Electrospun vascular grafts fabricated from poly(L-lactide-co-ε-caprolactone) used as a bypass for the rabbit carotid artery.

The study involved the electrospinning of the copolymer poly(L-lactide-co-ε-caprolactone) (PLCL) into tubular grafts. The subsequent material characterization, including micro-computed tomography analysis, revealed a level of porosity of around 70%, with pore sizes of 9.34 ± 0.19 µm and fiber diameters of 5.58 ± 0.10 µm. Unlike fibrous polycaprolactone, the electrospun PLCL copolymer promoted fibroblast and endothelial cell adhesion and proliferation in vitro. Moreover, the regeneration of the vessel wall was detected following implantation and, after six months, the endothelialization of the lumen and the infiltration of arranged smooth muscle cells producing collagen was observed. However, the degradation rate was found to be accelerated in the rabbit animal model. The study was conducted under conditions that reflected the clinical requirements-the prostheses were sutured in the end-to-side fashion and the long-term end point of prosthesis healing was assessed. The regeneration of the vessel wall in terms of endothelialization, smooth cell infiltration and the presence of collagen fibers was observed after six months in vivo. A part of the grafts failed due to the rapid degradation rate of the PLCL copolymer.

Comprehensive assessment of electrospun scaffolds hemocompatibility.

Biodegradable polyesters, namely polycaprolactone (PCL) and copolymer of polylactide and polycaprolactone (PLCL) were electrospun into various fibrous structures and their hemocompatibility was evaluated in vitro. Firstly, hemolytic effect was evaluated upon incubation with diluted whole blood. The results showed that the degree of hemolysis depended on chemical composition and fibrous morphology. Electrospun polycaprolactone induced slight degree of hemolysis depending on its molecular weight and fibrous morphology; copolymer PLCL did not cause detectable hemolysis. The influence of coagulation pathways was examined by measurement of coagulation times. It was showed that intrinsic coagulation pathway assessed by activated partial thromboplastin time (APTT) was moderately accelerated after incubation with PCL and prolonged after incubation with copolymer PLCL. Extrinsic activation of coagulation tested by prothrombin time (PT) was slightly accelerated after incubation with all tested electrospun samples. Thrombogenicity assessment of fibrous samples revealed high thrombogenic properties of fibrous materials that was comparable to high degree of collagen thrombogenicity. The level of platelet activation was dependent on chemical composition and surface morphology of tested materials.