Despite of excellent thermal properties and high sputtering resistance, pure tungsten cannot fully satisfy the requirements for plasma facing materials in future high-duty cycle nuclear fusion reactions due to the coupled extreme environments, including the high thermal loads, plasma exposure, and radiation damage. Here, we demonstrated that tungsten-based composite materials fabricated using spark-plasma sintering (SPS) present promising solutions to these challenges. Through the examination of two model systems, i.e., tungsten-zirconium composite for producing porous tungsten near the surface and dispersoid-strengthened tungsten, we discussed both the strengths and limitations of the SPS-fabricated materials. Our findings point towards the need for future studies aimed at optimizing the SPS process to achieve desired microstructures and effective control of oxygen impurities in the tungsten-based composite materials.
RESUMEN
The formation of helium bubbles and subsequent property degradation poses a significant challenge to tungsten as a plasma-facing material in future long-pulse plasma-burning fusion reactors. In this study, we investigated helium bubble formation in dispersion-strengthened tungsten doped with transition metal carbides, including TaC, ZrC, and TiC. Of the three dispersoids, TaC exhibited the highest resistance to helium bubble formation, possibly due to the low vacancy mobility in the Group VB metal carbide and oxide phases. Under identical irradiation conditions, large helium bubbles formed at grain boundaries in tungsten, while no bubbles were observed at the interfaces between the carbide dispersoid and tungsten matrix. Moreover, our results showed the interfaces could suppress helium bubble formation in the nearby tungsten matrix, suggesting that the interfaces are more effective in trapping helium as tiny clusters. Our research provided new insights into optimizing the microstructure of dispersion-strengthened tungsten alloys to enhance their performance.