RESUMEN
This study assessed the physicochemical and antibiofilm properties of white mineral trioxide aggregate (MTA) associated with 1 or 2% of farnesol. Setting time was evaluated based on ISO 6876/2012. Radiopacity was evaluated by radiographic analysis. pH was assessed after time intervals of 1, 3, 7, 14, 21, and 28 days. Solubility (% mass loss) and volumetric change (by micro-CT) of the cements were evaluated after immersion in distilled water. The presence of voids inside the materials was assessed by using micro-CT. Antibiofilm activity against Enterococcus faecalis was evaluated by crystal violet assay and the modified direct contact test performed with biofilm previously formed on bovine root dentin for 14 days. Data were submitted to ANOVA/Tukey tests with 5% significance level. The incorporation of farnesol into MTA increased its setting time, but decreased its solubility at 30 days and its volumetric loss in all periods (p < 0.05). Radiopacity and solubility after 7 days were similar among the materials (p > 0.05). The association of farnesol showed the highest pH value after 1 and 3 days (p < 0.05). The association of farnesol with MTA promoted a decrease in the presence of voids, and increased the antimicrobial activity on biofilm biomass of E. faecalis (p < 0.05). In conclusion, the addition of farnesol can be suggested to improve the antimicrobial properties and the consistency of MTA.
Asunto(s)
Compuestos de Aluminio , Biopelículas , Compuestos de Calcio , Combinación de Medicamentos , Enterococcus faecalis , Farnesol , Ensayo de Materiales , Óxidos , Materiales de Obturación del Conducto Radicular , Silicatos , Solubilidad , Silicatos/farmacología , Silicatos/química , Óxidos/farmacología , Óxidos/química , Biopelículas/efectos de los fármacos , Compuestos de Calcio/farmacología , Compuestos de Calcio/química , Enterococcus faecalis/efectos de los fármacos , Compuestos de Aluminio/farmacología , Compuestos de Aluminio/química , Farnesol/farmacología , Farnesol/química , Concentración de Iones de Hidrógeno , Factores de Tiempo , Bovinos , Materiales de Obturación del Conducto Radicular/farmacología , Materiales de Obturación del Conducto Radicular/química , Animales , Análisis de Varianza , Reproducibilidad de los Resultados , Dentina/efectos de los fármacos , Valores de Referencia , Propiedades de Superficie/efectos de los fármacosRESUMEN
Objective: To evaluate the solubility and the volumetric and morphological alterations of bioceramic filling material (Bio-CP) for primary teeth. Materials and Methods: Bio-CP, Calen thickened with zinc oxide (Calen-ZO), and with zinc oxide eugenol (ZOE) were placed in 1- or 2-mm-diameter polyethylene tubes and immersed in water or phosphate-buffered saline (PBS) for 30 days. The solubility (mass loss) was assessed using methodology modified from ISO 6876. Filling capacity, volumetric changes, and presence of voids were assessed by microcomputed tomography (micro-CT). The surface distribution of the chemical elements and the crystalline phases was evaluated by energy scattering X-ray scanning electron microscopy (SEM-EDX) and X-ray diffraction (XRD) to detect hydroxyapatite precipitate and components. The Shapiro-Wilk, Kruskal-Wallis, and Dunn's or two-way ANOVA and Tukey post hoc test were used (α = 0.05). Results: The solubility was ZOE > Calen-ZO = Bio-CP. Calen-ZO and Bio-CP were more soluble in water than in PBS. All the materials showed greater solubility in 2-mm tube diameter in both PBS and distilled water, except for Bio-CP in distilled water, which showed no difference between both tube diameters (1 and 2 mm). Only Calen-ZO and ZOE were analyzed by micro-CT, because Bio-CP separated into two phases during scanning. Calen-ZO had greater volumetric loss and presence of voids than ZOE in water, but there was no difference in PBS. The hydroxyapatite precipitate on the surface of Bio-CP and Calen-ZO was detected after immersion in PBS. Conclusion: Although Bio-CP had acceptable solubility and filling capacity, its composition did not allow a proper volumetric and void assessment. From a clinical perspective, Bio-CP has the potential to become a suitable material for root canal filling in primary teeth. Nonetheless, its composition must first be revised to achieve better chemical stability prior to its recommendation.
RESUMEN
This study evaluated the biocompatibility, bioactivity, porosity, and sealer/dentin interface of Sealer Plus BC (SP), Bio-C Sealer (BIOC), TotalFill BC Sealer (TF), and AH Plus (AHP). Dentin tubes filled with the sealers and empty tubes (control group) were implanted in the subcutaneous tissue of rats for different periods (n = 6 per group/period). Number of inflammatory cells (ICs), capsule thickness, von Kossa reaction, interleukin-6 (IL-6) and osteocalcin (OCN) were evaluated. Porosity and voids in the interface dentin/sealers were assessed by micro-computed tomography. The data were submitted to ANOVA/Tukey's tests (α = 0.05). Greater capsule thickness, ICs and IL-6 immunolabeling cells were observed in AHP. No significant difference in thickness of capsule, ICs, and IL-6- immunolabeling cells was detected between SP and TF, in all periods, and after 30 and 60 days between all groups. At 60 days all groups had reduction in capsule thickness, ICs and IL-6 immunolabeling cells. Von Kossa-positive and birefringent structures were observed in the capsules around the sealers. BIOC, SP, and TF exhibited OCN-immunolabeling cells. All sealers had porosity values below 5%, besides low and similar interface voids. BIOC, SP and TF are biocompatible, bioactive, and have low porosity and voids. The dentin-tube model used is an alternative for evaluating bioceramic materials.
