RESUMEN
Titanium alloys, especially ß alloys, are favorable as implant materials due to their promising combination of low Young's modulus, high strength, corrosion resistance, and biocompatibility. In particular, the low Young's moduli reduce the risk of stress shielding and implant loosening. The processing of Ti-24Nb-4Zr-8Sn through laser powder bed fusion is presented. The specimens were heat-treated, and the microstructure was investigated using X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The mechanical properties were determined by hardness and tensile tests. The microstructures reveal a mainly ß microstructure with αâ³ formation for high cooling rates and α precipitates after moderate cooling rates or aging. The as-built and αâ³ phase containing conditions exhibit a hardness around 225 HV5, yield strengths (YS) from 340 to 490 MPa, ultimate tensile strengths (UTS) around 706 MPa, fracture elongations around 20%, and Young's moduli about 50 GPa. The α precipitates containing conditions reveal a hardness around 297 HV5, YS around 812 MPa, UTS from 871 to 931 MPa, fracture elongations around 12%, and Young's moduli about 75 GPa. Ti-24Nb-4Zr-8Sn exhibits, depending on the heat treatment, promising properties regarding the material behavior and the opportunity to tailor the mechanical performance as a low modulus, high strength implant material.
RESUMEN
Thin film thermocouples are widely used for local temperature determinations of surfaces. However, depending on the environment in which they are used, thin film thermocouples need to be covered by a wear or oxidation resistant top layer. With regard to the utilization in wide-slit nozzles for plastic extrusion, Ni/Ni-20Cr thin film thermocouples were manufactured using direct-current (DC) magnetron sputtering combined with Aluminiumnitride (AlN) and Boron-Carbonitride (BCN) thin films. On the one hand, the deposition parameters of the nitride layers were varied to affect the chemical composition and morphology of the AlN and BCN thin films. On the other hand, the position of the nitride layers (below the thermocouple, above the thermocouple, around the thermocouple) was changed. Both factors were investigated concerning the influence on the Seebeck coefficient and the reaction behaviour of the thermocouples. Therefore, the impact of the nitride thin films on the morphology, physical structure, crystallite size, electrical resistance and hardness of the Ni and Ni-20Cr thin films is analysed. The investigations reveal that the Seebeck coefficient is not affected by the different architectures of the thermocouples. Nevertheless, the reaction time of the thermocouples can be significantly improved by adding a thermal conductive top coat over the thin films, whereas the top coat should have a coarse structure and low nitrogen content.
RESUMEN
Magnesium (Mg)-based biomaterials are promising candidates for bone and tissue regeneration. Alloying and surface modifications provide effective strategies for optimizing and tailoring their degradation kinetics. Nevertheless, biocompatibility analyses of Mg-based materials are challenging due to its special degradation mechanism with continuous hydrogen release. In this context, the hydrogen release and the related (micro-) milieu conditions pretend to strictly follow in vitro standards based on ISO 10993-5/-12. Thus, special adaptions for the testing of Mg materials are necessary, which have been described in a previous study from our group. Based on these adaptions, further developments of a test procedure allowing rapid and effective in vitro cytocompatibility analyses of Mg-based materials based on ISO 10993-5/-12 are necessary. The following study introduces a new two-step test scheme for rapid and effective testing of Mg. Specimens with different surface characteristics were produced by means of plasma electrolytic oxidation (PEO) using silicate-based and phosphate-based electrolytes. The test samples were evaluated for corrosion behavior, cytocompatibility and their mechanical and osteogenic properties. Thereby, two PEO ceramics could be identified for further in vivo evaluations.