Microstructural Degradation of the AlMo0.5NbTa0.5TiZr Refractory Metal High-Entropy Superalloy at Elevated Temperatures.

Refractory metal high-entropy superalloys (RSA), which possess a nanoscale microstructure of B2 and bcc phases, have been developed to offer high temperature capabilities beyond conventional Ni-based alloys. Despite showing a number of excellent attributes, to date there has been little consideration of their microstructural stability, which is an essential feature of any material employed in high temperature service. Here, the stability of the exemplar RSA AlMo0.5NbTa0.5TiZr is studied following 1000 h exposures at 1200, 1000 and 800 °C. Crucially, the initial nanoscale cuboidal B2 + bcc microstructure was found to be unstable following the thermal exposures. Extensive intragranular precipitation of a hexagonal Al-Zr-rich intermetallic occurred at all temperatures and, where present, the bcc and B2 phases had coarsened and changed morphology. This microstructural evolution will concomitantly change both the mechanical and environmental properties and is likely to be detrimental to the in-service performance of the alloy.

Data on a new beta titanium alloy system reinforced with superlattice intermetallic precipitates.

The data presented in this article are related to the research article entitled "a new beta titanium alloy system reinforced with superlattice intermetallic precipitates" (Knowles et al., 2018) [1]. This includes data from the as-cast alloy obtained using scanning electron microscopy (SEM) and x-ray diffraction (XRD) as well as SEM data in the solution heat treated condition. Transmission electron microscopy (TEM) selected area diffraction patterns (SADPs) are included from the alloy in the solution heat treated condition, as well as the aged condition that contained < 100 nm B2 TiFe precipitates [1], the latter of which was found to exhibit double diffraction owing to the precipitate and matrix channels being of a similar width to the foil thickness (Williams and Carter, 2009) [2]. Further details are provided on the macroscopic compression testing of small scale cylinders. Of the micropillar deformation experiment performed in [1], SEM micrographs of focused ion beam (FIB) prepared 2 µm micropillars are presented alongside those obtained at the end of the in-situ SEM deformation as well as videos of the in-situ deformation. Further, a table is included that lists the Schmidt factors of all the possible slip systems given the crystal orientations and loading axis of the deformed micropillars in the solution heat treated and aged conditions.

Data on a Laves phase intermetallic matrix composite in situ toughened by ductile precipitates.

The data presented in this article are related to the research article entitled "Laves phase intermetallic matrix composite in situ toughened by ductile precipitates" (Knowles et al.) [1]. The composite comprised a Fe2(Mo, Ti) matrix with bcc (Mo, Ti) precipitated laths produced in situ by an aging heat treatment, which was shown to confer a toughening effect (Knowles et al.) [1]. Here, details are given on a focused ion beam (FIB) slice and view experiment performed on the composite so as to determine that the 3D morphology of the bcc (Mo, Ti) precipitates were laths rather than needles. Scanning transmission electron microscopy (S(TEM)) micrographs of the microstructure as well as energy dispersive X-ray spectroscopy (EDX) maps are presented that identify the elemental partitioning between the C14 Laves matrix and the bcc laths, with Mo rejected from the matrix into laths. A TEM selected area diffraction pattern (SADP) and key is provided that was used to validate the orientation relation between the matrix and laths identified in (Knowles et al.) [1] along with details of the transformation matrix determined.