Effect of calcination on minimally processed recycled zirconia powder derived from milling waste.

OBJECTIVE: To assess the influence of calcination process on the properties of minimally processed recycled 3Y-TZP, and to compare it with its commercial counterpart. METHODS: Non-milled 3Y-TZP waste was collected, fragmented and ball-milled to a granulometric < 5 µm. Half of the recycled powder was calcined at 900 °C. Recycled 3Y-TZP disks were uniaxially pressed and sintered to create two recycled groups: 1) Calcined and 2) Non-calcined to be compared with a commercial CAD/CAM milled 3Y-TZP. The microstructure of experimental groups was assessed through density (n = 6), scanning electron microscopy (n = 3) and energy-dispersive X-ray spectroscopy (n = 3); and the crystalline content was evaluated through X-ray diffraction (XRD) (n = 3). Optical and mechanical properties were investigated through reflectance tests (n = 10), and Vickers hardness, fracture toughness (n = 5), and biaxial flexural strength tests (n = 16), respectively. Fractographic analysis was performed to identify fracture origin and crack propagation. Statistical analyses were performed through ANOVA followed by Tukey´s test, and by Weibull statistics. RESULTS: Particle size distribution of recycled powder revealed an average diameter of ∼1.60 µm. The relative density of all experimental groups was > 98.15 % and XRD analysis exhibited a predominance of tetragonal-phase in both recycled groups, which were similar to the crystallographic pattern of the control group. Cross-section micrographs presented flaws on the non-calcined group, and a more homogeneous microstructure for the calcined and commercial groups. Commercial samples showed lower contrast-ratio and higher translucency-parameter than the recycled groups, where non-calcined presented higher translucency-parameter and lower contrast-ratio than its calcined counterpart. The commercial group presented higher fracture toughness and characteristic strength than the recycled groups. Moreover, the calcined group exhibited higher hardness, characteristic strength, and probability of survival at higher loads than the non-calcined group. Fractographic analysis depicted the presence of microstructural flaws in the non-calcined group, which may have acted as stress-raisers and led to failures at lower flexural strengths values. SIGNIFICANCE: The calcination process improved the microstructure, optical, and mechanical properties of the recycled 3Y-TZP.

The effect of photoinitiator type and filler load on physicochemical and mechanical properties of experimental light-cured resin cements through lithium disilicate ceramics of different shades and thicknesses.

OBJECTIVE: This study investigated the influence of photoinitiator types on degree of conversion (DC), rate of polymerization (RP), flexural strength (FS), flexural modulus (FM), and light transmittance (LT) of filled and unfilled light-curable resin cements through different thicknesses and shades of lithium disilicate ceramics. METHODS: Lithium disilicate ceramic discs (IPS Emax Press, background [0.0], 0.5, 1.0, 2.0, 3.0, and 4.0 mm, shades A1 and BL3) were prepared. Experimental resin-based cements [TEGDMA/BisGMA (50/50 mass%)] were prepared using either camphorquinone (CQ)/amine (0.44/1.85 mol%) or TPO (0.44 mol%)], and a micro and nanofiller loads of nil (unfilled); 40/10 mass%; and 50/10 mass%). Resin cements (0.2 mm thick) were placed on the lower surface of the ceramic specimens and light-activated for 30 s from the upper surface using a Bluephase Style curing light (exitance at tip: 1236 mW/cm2 ± 1.20). LT and distribution of irradiance through the ceramics were measured using a UV-vis spectrometer and a beam profile camera, respectively (n = 3). The DC and RP were measured in real-time using mid infrared spectroscopy in attenuated total reflectance (ATR) mode (n = 3). FS and FM were measured using a universal testing machine (n = 5). Statistical analyses were performed on LT, DC, RP, FS, and FM data using a general linear model, and supplementary ANOVA and post hoc Tukey multiple comparison test were also performed (α = .05). RESULTS: Thicknesses, shades, photoinitiator type, and fillers load significantly influenced the optical and mechanical characteristics of the resin-based materials (p < 0.05). The BL3 shade ceramic provided higher values of DC, RP, FS, FM, and LT compared with the A1 shade (p < 0.05). Increasing ceramic thickness decreased the properties of the resin-based materials (p < 0.05). Generally, TPO improved mechanical properties of the resin cement compared with CQ (p < 0.05). SIGNIFICANCE: The luting process of indirect restorations may be improved by using high molar absorptivity, more reactive, and more efficient photoinitiators such as TPO, as opposed to conventional CQ. The use of such initiator may allow the placement of thicker and more opaque indirect restorations.

