicrobial approaches, such as the use of bioactive glass. Therefore, in order to avoid abrasion during implantation procedures, we developed an antimicrobial coating with great mechanical stability for orthopaedic implants, to prevent Staphylococcus aureus BAI. We incorporated 5 and 10 wt % chlorhexidine in a novel mechanically stable epoxy-based coating, designated CHX5 and CHX10, respectively. The coatings displayed potent bactericidal activity in vitro against S. aureus, with over 80 % of the release (19 µg/cm2 for CHX5 and 41 µg/cm2 for CHX10) occurring within the first 24 h. In mice, the CHX10 coating significantly reduced the number of CFU (colony forming units), both on the implants and in the peri-implant tissues, 1 d after S. aureus challenge. The CHX10-coated implants were well-tolerated by the animals, with no signs of toxicity observed by histological analysis. Moreover, the coating significantly reduced the frequency of culture-positive tissues 1 d, and of culture-positive implants 1 and 4 d after challenge. In summary, the chlorhexidine-releasing mechanically stable epoxy-based CHX10 coating prevented implant colonisation and S. aureus BAI in mice and has good prospects for clinical development.

Fabrication of oxide layer on zirconium by micro-arc oxidation: Structural and antimicrobial characteristics.

The aim of this study was to cover the surfaces of zirconium (Zr) with an antimicrobial layer for biomedical applications. For this purpose, the micro-arc oxidation (MAO) process was employed in a sodium silicate and sodium hydroxide containing base electrolyte with and without addition of silver acetate (AgC2H3O2). In general, synthesized MAO layers were composed of zirconium oxide (ZrO2) and zircon (ZrSiO4). Addition of AgC2H3O2 into the base electrolyte caused homogenous precipitation of silver-containing particles in the MAO layer, which exhibited excellent antibacterial efficiency against methicillin-resistant Staphylococcus aureus (MRSA) as compared to the untreated and MAO-treated Zr.

Prevention of Staphylococcus aureus biomaterial-associated infections using a polymer-lipid coating containing the antimicrobial peptide OP-145.

The scarcity of current antibiotic-based strategies to prevent biomaterial-associated infections (BAI) and their risk of resistance development prompted us to develop a novel antimicrobial implant-coating to prevent Staphylococcus aureus-induced BAI. We incorporated the antimicrobial peptide OP-145 into a Polymer-Lipid Encapsulation MatriX (PLEX)-coating to obtain high peptide levels for prolonged periods at the implant-tissue interphase. We first confirmed that OP-145 was highly effective in killing S. aureus and inhibiting biofilm formation in vitro. OP-145 injected along S. aureus-inoculated implants in mice significantly reduced the number of culture-positive implants. OP-145 was released from the PLEX coating in a controlled zero-order kinetic rate after an initial 55%-burst release and displayed bactericidal activity in vitro. In a rabbit intramedullary nail-related infection model, 67% of rabbits with PLEX-OP-145-coated nails had culture-negative nails after 28days compared to 29% of rabbits with uncoated nails. In rabbits with PLEX-OP-145-coated nails, bone and soft tissue samples were culture-negative in 67% and 80%, respectively, whereas all bone samples and 71% of the soft tissue samples of rabbits with uncoated nails were infected. Together, PLEX-OP-145 coatings, of which both compounds have already been found safe in man, can prevent implant colonization and S. aureus-induced BAIs.