Asunto(s)
Materiales Biocompatibles , Dentina , Ensayo de Materiales , Animales , Porosidad , Dentina/química , Dentina/metabolismo , Materiales Biocompatibles/química , Materiales Biocompatibles/farmacología , Ratas , Cerámica/química , Interleucina-6/metabolismo , Microtomografía por Rayos X , Masculino , Ratas Wistar , Selladores de Fosas y Fisuras/químicaRESUMEN
This study evaluated the effect of ultrasonic agitation on the filling capacity of ready-to-use calcium silicate-based sealer Bio-C Sealer (BCS, Angelus, Paraná, Brazil) or powder-liquid BioRoot RCS (BR, Septodont, Saint-Maur-des-Fossés, France) using curved artificial canals by micro-computed tomography (micro-CT). Additionally, flow (mm) and flow area (mm2) were evaluated for both materials. Acrylic resin main canal (60° curvature and 5 mm radius, with 3 lateral canals in the cervical, middle, and apical thirds) were prepared up to size 40/.05 (Prodesign Logic, Brazil). The agitation method was used with ultrasonic tip (US, Irrisonic, Helse, Brazil): BCS, BCS/US, BR, and BR/US. All specimens were filled using the single-cone technique. The samples were scanned by micro-CT (8,74 µm) after obturation. The percentage of filling material and voids were calculated. Flow was evaluated based on ISO 6876/2012 standards (mm) and area (mm2). The data were statistically analyzed using ANOVA and Tukey tests (α = 0.05). BR/US showed lower percentage of filling material in the lateral canals than and, BCS/US (p<0.05). BR/US resulted in a higher percentage of voids than BR in the lateral apical third (p<0.05). BCS showed higher flow than BR (p<0.05). BCS and BR presented proper filling capacity in the simulated curved canals regardless of the use of ultrasonic agitation. However, BR/US showed more voids in the apical third. BCS demonstrates higher filling ability.
Asunto(s)
Compuestos de Calcio , Materiales de Obturación del Conducto Radicular , Silicatos , Compuestos de Calcio/química , Materiales de Obturación del Conducto Radicular/química , Silicatos/química , Microtomografía por Rayos X/métodos , Polvos , Ultrasonido , Ensayo de Materiales , Obturación del Conducto Radicular/métodosRESUMEN
Both root canal sealer-based and supplementary protocols may influence removal of filling material during endodontic retreatment. Mesial root canals of extracted mandibular molars were prepared using HyFlex EDM 25/.08, and filled with a calcium silicate sealer (Bio-C Sealer), or an epoxy resin (AH Plus), using the single cone technique (n = 12). Retreatment was performed using ProDesign Logic (PDL) RT and PDL 35/.05. The specimens were randomly divided into two experimental groups (n = 12), and the sealers were distributed similarly. A supplementary protocol was performed with PDL 50/.01 or XP-endo Finisher. Root canal transportation and volume, in addition to the remaining filling material percentage were evaluated using high-resolution (5 µm voxel size) micro-CT. Statistical analysis was performed using t-tests (α = 0.05). Root canals filled with AH Plus presented high residual filling material (p < 0.05). Both protocols decreased residual volume of filling material in the apical third (p < 0.05). PDL 50/.01 increased the apical root canal volume (p < 0.05). No difference was observed between the systems regarding canal transportation (p > 0.05). In conclusion, AH Plus is more difficult to remove from the apical third than Bio-C Sealer. PDL 50/.01 and XP-endo Finisher enabled greater removal of filling materials in the apical third, in the retreatment of curved root canals, without promoting apical transport.
