RESUMEN
Laser cladding is one of the emerging additive manufacturing technologies and has been adopted in various industrial fields. In this study, the morphological characteristics of a single clad of Inconel 718 manufactured by coaxial laser cladding with high laser power from 4200 W to 5400 W, powder feeding rate from 25 g/min to 50 g/min, and cladding speed from 20 mm/s to 50 mm/s are studied. The cross-section of the melt pool is analyzed and classified by type into three types: shallow dilution, flat dilution, and fluctuating dilution. Nine parameters are designed to describe the morphological characteristics of the clad, and the corresponding linear regression models are developed to establish a quantitative relationship between the combined process parameters and morphological characteristics. The results indicate that the total area of the cross-section A, the clad area above the substrate Ac, the area of the molten substrate Am, the total height of the cross-section H, the height of the clad above the substrate hc, the penetration depth hm, the clad width W, the dilution ratio D, and the wetting angle θ are determined by complex coupling of energy input and mass accumulation, and they are proportional to PF0.4/V, P0.5F/V, P/F0.2/V0.4, P2F0.6/V, PF0.7/V, P2/F/V0.3, P/V0.8, P/FV0.2, and PF7/V0.8, respectively. The large linear regression coefficients and the analysis residuals indicate the high reliability of the statistical linear regression models. This work aims to provide a comprehensive understanding of the influence of the main processing parameters on the morphological characteristics of the clad, which is of great value in providing a reference and laying a basis for the practical application of laser cladding technology at a high deposition rate.
RESUMEN
The profile of the laser beam plays a significant role in determining the heat input on the deposition surface, further affecting the molten pool dynamics during laser-based directed energy deposition. The evolution of molten pool under two types of laser beam, super-Gaussian beam (SGB) and Gaussian beam (GB), was simulated using a three-dimensional numerical model. Two basic physical processes, the laser-powder interaction and the molten pool dynamics, were considered in the model. The deposition surface of the molten pool was calculated using the Arbitrary Lagrangian Eulerian moving mesh approach. Several dimensionless numbers were used to explain the underlying physical phenomena under different laser beams. Moreover, the solidification parameters were calculated using the thermal history at the solidification front. It is found that the peak temperature and liquid velocity in the molten pool under the SGB case were lower compared with those for the GB case. Dimensionless numbers analysis indicated that the fluid flow played a more pronounced role in heat transfer compared to conduction, especially in the GB case. The cooling rate was higher for the SGB case, indicating that the grain size could be finer compared with that for the GB case. Finally, the reliability of the numerical simulation was verified by comparing the computed and experimental clad geometry. The work provides a theoretical basis for understanding the thermal behavior and solidification characteristics under different laser input profile during directed energy deposition.
RESUMEN
Polyether-ether-ketone (PEEK), with its superior mechanical, chemical, and thermal properties, as well as high biocompatibility, has been used in aerospace, electronics, and biomedical applications. In this paper, a large number of experiments of single-pulse laser drilling on PEEK were performed to analyze the hole morphology and keyhole evolution, which were characterized by an optical microscope, charge-coupled device (CCD), and high-speed camera. A novel method is proposed to observe and measure the dimension of the processed hole rapidly right after laser drilling for special polymer materials with wear-resistance and non-conductivity. Morphological characteristics of holes are presented to illustrate the effect of pulse width and peak power on hole depth, hole diameter, and aspect-ratio. The obtained maximum drilling depth was 7.06 mm, and the maximum aspect-ratio was 23. In situ observations of the dynamic process of laser drilling, including the keyhole evolution together with ejection and vaporization behavior, were also carried out. The keyhole evolution process can be divided into three stages: rapid increment stage (0−2 ms) at a rate of 2.1 m/s, slow increment stage (2−4 ms) at a rate of 0.3 m/s, and stable stage (>4 ms). Moreover, the variation of dimensionless laser power density with the increase in pulse width was calculated. The calculated maximum drilling depth based on energy balance was compared with the experimental depth. It is proven that the laser−PEEK interaction is mainly influenced by a photothermal effect. Ejection is the dominant material-removal mechanism and contributes to over 60% of the depth increment during the rapid increment stage, while vaporization is dominant and contributes to about 80% of the depth increment during the slow increment stage. The results reveal the material removal mechanism for single-pulse laser drilling on PEEK, which is helpful to understand the dynamic process of keyhole evolution. This not only provides a processing window for future laser drilling of PEEK but also gives a guide for the manufacturing of other polymers.