RESUMEN
Peri-implantitis is the pathological condition of connective tissue inflammation and the progressive loss of supporting bone around dental implants. One of the primary causes of peri mucositis evolving into peri-implantitis is bacterial infection, including infection from Porphyromonas gingivalis. Enhancing the surface smoothness of implants helps to prevent P. gingivalis adhesion to the implant's surface. Interaction analyses between bacteria and the surface roughness of zirconia (Zr) discs subjected to a glow discharge plasma (GDP) treatment compared with non-plasma-treated autoclaved control Zr discs were done. Examinations of the material prosperities revealed that the GDP-treated Zr group had a smoother surface for a better wettability. The GDP-treated Zr discs improved the proliferation of the osteoblast-like cells MG-63, and the osteoblastic differentiation was assessed through alkaline phosphatase detection and marker gene bone sialoprotein (Bsp) and osteocalcin (OC) induction. Scanning electron microscopy demonstrated a relatively low P. gingivalis adhesion on GDP-treated Zr disks, as well as lower colonization of P. gingivalis compared with the control. Our findings confirmed that the GDP treatment of Zr discs resulted in a significant reduction of P. gingivalis adhesion and growth, demonstrating a positive correlation between surface roughness and bacteria adhesion. Therefore, the GDP treatment of Zr dental implants can provide a method for reducing the risk of peri-implantitis.
RESUMEN
Porphyromonas gingivalis infection is one of the causes of implant failures, which can lead to peri-implantitis. Implant surface roughness is reportedly related strongly to P. gingivalis adhesion, which can lead to peri-implantitis and, later, cell adhesion. Our aim was to evaluate the effects of Er,Cr:YSGG laser on titanium (Ti) disc surfaces and its interaction with bacterial adhesion and fibroblast viability. Ti discs underwent two treatments: autoclaving (control) and erbium, chromium-doped yttrium scandium gallium garnet (Er,Cr:YSGG) laser treatment (test). Ti disc surfaces were examined with scanning electronic microscope (SEM), Energy-dispersive spectrometry (EDX), X-ray photoelectron spectroscopy (XPS). The surface roughness same as wettability were also investigated. Fibroblast viability was assessed with the water-soluble tetrazolium 1 (WST-1) test, and osteoblast differentiation was assessed with the alkaline phosphatase (ALP) assay. Bacterial structure and colony formation were detected with scanning electron microscopy and Gram stain. In comparison to control discs, the test discs showed smoother surfaces, with 0.25-µm decrease in surface roughness (p < 0.05); lower P. gingivalis adhesion (p < 0.01); less P. gingivalis colonization (p < 0.05); and increased fibroblast viability and osteoblast differentiation (p < 0.05). Er,Cr:YSGG laser treatment improved disc surfaces by making them slightly smoother, which reduced P. gingivalis adhesion and increased fibroblast viability and osteoblast differentiation. Er,Cr:YSGG laser treatment can be considered a good option for managing peri-implantitis. Further investigations of laser-assisted therapy are necessary for better guidelines in the treatment of peri-implantitis.