Asunto(s)
Resinas Epoxi , Ensayo de Materiales , Retratamiento , Materiales de Obturación del Conducto Radicular , Microtomografía por Rayos X , Materiales de Obturación del Conducto Radicular/química , Materiales de Obturación del Conducto Radicular/uso terapéutico , Humanos , Retratamiento/métodos , Resinas Epoxi/química , Resinas Epoxi/uso terapéutico , Preparación del Conducto Radicular/métodos , Preparación del Conducto Radicular/instrumentación , Cavidad Pulpar/diagnóstico por imagen , Cavidad Pulpar/efectos de los fármacos , Compuestos de Calcio/uso terapéutico , Silicatos/química , Reproducibilidad de los Resultados , Obturación del Conducto Radicular/métodos , Diente Molar , Valores de ReferenciaRESUMEN
Introduction: The anatomical configuration classified as Vertucci's type III is described as the second most prevalent in mandibular incisors. Methods: Thirty-six Vertucci's type III mandibular incisors were evaluated by micro-computed tomography (micro-CT) and divided into 3 groups (n = 12) according to the root canal preparation protocol (HyFlex CM [HCM], HyFlex EDM [HEDM], and Sequence Rotary File [SRF]). The teeth were scanned before and after performing 0.25 mm and 0.40 mm apical diameter preparations. The canal volume, dentin thickness, percentage of accumulated debris and untouched canal areas, transportation, and centering ability were measured. The data were statistically analyzed by ANOVA, Tukey, Kruskal-Wallis, and Dunn tests (P < 0.05). Results: The volume increase was more evident in the apical third. After 0.40 mm preparation, the SRF system provided a higher reduction (P < 0.05) in dentin thickness on the buccal surface 1 mm from the apex. There was higher canal transportation in the bucco-lingual direction. The 0.40 mm apical preparation reduced the percentage of untouched canal areas. The apical third had the highest percentage of untouched canal areas. The cervical third had the lowest volume of accumulated debris. Conclusions: Increasing the apical preparation to a diameter of 0.40 mm with the HCM, HEDM, and SRF systems in Vertucci's type III root canals of mandibular incisors proved to be safe and effective, reducing untouched canal areas. Clinical relevance: Root flattening can be intense to the point of generating a root canal bifurcation. Despite the decrease in the root canal diameter, a greater enlargement of the apical region is necessary and safe.
RESUMEN
Acidic pH can modify the properties of repair cements. In this study, volumetric change and solubility of the ready-to-use bioceramic repair cement Bio-C Repair (BCR, Angelus, Londrina, PR, Brazil) were evaluated after immersion in phosphate-buffered saline (PBS) (pH 7.0) or butyric acid (pH 4.5). Solubility was determined by the difference in initial and final mass using polyethylene tubes measuring 4 mm high and 6.70 mm in internal diameter that were filled with BCR and immersed in 7.5 mL of PBS or butyric acid for 7 days. The volumetric change was established by using bovine dentin tubes measuring 4 mm long with an internal diameter of 1.5 mm. The dentin tubes were filled with BCR at 37°C for 24 hours. Scanning was performed with micro-computed tomography (micro-CT; SkyScan 1176, Bruker, Kontich, Belgium) with a voxel size of 8.74 µm. Then, the specimens were immersed in 1.5 mL of PBS or butyric acid at and 37 °C for 7 days. After this period, a new micro-CT scan was performed. Bio-C Repair showed greater mass loss after immersion in butyric acid when compared with immersion in PBS (p<0.05). Bio-C Repair showed volumetric loss after immersion in butyric acid and increase in volume after immersion in PBS (p<0.05). The acidic pH influenced the solubility and dimensional stability of the Bio-C Repair bioceramic cement, promoting a higher percentage of solubility and decrease in volumetric values.
Asunto(s)
Óxidos , Materiales de Obturación del Conducto Radicular , Animales , Bovinos , Solubilidad , Óxidos/química , Compuestos de Calcio/química , Microtomografía por Rayos X , Ácido Butírico , Ensayo de Materiales , Cementos Dentales/química , Cementos de Ionómero Vítreo , Concentración de Iones de Hidrógeno , Silicatos/química , Materiales de Obturación del Conducto Radicular/químicaRESUMEN
AIM: To evaluate the inflammatory reaction and the ability to induce mineralization activity of a new repair material, NeoPUTTY (NPutty; NuSmile, USA), in comparison with Bio-C Repair (BC; Angelus, Brazil) and MTA Repair HP (MTA HP; Angelus, Brazil). METHODOLOGY: Polyethylene tubes were filled with materials or kept empty (control group, CG) and implanted in subcutaneous tissue of rats for 7, 15, 30, and 60 days (n = 6/group). Capsule thickness, number of inflammatory cells (ICs), fibroblasts, collagen content, and von Kossa analysis were performed. Unstained sections were evaluated under polarized light and by immunohistochemistry for osteocalcin (OCN). Data were submitted to two-way anova followed by Tukey's test (p ≤ .05), except for OCN. OCN data were submitted to Kruskal-Wallis and Dunn and Friedman post hoc tests followed by the Nemenyi test at a significance level of 5%. RESULTS: At 7, 15, and 30 days, thick capsules containing numerous ICs were seen around the materials. At 60 days, a moderate inflammatory reaction was observed for NPutty, BC while MTA HP presented thin capsules with moderate inflammatory cells. In all periods, NPutty specimens contained the highest values of ICs (p < .05). From 7 to 60 days, the number of ICs reduced significantly while an increase in the number of fibroblasts and birefringent collagen content was observed. At 7 and 15 days, no significant difference was observed in the immunoexpression of OCN (p > .05). At 30 and 60 days, NPutty showed the lowest values of OCN (p < .05). At 60 days, a similar immunoexpression was observed for BC and MTA HP (p > .05). In all time intervals, capsules around NPutty, BC, and MTA HP showed von Kossa-positive and birefringent structures. CONCLUSIONS: Despite the greater inflammatory reaction promoted by NeoPutty than BC and MTA HP, the reduction in the thickness of capsules, the increase in the number of fibroblasts, and the reduction in the number of ICs indicate that this bioceramic material is biocompatible Furthermore, NeoPutty presents the ability to induce mineralization activity.