Biaxial flexural strength of hydrothermally aged resin-based materials.

PURPOSE: The strength of temporary restorations plays a vital role in full-mouth reconstruction, and it can be impacted by the aging process. The aim of this in vitro study was to evaluate the biaxial flexural strength and fractographic features of different resin-based materials submitted to thermal aging. MATERIAL AND METHODS: One hundred and ninety-two resin disc-shaped specimens (6.5 mm in diameter and 0.5 mm in thickness) were fabricated and divided into six experimental groups according to the resin-based materials (Filtek Bulk-Fill flowable resin; J-Temp temporary resin; and Fuji Lining glass ionomer cement) and aging process (before and after thermal cycling). Biaxial flexural strength test was performed using a universal testing machine at a crosshead speed of 0.5 mm/min before and after thermal cycling (5 °C and 55 °C, 5760 cycles, 30 s). The mechanical properties were assessed using Weibull parameters (characteristic strength and Weibull modulus) (n = 30). Fractured specimens were examined under a polarized light stereomicroscope to identify crack origin and propagation direction. The surface microstructure of the resin-based materials was assessed by scanning electron microscopy (n = 2). The Weibull modulus (m), characteristic strength, and reliability properties were calculated, and a contour plot was used to detect differences among groups (95% confidence interval). RESULTS: The Weibull modulus (m), characteristic strength, and reliability of the resin-based compounds were influenced by material type and thermal aging (p < 0.05). Weibull modulus (m) revealed no differences when comparing the materials and aging process (p > 0.05), except for the preceding aging period where Filtek Bulk-Fill exhibited higher values compared to J-Temp (p < 0.05). Filtek Bulk-Fill demonstrated superior characteristic strength and reliability compared to J-Temp and Fuji Lining before and after thermal cycling (p < 0.05). Fractography of the resin-based materials showed fractures originating from surface defects exposed to tensile side and their propagation toward the compressive side. Generally, no differences in surface microstructure were observed on micrographs before and after thermal aging for Filtek Bulk-Fill and Fuji Lining. However, the aging process developed flaws in J-Temp. CONCLUSION: Resin-based material composition resulted in different flexural strength performance, impacting the Weibull modulus (m), characteristic strength, and reliability of the resin-based restorations.

A systematic review and meta-analysis on the effects of phototherapy on postoperative pain in conventional endodontic reintervention.

OBJECTIVES: This systematic review and meta-analysis (SRM) aimed to evaluate the efficacy of laser phototherapy (LPT) on the reduction in postoperative pain (PP) of endodontic origin after conventional/non-surgical reintervention of root canals. METHODS: This SRM was registered with PROSPERO (CRD42021243500) and followed the guidelines of the Preferred Reporting Items for Systematic Reviews and Meta-Analysis. Meta-analysis was conducted using R software with the "META" package, the mean difference (MD) measure of effect was calculated, and the fixed effect model was applied with a 95% confidence interval (CI). The Cochrane collaboration scale was used to assess the risk of bias and the GRADE tool to assess the quality of evidence. RESULTS: Initially, 1028 articles were found, and five articles were included. Most studies were classified as "low" risk of bias. Of the five clinical studies, four showed a significant decrease in PP after endodontic reintervention in the LPT groups compared to the control group, especially in the first four days after the intervention. In symptomatic teeth with multiple roots, LPT led to less PP at 24 h (MD -0.52 [-1.03; -0.02] p = .04). However, no significant difference between the groups was found at 48 and 72 h (p > .05). The certainty of the evidence was classified as low. CONCLUSION: Despite the limitations of this SRM, LPT was shown to be a promising alternative for reducing and controlling PP in conventional endodontic reintervention. CLINICAL SIGNIFICANCE: The use of LPT in endodontic reintervention may be a safe and promising alternative to clinically efficacious agent for use in the management of PP in this procedure.

