Aqueous zinc-ion batteries (ZIBs) using the Zn metal anode have been considered as one of the next-generation commercial batteries with high security, robust capacity, and low price. However, parasitic reactions, notorious dendrites and limited lifespan still hamper their practical applications. Herein, an eco-friendly nitrogen-doped and sulfonated carbon dots (NSCDs) is designed as a multifunctional additive for the cheap aqueous ZnSO4 electrolyte, which can overcome the above difficulties effectively. The abundant polar groups (-COOH, -OH, -NH2 , and -SO3 H) on the CDs surfaces can regulate the solvation structure of Zn2+ through decreasing the coordinated active H2 O molecules, and thus redistribute Zn2+ deposition to avoid side reactions. Some of the negatively charged NSCDs are adsorbed on Zn anode surface to isolate the H2 O/SO4 2- corrosion through the electrostatic shielding effect. The synergistic effect of the doped nitrogen species and the surface sulfonic groups can induce a uniform electrolyte flux and a homogeneous Zn plating with a (002) texture. As a result, the excellent cycle life (4000 h) and Coulombic efficiency (99.5%) of the optimized ZIBs are realized in typical ZnSO4 electrolytes with only 0.1 mg mL-1 of NSCDs additive.
RESUMEN
Mn3 O4 is a promising cathode material for aqueous zinc ion batteries (ZIBs) which is a new type of low cost, eco-friendly, high security energy storage system, while those previously reported electrochemical capacities of Mn3 O4 are far from its theoretical value. In this work, Mn3 O4 nanoparticles and nitrogen-doped carbon dots (NCDs) are synthesized together through an in-situ hydrothermal route, and then calcined to be a nanocomposite in which Mn3 O4 nanoparticles are anchored on a nitrogen-doped carbon skeleton (designated as Mn3 O4 /NCDs). Although the carbon content is only 3.9â wt.% in the Mn3 O4 /NCDs, the NCDs-derived carbon skeleton provides an electrically conductive network and a stable structure. Such a special nanocomposite has a large specific surface area, plenty of active sites, excellent hydrophilicity and good electronic conductivity. Owing to these structural merits, the Mn3 O4 /NCDs electrode exhibits a preeminent specific capacity of 443.6â mAh g-1 and 123.3â mAh g-1 at current densities of 0.1 and 1.5â A g-1 in ZIBs, respectively, which are far beyond the bare Mn3 O4 nanoparticles synthesized under the similar condition. The electrochemical measurement results prove that carbon dots, as a new type of carbon nanomaterials, have strong ability to modify and improve the performance of existing electrode materials, which may push these electrode materials forward to practical applications.