Asunto(s)
Materiales Biocompatibles , Bismuto , Compuestos de Calcio , Ensayo de Materiales , Silicatos , Animales , Silicatos/farmacología , Compuestos de Calcio/farmacología , Ratas , Materiales Biocompatibles/farmacología , Ratas Wistar , Óxidos/farmacología , Combinación de Medicamentos , Masculino , Compuestos de Aluminio/farmacología , Cementos Dentales/farmacología , Fibroblastos/efectos de los fármacos , Colágeno/metabolismoRESUMEN
Intracanal medications are used in endodontic treatment due to their antibacterial activity and ability to induce the periapical repair. Among the intracanal medications, the Calen (CAL; SS. White, Brazil) is a calcium hydroxide-based medication that provides an alkaline pH and releases calcium, exerting an antimicrobial activity. Bio-C Temp (BIO; Angelus, Brazil), a ready-to-use bioceramic intracanal medication, was designed to stimulate the mineralized tissues formation. Here, we investigated the bioactive potential of BIO in comparison to the CAL in the rat subcutaneous. Polyethylene tubes filled with medications, and empty tubes (control group, CG) were implanted in the subcutaneous tissue of rats. After 7, 15, 30 and 60 days, the blood was collected for calcium (Ca+2) and alkaline phosphatase (ALP) measurement, and the capsules around the implants were processed for morphological analyses. The data were submitted to two-way ANOVA and Tukey test (p < 0.05). At 7, 15 and 30 days, the ALP level was grater in BIO and CAL than in CG (p < 0.0001). At 7 and 15 days, greater Ca+2 level was seen in the serum of CAL samples. From 7 to 60 days, an increase in the number of fibroblasts, osteocalcin- and osteopontin-immunolabelled cells was observed in BIO and CAL groups (p < 0.0001). In all periods, BIO and CAL specimens showed von Kossa-positive structures. Moreover, ultrastructural analysis revealed globules of mineralization in the capsules around the BIO and CAL specimens. Thus Bio-C Temp caused an increase in the ALP, osteocalcin and osteopontin, which may have allowed the formation of calcite, suggesting bioactive potential.
Asunto(s)
Calcinosis , Osteopontina , Animales , Ratas , Osteocalcina , Calcio , Tejido Subcutáneo , AntibacterianosRESUMEN
INTRODUCTION: The aim of this study was to evaluate the effectiveness of the XP-endo Finisher R (XPFR; FKG Dentaire, La Chaux-de-Fonds, Switzerland) or the Flatsonic ultrasonic tip (Helse Ultrasonic, Santa Rosa de Viterbo, SP, Brazil) in removing remaining filling material after the retreatment of flattened root canals using micro-computed tomographic imaging. METHODS: Twenty-four flattened distal root canals of mandibular molars with a buccolingual diameter 4 or more times larger than the mesiodistal diameter were prepared with Reciproc Blue (RB) R40 (VDW GmbH, Munich, Germany) and filled using the Tagger hybrid technique. All canals were retreated with RB R40, and apical enlargement was performed with RB R50 (VDW GmbH). The specimens were randomly distributed into 2 groups: XPFR or Flatsonic (n = 12). The percentage of remaining filling material after retreatment and centralization ability was evaluated. Data were submitted to Mann-Whitney, Wilcoxon, and unpaired t tests (α = 5%). RESULTS: Greater capacity to remove remaining filling material in the entire canal and the cervical and middle thirds was observed for the Flatsonic compared with the XPFR (P < .05). However, both supplementary cleaning techniques showed a similar percentage of residual filling material in the apical third (P > .05). No difference was observed in the centralization ability between the techniques (P > .05). CONCLUSIONS: The Flatsonic promotes greater removal of remaining filling material than the XPFR in the retreatment of flattened root canals. However, both supplementary cleaning approaches were similar in the apical third. The XPFR and Flatsonic were able to maintain root canal centralization.
Asunto(s)
Cavidad Pulpar , Diente Molar , Materiales de Obturación del Conducto Radicular , Preparación del Conducto Radicular , Microtomografía por Rayos X , Microtomografía por Rayos X/métodos , Humanos , Cavidad Pulpar/diagnóstico por imagen , Cavidad Pulpar/anatomía & histología , Materiales de Obturación del Conducto Radicular/uso terapéutico , Preparación del Conducto Radicular/instrumentación , Preparación del Conducto Radicular/métodos , Diente Molar/diagnóstico por imagen , Retratamiento , Obturación del Conducto Radicular/métodos , Terapia por Ultrasonido/métodosRESUMEN
The aim of this study was to evaluate the effect of radiopacifier calcium tungstate and manipulation with distilled water (DW) or liquid with additives (LA) on calcium silicate clinker Angelus (CL) properties, compared with MTA (Angelus, Brazil) and MTA Repair HP (MTAHP, Angelus, Brazil). The physicochemical properties, cellular viability and bioactivity were evaluated. ANOVA/Tukey and Bonferroni tests were performed (α = 0.05). There was no difference in material setting time (p > 0.05). MTA and MTAHP were similar (p > 0.05) and had greater radiopacity than CL + DW and CL + LA (p < 0.05). All experimental materials showed mass increase, alkalinisation capacity, besides biocompatibility and bioactivity at 3 and 7 days. The different liquids had no influence in the biological properties and bioactivity of the calcium silicate clinker Angelus. Calcium tungstate provided radiopacity, without changing the setting time, maintaining the mass increase and alkalinisation ability of the calcium silicate materials.