The impact of methylene blue photosensitizer, aPDT and a calcium hydroxide-based paste on the physicochemical and mechanical characteristics of root canal dentin and the bonding interface of fiberglass posts.

PURPOSE: To investigate the influence of methylene blue (MB)-mediated antimicrobial photodynamic therapy (aPDT) and calcium hydroxide (CH) medication on the mechanical characteristics, degree of conversion (DC), quantification, and volume of gaps at the adhesive interface of glass fiber posts (GFPs) luted to distinct thirds of root canal dentin. Additionally, the microhardness (MH), elastic modulus (Eit), morphology, and chemical structure of the intraradicular dentin were assessed. MATERIALS AND METHODS: 6 experimental groups were formed by sorting 102 bovine incisors. Canals receiving deionized water irrigation as a negative control; canals receiving deionized water irrigation and filled with CH as a positive control; groups treated with CH + MB at 50 and 100 mg/L without irradiation; and groups treated with CH + MB at 50 and 100 mg/L irradiated by red laser for 60 s (660 nm; 100 mW; 6.5 J; 72 J/cm2). MH, Eit, and DC properties were evaluated for both the resin cement layer and root dentin substrate (n = 8). Volume and quantification of gaps at the bonding interface (n = 6), and dentin morphology and chemical content were investigated (n = 3). Data were analyzed using a repeated-measures 2-way ANOVA followed by Tukey post hoc analysis (α = 0.05). RESULTS: The distinct intraradicular thirds and treatment with MB-mediated aPDT, whether activated or not, in combination with CH, had a significant impact on the mechanical characteristics of the root dentin. This effect was also observed in the MH, Eit, DC, quantification, and volume of gaps at the luting interface (P < .05). In general, a higher concentration of MB, whether activated by a red laser or not, led to lower values in the mechanical properties of the root dentin, as well as in MH, Eit, and DC at the adhesive interface (P < .05). Additionally, these groups exhibited higher values for quantification and volume of gaps at the luting substrate (P < .05). Scanning electron micrographs and energy dispersive X-ray spectra showed qualitative similarity among all groups, except for the negative experimental control group. CONCLUSIONS: MB-mediated aPDT at 50 mg/L, in combination with CH, demonstrated favorable physico-chemical and mechanical characteristics in intraradicular dentin, along with satisfactory mechanical features and the adhesive interface integrity for GFPs at all intraradicular depths. CLINICAL SIGNIFICANCE: MB-mediated aPDT at a concentration of 50 mg/L combined to CH medication represents a suitable choice for photosensitization in the context of intracanal disinfection following the biomechanical procedure and prior to luting of intraradicular restorations.

Influence of bioceramic sealers on dentinal tubule penetration and antimicrobial effectiveness: a systematic review and meta-analysis of in vitro studies.

The aim of this systematic review and meta-analysis (SRM) was to evaluate whether bioceramic sealers have better penetration capacity in dentinal tubules and antimicrobial activity when compared to AH Plus® sealer. This SRM was recorded in the Open Science Framework database and followed the guidelines of the PRISMA 2020. Five databases were searched by two independent reviewers. Only in vitro studies that evaluated the effects of bioceramic sealers on dentinal tubule penetration and antimicrobial activity outcomes compared to AH Plus® sealer were included. Meta-analysis was conducted using R software, using the effect measure of the standardized mean difference (SMD) and inverse variance method. A modified Joanna Briggs Institute's Checklist was used for the risk of bias assessment. A total of 1486 studies were identified, and only 54 studies that fulfilled our eligibility criteria were included in this review. There was no statistical difference between the sealers evaluated for dentinal tubule penetration, in the thirds evaluated: coronal SMD 0.58 [0.14; 1.31], p = 0.12; middle SMD 0.07 [0.54; 0.39], p = 0.75; and apical SMD 0.08 [0.73; 0.56], p = 0.80. Both sealers demonstrated similar antimicrobial action (SMD [3.42; 5.32], p = 0.67 and SMD 0.67 [1.89; 0.55], p = 0.28). The studies presented a low risk of bias. Based on the in vitro studies included and according to the limitations of the present review, the data suggest that bioceramic and AH Plus® sealers present similar penetration capacity in dentinal tubules and antimicrobial effect, making them suitable materials to be considered in clinical practice.

