Structure-Related Electronic and Magnetic Properties in Ultrathin Epitaxial NixFe3-xO4 Films on MgO(001).

Off-stoichiometric NixFe3-xO4 ultrathin films (x < 2.1) with varying Ni content x and thickness 16 (±2) nm were grown on MgO(001) by reactive molecular beam epitaxy. Synchrotron-based high-resolution X-ray diffraction measurements reveal vertical compressive strain for all films, resulting from a lateral pseudomorphic adaption of the film to the substrate lattice without any strain relaxation. Complete crystallinity with smooth interfaces and surfaces is obtained independent of the Ni content x. For x < 1 an expected successive conversion from Fe3O4 to NiFe2O4 is observed, whereas local transformation into NiO structures is observed for films with Ni content x > 1. However, angle-resolved hard X-ray photoelectron spectroscopy measurements indicate homogeneous cationic distributions without strictly separated phases independent of the Ni content, while X-ray absorption spectroscopy shows that also for x > 1, not all Fe2+ cations are substituted by Ni2+ cations. The ferrimagnetic behavior, as observed by superconducting quantum interference device magnetometry, is characterized by decreasing saturation magnetization due to the formation of antiferromagnetic NiO parts.

Real-Time Monitoring of Strain Accumulation and Relief during Epitaxy of Ultrathin Co Ferrite Films with Varied Co Content.

Ultrathin CoxFe3-xO4 films of high structural quality and with different Co content (x = 0.6-1.2) were prepared by reactive molecular beam epitaxy on MgO(001) substrates. Epitaxy of these ferrite films is extensively monitored by means of time-resolved (operando) X-ray diffraction recorded in out-of-plane geometry to characterize the temporal evolution of the film structure. The Co ferrite films show high crystalline ordering and smooth film interfaces independent of their Co content. All CoxFe3-xO4 films exhibit enhanced compressive out-of-plane strain during the early stages of growth, which partly releases with increasing film thickness. When the Co content of the ferrite films increases, the vertical-layer distances increase, accompanied by slightly increasing film roughnesses. The latter result is supported by surface-sensitive low-energy electron diffraction as well as X-ray reflectivity measurements on the final films. In contrast, the substrate-film interface roughness decreases with increasing Co content, which is confirmed with X-ray reflectivity measurements. In addition, the composition and electronic structure of the ferrite films is characterized by means of hard X-ray photoelectron spectroscopy performed after film growth. The experiments reveal the expected increasing Fe3+/Fe2+ cation ratios for a higher Co content.

Click-Functionalization of Silanized Carbon Nanotubes: From Inorganic Heterostructures to Biosensing Nanohybrids.

Here we present an approach to functionalize silanized single-walled carbon nanotubes (SWNTs) through copper-free click chemistry for the assembly of inorganic and biological nanohybrids. The nanotube functionalization route involves silanization and strain-promoted azide-alkyne cycloaddition reactions (SPACC). This was characterized by X-ray photoelectron spectroscopy, scanning electron microscopy, transmission electron microscopy, Raman spectroscopy and Fourier transform infra-red spectroscopy. Silane-azide-functionalized SWNTs were immobilized from solution onto patterned substrates through dielectrophoresis (DEP). We demonstrate the general applicability of our strategy for the functionalization of SWNTs with metal nanoparticles (gold nanoparticles), fluorescent dyes (Alexa Fluor 647) and biomolecules (aptamers). In this regard, dopamine-binding aptamers were conjugated to the functionalized SWNTs to perform real-time detection of dopamine at different concentrations. Additionally, the chemical route is shown to selectively functionalize individual nanotubes grown on the surface of silicon substrates, contributing towards future nano electronic device applications.

Reactive Additive Capillary Stamping with Double Network Hydrogel-Derived Aerogel Stamps under Solvothermal Conditions.

Integration of solvothermal reaction products into complex thin-layer architectures is frequently achieved by combinations of layer transfer and subtractive lithography, whereas direct additive substrate patterning with solvothermal reaction products has remained challenging. We report reactive additive capillary stamping under solvothermal conditions as a parallel contact-lithographic access to patterns of solvothermal reaction products in thin-layer configurations. To this end, corresponding precursor inks are infiltrated into mechanically robust mesoporous aerogel stamps derived from double-network hydrogels. The stamp is then brought into contact with a substrate to be patterned under solvothermal reaction conditions inside an autoclave. The precursor ink forms liquid bridges between the topographic surface pattern of the stamp and the substrate. Evaporation-driven enrichment of the precursors in these liquid bridges, along with their liquid-bridge-guided conversion into the solvothermal reaction products, yields large-area submicron patterns of the solvothermal reaction products replicating the stamp topography. For example, we prepared thin hybrid films, which contained ordered monolayers of superparamagnetic submicron nickel ferrite dots prepared by solvothermal capillary stamping surrounded by nickel electrodeposited in a second orthogonal substrate functionalization step. The submicron nickel ferrite dots acted as a magnetic hardener, halving the remanence of the ferromagnetic nickel layer. In this way, thin-layer electromechanical systems, transformers, and positioning systems may be customized.