Asunto(s)
Óxidos , Materiales de Obturación del Conducto Radicular , Compuestos de Tungsteno , Óxidos/farmacología , Ensayo de Materiales , Compuestos de Calcio/farmacología , Compuestos de Calcio/química , Silicatos/farmacología , Silicatos/química , Combinación de Medicamentos , Compuestos de Aluminio/farmacología , Materiales de Obturación del Conducto Radicular/farmacología , Materiales de Obturación del Conducto Radicular/químicaRESUMEN
Abstract Acidic pH can modify the properties of repair cements. In this study, volumetric change and solubility of the ready-to-use bioceramic repair cement Bio-C Repair (BCR, Angelus, Londrina, PR, Brazil) were evaluated after immersion in phosphate-buffered saline (PBS) (pH 7.0) or butyric acid (pH 4.5). Solubility was determined by the difference in initial and final mass using polyethylene tubes measuring 4 mm high and 6.70 mm in internal diameter that were filled with BCR and immersed in 7.5 mL of PBS or butyric acid for 7 days. The volumetric change was established by using bovine dentin tubes measuring 4 mm long with an internal diameter of 1.5 mm. The dentin tubes were filled with BCR at 37°C for 24 hours. Scanning was performed with micro-computed tomography (micro-CT; SkyScan 1176, Bruker, Kontich, Belgium) with a voxel size of 8.74 µm. Then, the specimens were immersed in 1.5 mL of PBS or butyric acid at and 37 °C for 7 days. After this period, a new micro-CT scan was performed. Bio-C Repair showed greater mass loss after immersion in butyric acid when compared with immersion in PBS (p<0.05). Bio-C Repair showed volumetric loss after immersion in butyric acid and increase in volume after immersion in PBS (p<0.05). The acidic pH influenced the solubility and dimensional stability of the Bio-C Repair bioceramic cement, promoting a higher percentage of solubility and decrease in volumetric values.
RESUMEN
Abstract This study evaluated the effect of ultrasonic agitation on the filling capacity of ready-to-use calcium silicate-based sealer Bio-C Sealer (BCS, Angelus, Paraná, Brazil) or powder-liquid BioRoot RCS (BR, Septodont, Saint-Maur-des-Fossés, France) using curved artificial canals by micro-computed tomography (micro-CT). Additionally, flow (mm) and flow area (mm2) were evaluated for both materials. Acrylic resin main canal (60° curvature and 5 mm radius, with 3 lateral canals in the cervical, middle, and apical thirds) were prepared up to size 40/.05 (Prodesign Logic, Brazil). The agitation method was used with ultrasonic tip (US, Irrisonic, Helse, Brazil): BCS, BCS/US, BR, and BR/US. All specimens were filled using the single-cone technique. The samples were scanned by micro-CT (8,74 µm) after obturation. The percentage of filling material and voids were calculated. Flow was evaluated based on ISO 6876/2012 standards (mm) and area (mm2). The data were statistically analyzed using ANOVA and Tukey tests (α = 0.05). BR/US showed lower percentage of filling material in the lateral canals than and, BCS/US (p<0.05). BR/US resulted in a higher percentage of voids than BR in the lateral apical third (p<0.05). BCS showed higher flow than BR (p<0.05). BCS and BR presented proper filling capacity in the simulated curved canals regardless of the use of ultrasonic agitation. However, BR/US showed more voids in the apical third. BCS demonstrates higher filling ability.
Resumo Este estudo avaliou o efeito da agitação ultrassônica na capacidade de preenchimento de cimento pronto para uso à base de silicato de cálcio Bio-C Sealer (BCS, Angelus, Paraná, Brasil) ou pó-líquido BioRoot RCS (BR, Septodont, Saint-Maur -des-Fossés, França) utilizando canais artificiais curvos por microtomografia computadorizada (micro-CT). Adicionalmente, escoamento (mm) e área de escoamento (mm2) foram avaliados para ambos materiais. Please, replace the sentence highlighted in yellow to: O canal principal de resina acrílica (curvatura de 60° e raio de 5 mm, com 3 canais laterais nos terços cervical, médio e apical) foi preparado até o tamanho 40/.05 (Prodesign Logic, Brasil). O método de agitação foi utilizado com ponta ultrassônica (US, Irrisonic, Helse, Brasil): BCS, BCS/US, BR e BR/US. Todos os espécimes foram obturados usando a técnica de cone único. As amostras foram escaneadas por micro-CT (8,74 µm) após obturação. A porcentagem de material obturador e vazios foram calculados. O escoamento foi avaliado com base nas normas ISO 6876/2012 (mm) e área (mm2). Os dados foram analisados estatisticamente pelos testes ANOVA e Tukey (α = 0,05BR/US apresentou menor percentual de material obturador nos canais laterais que BCS e BCS/US (p<0,05). BR/US resultou em maior porcentagem de vazios que o BR no canal lateral do terço apical (p<0,05). BCS apresentou maior escoamento que BR (p<0,05)." BCS e BR apresentaram capacidade de preenchimento adequada nos canais curvos simulados independente do uso de agitação ultrassônica. No entanto, BR/US apresentou mais vazios no terço apical. BCS demonstra maior capacidade de preenchimento.