Hydrofluoric acid concentration and etching time affect differently the microstructure and surface properties of pressed lithium disilicate glass ceramics.

OBJECTIVE: To evaluate the effect of different hydrofluoric acid concentrations and etching times on the surface, chemical composition and microstructure of lithium disilicate. MATERIAL AND METHODS: Ninety specimens of pressed lithium disilicate (LDS) were obtained (IPS e.max Press, Rosetta SP and LiSi Press). The specimens of each material were divided in two groups according to the hydrofluoric acid concentration: 5% and 10% (n = 15/group), and subdivided according to the etching time: 20, 40 and 60 s (n = 5/group). Crystalline evaluations and chemical composition were performed through x-ray diffraction (XRD) and energy-dispersive x-ray spectroscopy (EDS), respectively. Microstructural analyses were performed by scanning electron microscope (SEM), surface roughness (Ra), and material thickness removal evaluation. Thickness removal and Ra data were analyzed by ANOVA and Tukey test (p < 0.05). RESULTS: XRD demonstrated characteristic peaks of lithium disilicate crystals, lithium phosphate and of a vitreous phase for all materials. EDS identified different compositions and SEM confirmed different surface responses to acid etching protocols. Material and etching time influenced Ra and material thickness removal (p < 0.05). CONCLUSION: Hydrofluoric acid concentration and etching time affect the surface characteristics of LDS differently. LiSi Press presented higher resistance to hydrofluoric acid etching compared to e.max Press and Rosetta SP. CLINICAL SIGNIFICANCE: Applying the appropriate etching protocol is pivotal to avoid excessive material removal and to prevent jeopardize the mechanical and optical properties of the material.

Minimally processed recycled yttria-stabilized tetragonal zirconia for dental applications: Effect of sintering temperature on glass infiltration.

This study aimed to develop a recycling process for the remnants of milled 3Y-TZP and enhance their properties using glass infiltration. 3Y-TZP powder was gathered from the vacuum system of CAD-CAM milling equipment, calcined and sieved (x < 75 µm). One hundred twenty discs were fabricated and pre-sintered at 1000 °C/h. These specimens were then divided into four groups, categorized by glass infiltration (non-infiltrated [Zr] or glass-infiltrated [Zr-G]) and sintering temperature (1450 °C [Zr-1450] or 1550 °C [Zr-1550]/2h). After sintering, the specimens were characterized by X-Ray Diffraction (XRD), relative density measurement, and scanning electron microscopy and energy dispersive spectroscopy (SEM-EDS). The biaxial flexural strength test was performed according to the ISO 6872 and followed by fractographic analysis. Subsequent results were analyzed using Weibull statistics. Relative density values of the sintered specimens from Zr-1450 and Zr-1550 groups were 86.7 ± 1.5% and 92.2 ± 1.7%, respectively. Particle size distribution revealed particles within the range of 0.1-100 µm. XRD analysis highlighted the presence of the ZrO2-tetragonal in both the Zr-1450 and Zr-1550 groups. Glass infiltration, however, led to the formation of the ZrO2-monoclinic of 9.84% (Zr-1450-G) and 18.34% (Zr-1550-G). SEM micrographs demonstrated similar microstructural characteristics for Zr-1450 and Zr-1550, whereas the glass-infiltrated groups exhibited comparable infiltration patterns. The highest characteristic strength was observed in the glass-infiltrated groups. Fractographic analyses suggested that fracture origins were related to defects on the tensile side, which propagated to the compression side of the samples. Both the sintering temperature and glass infiltration significantly influenced the mechanical properties of the 3Y-TZP recycled.

Do different adhesives influence the color stability and fluorescence of composite restorations after aging?

