Investigation of Stress Corrosion Cracking Resistance of Irradiated 12Cr Ferritic-Martensitic Stainless Steel in Supercritical Water Environment.

The supercritical water-cooled reactors (SWCR) belong to Generation IV of reactors. These reactors have a number of advantages over currently operating WWERs and PWRs. These advantages include higher thermal efficiency, a more simplified unit design, and the possibility of incorporating it into a closed fuel cycle. It is therefore necessary to identify candidate materials for the SWCR and validate the safety and effectiveness of their use. 12Cr ferritic-martensitic (F/M) stainless steel is considered a candidate material for SWCR internals. Radiation embrittlement and corrosion cracking in the primary circuit coolant environment are the main mechanisms of F/M steels degradation during SWCR operation. Here, the stress corrosion cracking (SCC) in supercritical water at 390 and 550 °C of 12Cr F/M steel irradiated by neutrons to 12 dpa is investigated. Autoclave tests of specially designed disk specimens in supercritical water were performed. The tests were carried out under different constant load (CL), temperature 450 °C, and pressure in autoclave 25 MPa. The threshold stress, below which the SCC initiation of irradiated 12Cr F/M steel does not occur, was determined.

Multiphoton microscopy assessment of the structure and variability changes of dermal connective tissue in vulvar lichen sclerosus: A pilot study.

In this article, we offer a novel classification of progressive changes in the connective tissue of dermis in vulvar lichen sclerosus (VLS) relying on quantitative assessment of the second harmonic generation (SHG) signal received from formalin fixed and deparaffinized tissue sections. We formulate criteria for distinguishing four degrees of VLS development: Initial-Mild-Moderate-Severe. Five quantitative characteristics (length and thickness type I Collagen fibers, Mean SHG signal intensity, Skewness and Coherence SHG signal) are used to describe the sequential degradation of connective tissue (changes in the structure, orientation, shape and density of collagen fibers) up to the formation of specific homogeneous masses. Each of the degrees has a characteristic set of quantitatively expressed features. We focus on the identification and description of early, initial changes of the dermis as the least specific. The results obtained by us and the proposed classification of the degrees of the disease can be used to objectify the dynamics of tissue changes during treatment.