RESUMEN
Abstract Both root canal sealer-based and supplementary protocols may influence removal of filling material during endodontic retreatment. Mesial root canals of extracted mandibular molars were prepared using HyFlex EDM 25/.08, and filled with a calcium silicate sealer (Bio-C Sealer), or an epoxy resin (AH Plus), using the single cone technique (n = 12). Retreatment was performed using ProDesign Logic (PDL) RT and PDL 35/.05. The specimens were randomly divided into two experimental groups (n = 12), and the sealers were distributed similarly. A supplementary protocol was performed with PDL 50/.01 or XP-endo Finisher. Root canal transportation and volume, in addition to the remaining filling material percentage were evaluated using high-resolution (5 µm voxel size) micro-CT. Statistical analysis was performed using t-tests (α = 0.05). Root canals filled with AH Plus presented high residual filling material (p < 0.05). Both protocols decreased residual volume of filling material in the apical third (p < 0.05). PDL 50/.01 increased the apical root canal volume (p < 0.05). No difference was observed between the systems regarding canal transportation (p > 0.05). In conclusion, AH Plus is more difficult to remove from the apical third than Bio-C Sealer. PDL 50/.01 and XP-endo Finisher enabled greater removal of filling materials in the apical third, in the retreatment of curved root canals, without promoting apical transport.
RESUMEN
The aim of this study was to evaluate root canal preparation with nickel titanium rotary instruments and complementary preparation with ultrasonic tip in curved canals of mandibular molars with isthmus. Twenty-eight mesial roots of mandibular molars with curvature between 20° and 40° and presence of isthmus throughout the entire extension of the root canals were prepared using ProDesign Logic CM (PDL) up to size 40.05, or HyFlex EDM (HFEDM) up to size 40.04. Complementary preparation was performed in the isthmus region using the ultrasonic insert E18D (Helse, Istmo Diamantada). The root canals were scanned using micro-CT (SkyScan 1176) at 9 µm voxel size before and after each preparation step. Transportation, percentage of increase in volume, debris and uninstrumented surface (UNS) were evaluated. Mann Whitney, Wilcoxon, paired and non-paired t-tests were used for statistical analysis (α = 0.05). The canals prepared with PDL and HFEDM obtained similar results for all the variables assessed before using E18D (p > 0.05). E18D significantly decreased the percentage of debris and UNS values in both Groups (p < 0.05). The complementary preparations with E18D caused a smaller quantity of debris in the isthmus of the canals previously prepared with PDL in comparison with HFEDM (p < 0.05). PDL and HFEDM provided similar root canal preparation. PDL promoted a smaller quantity of Debris in the isthmus than HFEDM after using E18D. E18D significantly improved cleaning, and reduced Debris and UNS.
Asunto(s)
Cavidad Pulpar , Ultrasonido , Cavidad Pulpar/diagnóstico por imagen , Microtomografía por Rayos X , Preparación del Conducto Radicular , Titanio , Diente Molar/diagnóstico por imagenRESUMEN
This study aimed to evaluate the effect of apicoectomy performed with a bur or an ultrasonic tip on the adaptation of the filling material to root canal dentin. Twenty human mandibular incisors were selected and prepared with a ProDesign Logic system up to diameter 40/.05. The root canals were filled with Bio-C Sealer (Angelus, PR, Brazil) using the single cone technique and were stored at 37ºC and 95% relative humidity for 7 days. After this period, the apicoectomy of the 3 millimeters of the root apex was performed using Endo-Z bur (Dentsply Sirona) or Bladesonic ultrasonic tip (Helse Ultrasonic, Santa Rosa de Viterbo, Brazil) (n=10). The specimens were scanned by micro-computed tomography (micro-CT; SkyScan 1176) with a voxel size of 8.74 µm after obturation and after apicoectomy. The percentage of voids at the interface between the filling material and the root canal wall was evaluated in the apical 4 mm of the root after apicoectomy, besides the time cutting to both devices. The data obtained were submitted to paired and unpaired t-tests (α = 0.05). Endo-Z and Bladesonic increased the percentage of voids between the filling material and the dentin after apicectomy (p<0.05), and they were similar (p>0.05). Endo-Z has a shorter time to perform apicoectomy compared to Bladesonic (p<0.05). Apicectomies with Endo-Z or Bladesonic could harm the material/dentin interface, while the Endo-Z bur was faster than the Bladesonic ultrasonic tip.