This study aimed to evaluate the influence of dental adhesive color on the chromatic stability and fluorescence intensity of composite resin restorations of different thicknesses. Ninety bovine enamel samples were obtained and restored with resin composite varying thicknesses of restorative material and enamel (1.0 mm enamel and 1.0 mm composite; 1.5 mm enamel and 0.5 mm composite; 0.5 mm enamel and 1.5 mm composite). The restorations were made of composite resin (Opallis E-bleach H) using different types of dental adhesives: Ambar, Ambar APS, and Single Bond Universal (n=10). The samples were subjected to color measurement tests in a spectrophotometer using CIEDE2000 and fluorescence intensity measurements before and after aging in a red wine coloring solution. Data were subjected to analysis of variance (ANOVA) and Tukey's test (α = 0.05). There were no statistically significant changes in color stability or fluorescence intensity for restorations made of different materials or thicknesses (p>0.05). Single Bond Universal showed greater color stability at 0.5 mm thickness (ΔE00 = 4.4 ± 1.6) compared to other thicknesses of the same material (p=0.003), as well as a greater difference in fluorescence intensity after aging at 1.5 mm thickness (-414.9 ± 103.8) compared to other materials (p=0.0002). Overall, it was concluded that the different adhesive systems did not influence the color stability and fluorescence of restorations of different thicknesses.

In vitro assessment of the effect of luting agents, abutment height, and fatigue on the retention of zirconia crowns luted to titanium base implant abutments.

STATEMENT OF PROBLEM: The bonding of implant-supported prostheses is determined by abutment material, convergence angle, height, surface treatment, and luting agents. However, studies evaluating the bonding of luting agents to titanium base abutments with different heights under fatigue conditions are scarce. PURPOSE: The purpose of this in vitro study was to evaluate the retention of zirconia crowns bonded with different luting agents to titanium base abutments of different heights before and after fatigue testing. MATERIAL AND METHODS: Zirconia crowns were designed, milled, and distributed into 4 experimental groups according to the luting agents (G-Multi Primer/G-Cem LinkForce [MP/GC] and Scotchbond Universal/RelyX Ultimate [SU/RU]) and titanium base abutment heights (2.5 mm and 4 mm) (n=10). Pull-out testing was performed in a universal testing machine at a crosshead speed of 1 mm/min until crown displacement. Fatigue testing was performed by an electric precision fatigue simulator (1×106 cycles; 100 N; and 15 Hz), followed by pull-out testing of fatigued specimens. Collected data were statistically evaluated by using a linear mixed model after post hoc comparisons by the least significant difference test (α=.05). RESULTS: Luting agents, abutment heights, and fatigue influenced the bonding retention of zirconia crowns to titanium base abutments. SU/RU agents promoted higher pull-out compared with MP/GC for both abutment heights before and after fatigue. Higher abutment height increased pull-out regarding lower abutment height for SU/RU materials before and after fatigue testing. Although fatigue had no significant effect on the pull-out of MP/GC, lower bond retention was observed for SU/RU after fatigue, regardless of abutment height. CONCLUSIONS: Luting agent composition and the interaction with abutment height and fatigue influenced the retention of zirconia crowns to titanium base abutments.

Cranial anatomical structures with high sexual dimorphism in metric and morphological evaluation: A systematic review.

The mastoid process has attracted the attention of several researchers due to its protected position at the base of the skull and the fact that it is relatively compact, in addition to being highly resistant and dimorphic, considered as a gold standard anatomical structure in the determination of the sexual dimorphism of skulls. However, intrinsic and extrinsic factors may influence this anatomical structure over time, providing contradictory and ambiguous data. Therefore, other anatomical structures need to be evaluated concurrently with the mastoid process to provide better accuracy and reliability of skull sexual dimorphism data. Thus, the objective of this systematic review was to evaluate the degree of reliability of the mastoid process to determine sexual dimorphism compared to other dimorphic structures, since there are still no systematic reviews on the subject in the literature. This review follows the guidelines of the Preferred Reporting Items for Systematic Reviews and Meta-Analysis (PRISMA) and was recorded in the Prospective International Systematic Reviews Registry (PROSPERO) (CRD 42023395167 Systematic Registry) (CRD420223). The inclusion criteria for selecting the studies were based on the PICO question: "Are skull anatomical structures reliable as alternatives to determine sexual dimorphism compared to the mastoid process?". A literature search for studies was performed in the MEDLINE Scopus, Web of Science, LILACS, and Cochrane Library databases. The Kappa agreement presented an approval level of (k = 0.93). This systematic review analyzed 13 ex-vivo studies published between 2008 and 2023. The risk of bias was considered low in 12 of the studies, and high in 1 study. Based on the findings, it can be concluded that even with the limitations of this systematic review, quantitative and qualitative analyses are essential in sexual identification of human skulls, and different anatomical structures can be used as references in addition to the mastoid process, with high reliability and precision, among them the; glabella, frontal profile, superciliary arch, bizygomatic width, maximum cranial length, and nasal height.

