RESUMEN
OBJECTIVES: to evaluate the probability of survival and failure modes of lithium-disilicate, feldspathic-ceramic, and resin-nanoceramic anterior veneers cemented on dentin analog substrates after sliding-contact step-stress accelerated life testing (SSALT). METHODS: A virtual incisor tooth preparation was produced with a reduction of 1.5mm at the incisal edge and of 0.7mm buccally. A .STL file of the preparation was generated and CAD/CAM based G10 dentin-analog material was used for testing. Laminate veneers were milled in three different materials: lithium-disilicate (LDS, E.max CAD), resin-nanoceramic (RN, Lava Ultimate), and feldspathic-ceramic (FELDS, Vita Blocks). SSALT was employed where a spherical indenter contacted the veneer, slided along its interface with G10 to lift off and start a new cycle at 2Hz in water. Qualitative fractography was performed. The probability of survival (90% confidence-bounds) was calculated for several load/cycle missions. RESULTS: The probability of survival for a mission of 50,000 cycles decreased from 50 up to 150N equally for all groups and were not different between them. At 200N, the probability of survival was significantly lower for FELDS (10%) compared to RN veneers (41%), whereas LDS presented intermediate values (22%). The characteristic strength of RN (247N) was significantly higher than LDS (149N), and FELDS (151N). In FELDS and LDS, hackles, wake hackles and twist hackles indicated the direction of crack propagation. In RN, hackles were observed. CONCLUSIONS: Differences in probability of survival were observed only at 180 and 200N between groups. Failure modes were similar with veneer fracture down to the tooth-analog substrate.