An emerging strategy in the design of efficient gas storage technologies is the development of stimuli-responsive physisorbents which undergo transformations in response to a particular stimulus, such as pressure, heat or light. Herein, we report two isostructural light modulated adsorbents (LMAs) containing bis-3-thienylcyclopentene (BTCP), LMA-1 [Cd(BTCP)(DPT)2 ] (DPT=2,5-diphenylbenzene-1,4-dicarboxylate) and LMA-2 [Cd(BTCP)(FDPT)2 ] (FDPT=5-fluoro-2,diphenylbenzene-1,4-dicarboxylate). Both LMAs undergo pressure induced switching transformations from non-porous to porous via adsorption of N2 , CO2 and C2 H2 . LMA-1 exhibited multi-step adsorption while LMA-2 showed a single-step adsorption isotherm. The light responsive nature of the BTPC ligand in both frameworks was exploited with irradiation of LMA-1 resulting in a 55 % maximum reduction of CO2 uptake at 298â K. This study reports the first example of a switching sorbent (closed to open) that can be further modulated by light.
RESUMEN
Flexible metal-organic materials that exhibit stimulus-responsive switching between closed (non-porous) and open (porous) structures induced by gas molecules are of potential utility in gas storage and separation. Such behaviour is currently limited to a few dozen physisorbents that typically switch through a breathing mechanism requiring structural contortions. Here we show a clathrate (non-porous) coordination network that undergoes gas-induced switching between multiple non-porous phases through transient porosity, which involves the diffusion of guests between discrete voids through intra-network distortions. This material is synthesized as a clathrate phase with solvent-filled cavities; evacuation affords a single-crystal to single-crystal transformation to a phase with smaller cavities. At 298 K, carbon dioxide, acetylene, ethylene and ethane induce reversible switching between guest-free and gas-loaded clathrate phases. For carbon dioxide and acetylene at cryogenic temperatures, phases showing progressively higher loadings were observed and characterized using in situ X-ray diffraction, and the mechanism of diffusion was computationally elucidated.