Does the use of antioxidant agents after dental bleaching compromise the aesthetic results of ceramic laminate veneers?

PURPOSE: This in vitro study aimed to evaluate the aesthetic compromise generated in adhesive interface of ceramic laminate veneer luted after tooth bleaching and the use of antioxidant agents. Thus, the chromatic coordinates and whitening index (WID) were evaluated, comparing whiteness changes (ΔWID) results to perceptibility and acceptability thresholds. MATERIAL AND METHODS: In total, 88 bovine enamel samples (7 × 8 × 4 mm; n = 8) were submitted to the ceramic laminate veneer luting protocol according to surface treatment (unbleached and bleached enamel), antioxidant agents (control; 10% ascorbic acid and 10% α-tocopherol), and luting periods (after 24 h and after 14 days). To lute IPS e.max ceramic restorations (7 × 8 × 0.6 mm), Tetric N-Bond Universal adhesive system and Variolink Aesthetic LC resin cement were used. An ultraviolet-visible spectrophotometer (UV-VIS) was utilized to measure CIE L*a*b* coordinates prior to and after UV-B artificial accelerated aging for 252, 504, and 756 h. L*, a*, and b* axes were evaluated separately, and the whitening stability (ΔWID) effect was assessed by varying the whiteness index for dentistry (WID). The 50:50% visual threshold was used to evaluate ΔWID values (whiteness perceptibility [WPT] and whiteness acceptability [WAT]). Color parameters changes (ΔL*Δa*Δb*), WID, and ΔWID data were subjected to 2-way repeated measures ANOVA followed by Tukey's test (α = 0.05). RESULTS: Different UV-aging periods influenced the chromatic coordinates, WID, and ΔWID of the ceramic restorations regardless of the bleaching treatment, antioxidant solutions and luting periods (P < .05). In general, ΔWID values after UV-aging periods were above perceptibility and acceptability thresholds (WPT = 0.72 and WAT = 2.62, respectively) for all experimental groups (P < .05). Unbleached and 10% ascorbic acid-treated enamels luted after 14 days of the antioxidant action exhibited lower ΔL* and Δb* values, while control group showed lower Δa* values. All experimental groups showed similar performance on ΔWID compared to the control group, regardless of the UV-aging period analyzed (P > .05). CONCLUSION: α-tocopherol is a suitable antioxidant solution to be used 24 h post enamel bleaching not compromising clinical acceptability of ceramic laminate veneers. CLINICAL RELEVANCE: The adhesive interface of ceramic laminate veneers may appear darker after the use of antioxidant agents affecting the clinical acceptability of the restorations.

Postoperative pain after root canal filling with bioceramic sealers: a systematic review and meta-analysis of randomized clinical trials.

The aim of this systematic review and meta-analysis (SRM) was to assess postoperative pain (PP) after endodontic treatment with bioceramic root canal sealer compared to AH Plus® sealer. This SRM was carried out in accordance with the items on the PRISMA 2020 checklist and Cochrane guidelines and registered in PROSPERO (CRD42021259283). Only randomized clinical trials (RCTs) were included. Meta-analysis was conducted using R software, the standardized means difference (SMD) measure of effect was calculated for quantitative variables, and the odds ratio (OR) for binary variables. The Cochrane tool (RoB 2.0) was used to assess the risk of bias, and the Grading of Recommendations Assessment, Development, and Evaluation (GRADE) approach was used to assess the quality of evidence. Qualitative and quantitative analysis included 18 and 17 studies, respectively. For quantitative variables, the bioceramic root canal sealer presented less occurrence of postoperative pain than the AH Plus® sealer in 24 h (SMD - 0.17 [- 0.34; - 0.01], p = 0.0340). For binary variables, there was no difference observed between the sealers evaluated, except for sealer extrusion where the bioceramic group had lower post-filling material extrusion (OR 0.52 [0.32; 0.84], p = 0.007). Regarding the risk of bias analysis, low risk was observed for most domains, except allocation that was considered unclear, while the certainty of evidence ranged from moderate to low. The results showed that bioceramics sealers reduced postoperative endodontic pain only after 24 h and showed less sealer extrusion compared to the AH Plus® sealer. However, more robust and standardized clinical trials are needed to confirm the results with less heterogeneity and higher quality of evidence.