Asunto(s)
Materiales de Obturación del Conducto Radicular , Humanos , Gutapercha , Microtomografía por Rayos X/métodos , Ultrasonido , Obturación del Conducto Radicular , Preparación del Conducto Radicular , Cavidad Pulpar , RetratamientoRESUMEN
Abstract The aim of this study was to compare the filling capacity in curved root canal using a new continuous wave of condensation technique (Termo Pack II, Easy Dental Equipments, Brazil) or lateral compaction. The percentage of voids in the filling of mesial root canals of mandibular molars was assessed by micro-computed tomography (micro-CT). Mesial root canals (n=24) of mandibular molars with a degree of curvature between 20° and 40° were prepared using rotary system (ProDesign Logic, Easy, Brazil) up to #35, .05 taper. The root canals were filled by using the continuous wave of condensation system or lateral compaction and AH Plus sealer (n=12). Scanning at 9 µm was performed after preparation and after filling by using micro-CT SkyScan 1176. The volumetric percentage of filling material and voids (total length and in each root canal third) were calculated. Data were analyzed using ANOVA/ Tukey and Student's t tests (α=0.05). Before the filling techniques, the root canals volume after preparation was similar (p>0.05). The root canals filled by the continuous wave of condensation technique presented the lowest percentage of voids, and the greatest percentage of filling material in total length and thirds (cervical, middle and apical) (p<0.05). Both techniques were not able of completely filling the root canals. The continuous wave of condensation technique Termo Pack II promoted better root canal filling in curved root canals, when compared with lateral compaction.
Resumen El objetivo de este estudio fue comparar la capacidad de obturación en conductos radiculares curvos utilizando una nueva técnica de condensación de onda continua (Termo Pack II, Easy Dental Equipments, Brasil) vs compactación lateral. El porcentaje de brechas en la obturación de los conductos radiculares mesiales de los molares mandibulares se evaluó mediante microtomografía computarizada (micro-CT). Se prepararon conductos radiculares mesiales (n=24) de molares mandibulares con un grado de curvatura entre 20° y 40° utilizando un sistema rotatorio (ProDesign Logic, Easy, Brasil) al #35, conicidad 0,05. Los conductos radiculares se obturaron utilizando un sistema de condensación de onda contínua o compactación lateral y cemento AH Plus (n=12). Se realizó un escaneo de 9 µm después de la preparación y después de la obturación usando el micro-CT SkyScan 1176. Se calculó el porcentaje volumétrico de material de obturación y vacíos (longitud total y en cada tercio del conducto radicular). Los datos se analizaron utilizando las pruebas ANOVA/Tukey y t de Student (α=0,05). Antes de las técnicas de obturación, el volumen de los conductos radiculares después de la preparación fue similar (p>0,05). Los conductos radiculares obturados con la técnica de condensación por onda contínua presentaron el menor porcentaje de vacíos y el mayor porcentaje de material de obturación en longitud total y en tercios (cervical, medio y apical) (p<0,05). Ambas técnicas no fueron capaces de llenar completamente los conductos radiculares. La técnica de condensación de onda contínua Termo Pack II promovió un mejor relleno del conducto radicular en conductos radiculares curvos en comparación con la compactación lateral.
Asunto(s)
Obturación del Conducto Radicular/instrumentación , Condensación , Pulpa Dental , Microtomografía por Rayos X/instrumentaciónRESUMEN
Abstract This study aimed to evaluate the effect of apicoectomy performed with a bur or an ultrasonic tip on the adaptation of the filling material to root canal dentin. Twenty human mandibular incisors were selected and prepared with a ProDesign Logic system up to diameter 40/.05. The root canals were filled with Bio-C Sealer (Angelus, PR, Brazil) using the single cone technique and were stored at 37ºC and 95% relative humidity for 7 days. After this period, the apicoectomy of the 3 millimeters of the root apex was performed using Endo-Z bur (Dentsply Sirona) or Bladesonic ultrasonic tip (Helse Ultrasonic, Santa Rosa de Viterbo, Brazil) (n=10). The specimens were scanned by micro-computed tomography (micro-CT; SkyScan 1176) with a voxel size of 8.74 µm after obturation and after apicoectomy. The percentage of voids at the interface between the filling material and the root canal wall was evaluated in the apical 4 mm of the root after apicoectomy, besides the time cutting to both devices. The data obtained were submitted to paired and unpaired t-tests (α = 0.05). Endo-Z and Bladesonic increased the percentage of voids between the filling material and the dentin after apicectomy (p<0.05), and they were similar (p>0.05). Endo-Z has a shorter time to perform apicoectomy compared to Bladesonic (p<0.05). Apicectomies with Endo-Z or Bladesonic could harm the material/dentin interface, while the Endo-Z bur was faster than the Bladesonic ultrasonic tip.