Phenolic Resin Dual-Use Stamps for Capillary Stamping and Decal Transfer Printing.

We report an optimized two-step thermopolymerization process carried out in contact with micropatterned molds that yields porous phenolic resin dual-use stamps with topographically micropatterned contact surfaces. With these stamps, two different parallel additive substrate manufacturing methods can be executed: capillary stamping and decal transfer microlithography. Under moderate contact pressures, the porous phenolic resin stamps are used for nondestructive ink transfer to substrates by capillary stamping. Continuous ink supply through the pore systems to the contact surfaces of the porous phenolic resin stamps enables multiple successive stamp-substrate contacts for lithographic ink deposition under ambient conditions. No deterioration of the quality of the deposited pattern occurs, and no interruptions for ink replenishment are required. Under a high contact pressure, porous phenolic resin stamps are used for decal transfer printing. In this way, the tips of the stamps' contact elements are lithographically transferred to counterpart substrates. The granular nature of the phenolic resin facilitates the rupture of the contact elements upon stamp retraction. The deposited phenolic resin micropatterns characterized by abundance of exposed hydroxyl groups are used as generic anchoring sites for further application-specific functionalizations. As an example, we deposited phenolic resin micropatterns on quartz crystal microbalance resonators and further functionalized them with polyethylenimine for preconcentration sensing of humidity and gaseous formic acid. We envision that also preconcentration coatings for other sensing methods, such as attenuated total reflection infrared spectroscopy and surface plasmon resonance spectroscopy, are accessible by this functionalization algorithm.

Cationic Ordering and Its Influence on the Magnetic Properties of Co-Rich Cobalt Ferrite Thin Films Prepared by Reactive Solid Phase Epitaxy on Nb-Doped SrTiO3(001).

Here, we present the (element-specific) magnetic properties and cation ordering for ultrathin Co-rich cobalt ferrite films. Two Co-rich CoxFe3-xO4 films with different stoichiometry (x=1.1 and x=1.4) have been formed by reactive solid phase epitaxy due to post-deposition annealing from epitaxial CoO/Fe3O4 bilayers deposited before on Nb-doped SrTiO3(001). The electronic structure, stoichiometry and homogeneity of the cation distribution of the resulting cobalt ferrite films were verified by angle-resolved hard X-ray photoelectron spectroscopy. From X-ray magnetic circular dichroism measurements, the occupancies of the different sublattices were determined using charge-transfer multiplet calculations. For both ferrite films, a partially inverse spinel structure is found with increased amount of Co3+ cations in the low-spin state on octahedral sites for the Co1.4Fe1.6O4 film. These findings concur with the results obtained by superconducting quantum interference device measurements. Further, the latter measurements revealed the presence of an additional soft magnetic phase probably due to cobalt ferrite islands emerging from the surface, as suggested by atomic force microscope measurements.

Close-packed silane nanodot arrays by capillary nanostamping coupled with heterocyclic silane ring opening.

We report the parallel generation of close-packed ordered silane nanodot arrays with nanodot diameters of few 100 nm and nearest-neighbor distances in the one-micron range. Capillary nanostamping of heterocyclic silanes coupled with ring-opening triggered by hydroxyl groups at the substrate surfaces yields nanodots consisting of silane monolayers with exposed terminal functional groups. Using spongy mesoporous silica stamps with methyl-terminated mesopore walls inert towards the heterocyclic silanes, we could manually perform multiple successive stamping cycles under ambient conditions without interruptions for ink refilling. Further functionalizations include the synthesis of polymer nanobrushes on the silane nanodots by surface-initiated atom-transfer radical polymerization. Proteins-of-interest fused to the HaloTag were site-specifically captured to silane nanodots functionalized by copper-free reactions with azide derivatives. Thus, bioorthogonal functionalization for bioanalytics with a spatial resolution in the one-micron range may be realized on solid supports compatible with fluorescence-based optical microscopy. The feature sizes of the silane nanodot arrays match well the length scales characteristic of a variety of biomolecular submicroscopic organizations in living cells, thus representing a compromise between miniaturization and the resolution limit of optical microscopy for sensitive high-throughput bioanalytics.