Effect of Antioxidant Agents After Dental Bleaching on Color Stability and Mechanical Properties of Bonding Interface Components in Ceramic Laminate Veneer Luting.

PURPOSE: Few studies have evaluated the influence of antioxidant agents on the optical and mechanical properties of ceramic laminate veneers after dental bleaching. Thus, this in vitro study aimed to evaluate the influence of antioxidant agents on the color stability and mechanical properties, such as nanohardness (HIT), elastic modulus (Eit*), and degree of conversion (DC) of the bonding interface components after dental bleaching in ceramic laminate veneer luting. METHODS AND MATERIALS: A total of 143 bovine teeth were distributed into experimental groups, according to the procedure method (unbleached or bleached with Whiteness HP Maxx 35%), antioxidant type (control, 10% ascorbic acid, or 10% α-tocopherol), and luting period (24 hours or 14 days) (n=13). The Tetric N-Bond Universal adhesive system and Variolink Esthetic LC resin cement were used as luting agents to lute IPS e.max ceramic restorations (0.6 mm in thickness) to enamel. A UV-visible spectrophotometer was used to assess color stability before and after UV-B artificial accelerated aging for 252, 504, and 756 hours (n=8). The HIT and Eit* of the adhesive and resin cement were measured using a nanohardness tester under a load of 1000 µN, and the DC was measured using a micro-Raman spectrometer (n=5). The color stability and mechanical properties were measured and evaluated by twoway and one-way ANOVA, respectively, and Tukey test (α=0.05). RESULTS: Distinct aging periods exerted significant changes on the color stability of the restorations luted in enamel associated with ascorbic acid, bleached and unbleached, and the bleached enamel under no antioxidant agent action, for the experimental groups evaluated after 14 days (p<0.05). The use of the α-tocopherol antioxidant solution after the bleaching process for 24 hours did not alter the optical and mechanical properties of the adhesive interface of the laminate restorations compared to those of the control group (p>0.05). CONCLUSION: The use of a 10% α-tocopherol antioxidant solution produced promising results, suggesting that it could be mediately used after tooth bleaching to lute ceramic laminate veneers.

A systematic review of photogrammetry as a reliable methodology in gender identification of human skull.

One of the most important parameters in the identification process in forensic Medicine and Dentistry is the determination of sex through the skull, based on morphological and metric dimorphism. Photogrammetry is an affordable option that allows the reconstruction of position, orientation, shape, and size, allowing the performance of quantitative and qualitative analyzes to identify the sex of the individual. However, there are few systematic reviews in the literature validating whether photogrammetry is a reliable methodology for sexual identification using human skulls. Therefore, the objective of the current systematic review was to validate whether photogrammetry of dry skulls is reliable as a method for calculating sex in human identification. This revision follows the guidelines of the Preferred Reporting Items for Systematic Reviews and Meta-Analysis (PRISMA) and was recorded in the Prospective International Systematic Reviews Registry (PROSPERO) (CRD420223 Systematic Registry) (CRD420223). The inclusion criteria for selecting the studies were based on the PICO question: "Is test photogrammetry reliable as a method for estimating sex in human identification?". A literature search for studies was performed in the databases MEDLINE Scopus, Web of Science, LILACS, and the Cochrane Library. The Kappa agreement presented an approval level of (k = 0.93). This systematic review analyzed 11 ex-vivo studies published between 2001 and 2021. The risk of bias was considered low in 8 of the studies, and high in 3 studies. Based on this systematic review, it can be concluded that the photogrammetry method is viable and reliable in identifying sexual dimorphism.

