Glass-Forming Ability and Thermal Properties of Al70Fe12.5V12.5X5(X = Zr, Nb, Ni) Amorphous Alloys via Minor Alloying Additions.

The Al70Fe12.5V12.5Ni5, Al70Fe12.5V12.5Zr5 and Al70Fe12.5V12.5Nb5 alloys were prepared via mechanical alloying. The influence of Zr, Nb or Ni addition on the glass-forming ability of Al-Fe-V amorphous alloys have been investigated. The structure of Al70Fe12.5V12.5Ni5 was amorphous and Al70Fe12.5V12.5Zr5 was not completely amorphous by transmission electron microscopy, selected area electron diffraction and differential scanning calorimetry. Different criteria were used to evaluate the influence of the addition of alloy elements on the Glass-forming ability. The Al70Fe12.5V12.5Ni5 amorphous alloys exhibits higher glass-forming ability and activation energies of crystallization. Comparison of the effective atomic size ratio and mixture enthalpy on the glass-forming ability of these amorphous alloys demonstrates that the effective atomic size ratio value becomes more significant than the values of mixture enthalpy.

Crystallization Behavior of Al70Fe12.5V12.5Nb5 Amorphous Alloy Formed by Mechanical Alloying.

In this study, the formation and crystallization of the Al70Fe12.5V12.5Nb5 amorphous alloys has been investigated. The addition of Nb enhances the supercooled liquid region and glass forming ability of the Al-Fe-V amorphous alloys. The Al70Fe12.5V12.5Nb5 amorphous alloy exhibits two distinct crystallization steps and a large supercooled liquid region at more than 100 K. Kissinger and Ozawa analyses showed that the two activation energies for crystallization (Ex) were estimated to be 366.3 ± 23.9 and 380.5 ± 23.9 kJ/mol. Large supercooled liquid regions are expected to gain an application field of Al-based amorphous alloys.