RESUMEN
Photoelectrochemical (PEC) technology is a promising approach for converting solar energy into chemical energy, offering significant potential for renewable energy applications. In this work, the CuO thin film was fabricated with different pH value in between 8.5 ± 0.1 and 10.5 ± 0.1 via Successive Ionic Layer Adsorption and Reaction (SILAR) method. The Effect of pH on thickness, structural, morphological, elemental composition and optical properties were investigated by using stylus profilometry, XRD, SEM, TEM, EDX, UV-vis and PL. The XRD results showed that as the pH increased, the crystallite size increased from 19.24 nm to 25.62 nm, with a monoclinic phase along the (111) direction. The CuO film deposited at pH value 10.5 ± 0.1 exhibit well defined identical particle with its size in the range between 200 and 300 nm was confirmed by SEM and TEM analysis. As the pH increased from 8.5 ± 0.1 to 10.5 ± 0.1, the CuO film bandgap (Eg) value reduced from 1.52 eV to 1.42 eV with indirect transition. The CuO photocathode deposited at pH 10.5 ± 0.1 shows maximum photocurrent density of 1.45 mA/cm2 at -0.1 V vs. RHE in 0.5 M Na2SO4 solution. Furthermore, the Electrochemical Impedance Spectroscopy (EIS) analysis shows, the CuO (pH 10.5 ± 0.1) electrode have higher conductivity value of 0.6862 S/cm compared CuO at pH 8.5 ± 0.1 (0.2779 S/cm) and CuO at pH 9.5 ± 0.1 (0.4646 S/cm) electrodes.