In vitro study on how photodynamic therapy and calcium hydroxide medication influence adhesive interface properties of glass-fiber posts to intraradicular dentin.

PURPOSE: This in vitro study evaluated the influence of antimicrobial photodynamic therapy (aPDT), using methylene blue (MB) as photosensitizer (PS) and calcium hydroxide (CH) as intracanal medication on adhesive bond strength, sealing, and integrity of the luting interface of glass-fiber posts to different thirds of endodontically treated root canal dentin. MATERIAL AND METHODS: 102 incisors were sorted into 6 groups: a negative control irrigated with deionized water; a positive control irrigated with deionized water and filled with CH; CH + MB 50 mg/L without laser radiation; CH + MB 100 mg/L without laser radiation; CH + MB 50 mg/L radiated by red laser; and CH + MB 100 mg/L radiated by red laser. Push-out bond strength (n = 8), adhesive interface sealing (n = 3), and volume and quantification of voids (n = 6) were assessed using a universal testing machine, confocal laser scanning microscope, and computerized microtomography, respectively. Scanning electron micrographs were obtained from representative samples to qualify the fracture patterns. Push-out bond strength and adhesive interface integrity data were subjected to 2-way ANOVA for repeated measures followed by Tukey's test (α = 0.05). Adhesive interface sealing was evaluated by the inter-examiner Kappa test and submitted to Kruskal-Wallis and Dunns tests (α = 0.05). RESULTS: Assessing the apical region, the positive control and MB100WA + Ca(OH)2 groups showed lower adhesive bond strength compared to the MB100A + Ca(OH)2 group (P < 0.05). The cervical third showed higher bond strength than the apical third for the positive control, MB50WA + Ca(OH)2, MB100WA + Ca(OH)2, and MB50A + Ca(OH)2 groups (P < 0.05). A prevalence of mixed failure was observed in all experimental groups. There were no statistically significant differences in adhesive interface sealing for any of the parameters assessed (P > 0.05). MB100WA + Ca(OH)2 and MB100A + Ca(OH)2 groups promoted a higher volume and quantification of voids compared to the negative control group evaluating the cervical third (P < 0.05). In general, there were no differences in the quantification of voids comparing the intraradicular thirds (P > 0.05), differently to the volume of voids in which, in general, the cervical third promoted higher values compared to the middle and apical thirds (P < 0.05). CONCLUSION: aPDT with methylene blue PS at 50 mg/L associated with calcium hydroxide as intracanal medication demonstrated satisfactory bond strength, sealing, and integrity of the adhesive interface at any intraradicular depth.

Antimicrobial effectiveness of ultrasonic irrigation in root canal treatment: a systematic review of randomized clinical trials and meta-analysis.

OBJECTIVE: The objective of this systematic review and meta-analysis (SRM) was to answer the question as to whether the use of ultrasonic irrigation (UI) results in better antimicrobial activity in root canal disinfection compared to conventional irrigation (CI). METHODS: A literature search was performed in the main scientific databases, carried out until October 2021. The eligibility criteria were randomized clinical trials (RCTs). Two meta-analyses were conducted using R software with the "META" package. The mean difference (MD) and odds ratio (OR) measure of effect were calculated. The fixed effect model was applied with a 95% confidence interval. The Cochrane collaboration scale was used to assess risk of bias and the GRADE tool to assess the quality of evidence. RESULTS: A total of 1782 records were screened, and 12 studies meeting the criteria were included in this review. A low risk of bias was observed for most domains, except allocation concealment that was considered unclear. The certainty of evidence was classified as moderate in the OR meta-analyses and low in the MD meta-analyses. Ultrasonic irrigation resulted in a better antimicrobial effect in both meta-analyses, MD 1.42 [1.60; 1.23] p < 0.0001, I2 = 80%; and OR 3.86 [1.98; 7.53] p< 0.0001, I2 = 28.7%. CONCLUSION: Within the limitations of this SRM, UI presented better antimicrobial efficacy than CI. CLINICAL RELEVANCE: UI should be used by clinicians as it promotes better antimicrobial efficacy in patients undergoing endodontic treatment.