Resumo O objetivo deste estudo foi avaliar o efeito da apicectomia realizada com broca ou inserto ultrassônico na adaptação do material obturador á dentina do canal radicular. Vinte incisivos inferiores humanos extraídos foram selecionados e preparados com o sistema ProDesign Logic até o diâmetro 40/.05. Os canais radiculares foram obturados com Bio-C Sealer (Angelus, PR, Brasil) por meio da técnica de cone único e foram armazenados em estufa a 37ºC e umidade relativa de 95% por 7 dias. Após esse período, foi realizada apicectomia dos 3 milímetros apicais utilizando broca Endo-Z (Maillefer - Dentsply) ou inserto ultrassônico BladeSonic (Helse Ultrasonic, Santa Rosa de Viterbo, Brasil) (n=10). Os espécimes foram escaneados por meio de microtomografia computadorizada (micro-CT; SkyScan 1176) com tamanho de voxel de 8,74 µm após obturação e após apicectomia. Please, correct this sentece to O percentual de falhas na interface entre o material obturador e a parede dentinaria foi avaliado nos 4 mm apicais da raiz apos apicectomia, alem do tempo de corte para ambos dispositivos. Os dados obtidos foram submetidos aos testes t pareado e não pareado (α = 0,05). Endo-Z e Bladesonic aumentaram o percentual de vazios entre o material obturador e a parede da dentina após apicectomia (p<0.05), sendo semelhantes entre si (p>0.05). Endo-Z demonstrou menor tempo para realizar apicectomia em comparação com Bladesonic (p<0.05). Apicectomias com Endo-Z ou Bladesonic podem prejudicar a interface material obturador/dentina, sendo a broca Endo-Z mais rápida que a ponta ultrassônica Bladesonic.
RESUMEN
The aim of this study was to assess the influence of micro-computed tomography (micro-CT) voxel size on evaluation of root canal preparation using rotary heat-treated nickel-titanium files. Curved mesial root canals of mandibular molars were prepared using ProDesign Logic 30/.05 (PDL) or HyFlex EDM 25/.08 (HEDM) (n=12). The specimens were scanned using micro-CT with 5μm of voxel size before and after root canal preparation. Images with sub-resolution of 10 and 20μm voxel sizes were obtained. The percentage of volume increase, debris and uninstrumented root canal surface were analyzed in the different voxel sizes. Data were compared using unpaired Student's t-test and ANOVA statistical tests (α=0.05). No differences were observed for percentage of volume increase, debris and instrumented surface between the root canals prepared by PDL and HEDM (p>0.05). Both systems promoted higher percentage of debris in the apical third compared to the middle third (p0.05). PDL and HEDM had similar root canal preparation capacity. Micro-CT images using different voxel sizes did not influence the results of volume increase and debris evaluation. However, images at 5µm showed greater accuracy to evaluate the percentage of uninstrumented surfaces.
El objetivo de este estudio fue evaluar la influencia del tamaño de vóxel de la microtomografía computarizada (micro-CT) en la evaluación de la preparación del conducto radicular utilizando limas rotatorias de níquel-titanio tratadas térmicamente. Se prepararon conductos radiculares mesiales curvos de molares mandibulares usando ProDesign Logic 30/.05 (PDL) o HyFlex EDM 25/.08 (HEDM) (n=12). Las muestras se escanearon usando micro-CT con un tamaño de vóxel de 5μm antes y después de la preparación del conducto radicular. Se obtuvieron imágenes con subresolución de vóxeles de 10 y 20μm. Se analizó el porcentaje de aumento de volumen, residuos y superficie del conducto radicular no instrumentado en diferentes tamaños de vóxel. Los datos se compararon usando la prueba t de Student no pareada y las pruebas estadísticas ANOVA (α=0,05). No se observaron diferencias en el porcentaje de aumento de volumen, detritus y superficie instrumentada entre los conductos radiculares preparados por PDL y HEDM (p>0,05). Ambos sistemas promovieron un mayor porcentaje de detritos en el tercio apical en comparación con el tercio medio (p0,05). PDL y HEDM tenían una capacidad de preparación del conducto radicular similar. Las imágenes de micro-CT que utilizan diferentes tamaños de vóxel no influyeron en los resultados de la evaluación del volumen y los desechos. Sin embargo, las imágenes de 5µm mostraron una mayor precisión al evaluar el porcentaje de superficies no instrumentadas.
RESUMEN
The aim of this study was to compare the quantification of hard-tissue debris by using micro-computed tomography (micro-CT) and nano-focus computed tomography (nano-CT) after root canal instrumentation. Ten mandibular molars containing an isthmus in the mesial root were scanned in a SkyScan 1172 micro-CT device with a voxel size of 12.8 µm and in a NanoTom nano-CT device with 5.5 µm. The mesial root canals were irrigated with 5 mL of saline solution at the orifice level, instrumented with Reciproc R25 files and a second scanning was performed by micro-CT and nano-CT devices for post-instrumentation images. DataViewer software was used for registering the pre- and post-operative micro-CT and nano-CT images. The root canal and the debris were segmented for quantitative analysis of the volume of the canal and volume of debris using CTAn software. Statistical analysis was performed using the T test for comparison between volume of the canal after instrumentation and volume of debris in both image modalities. The level of significance was set at p < 0.05. Nano-CT images showed higher values of debris when compared with micro-CT (p < 0.05) after root canal instrumentation. No difference was observed between the volume of the root canal after instrumentation in the two imaging methods used (p > 0.05). Nano-CT technology can be recommended as a more precise method for quantitative analysis of hard-tissue debris. Moreover, in Endodontic research it is a promising method, as it is capable of providing higher spatial and contrast resolution, faster scanning and higher image quality.