Optical Monitoring of the Biodegradation of Porous and Solid Silicon Nanoparticles.

Silicon nanoparticles (SiNP) are currently of great interest, especially in biomedicine, because of their unique physicochemical properties combined with biodegradability. SiNPs can be obtained in various ways and can have either a non-porous solid (sol-) or porous (por-) structure. In this work, we carry out detailed optical monitoring of sol- and por-SiNP biodegradation using Raman and photoluminescence (PL) micro-spectroscopy. SiNPs were obtained by ultrasound grinding of sol- or por-silicon nanowires, created by silver-assisted chemical etching of crystalline Si with different doping levels. In this case, sol-SiNPs consist of nanocrystals 30 nm in size, while por-SiNPs consist of small 3 nm nanocrystals and 16 nm pores. Both SiNPs show low in vitro cytotoxicity towards MCF-7 and HEK293T cells up to 800 µg/mL. The appearance of the F-band (blue-yellow) PL, as well as a decrease in the intensity of the Raman signal, indicate the gradual dissolution of the sol-SiNPs during 20 days of incubation. At the same time, the rapid dissolution of por-SiNP within 24 h is identified by the quenching of their S-band (red) PL and the disappearance of the Raman signal. The obtained results are important for development of intelligent biodegradable drug delivery systems based on SiNPs.

The effects of drying technique and surface pre-treatment on the cytotoxicity and dissolution rate of luminescent porous silicon quantum dots in model fluids and living cells.

Tailoring of the biodegradation of photoluminescent silicon quantum dots (Si QDs) is important for their future applications in diagnostics and therapy. Here, the effect of drying and surface pretreatment on the dissolution rate of Si QDs in model liquids and living cells was studied in vitro using a combination of photoluminescence and Raman micro-spectroscopy. Porous silicon particles were obtained by mechanical milling of electrochemically etched mesoporous silicon films, and consist of interlinked silicon nanocrystals (QDs) and pores. The samples were subjected to super-critical drying with CO2 solvent (SCD) or air drying (AD) and then annealed at 600 °C for 16 hours in 1% oxygen to obtain nano-sized Si QDs. The obtained samples were characterized by a core-shell structure with a crystalline silicon core and a SiO2 layer on the surface. The sizes of the crystalline silicon cores, calculated from Raman scattering spectra, were about 4.5 nm for the initial AD-SiQDs, and about 2 nm for the initial SCD-SiQDs. Both the AD-Si QDs and the SCD-Si QDs exhibited visible photoluminescence (PL) properties due to quantum confinement effects. The dissolution of the nanocrystals was evaluated through their PL quenching, as well as by the presence of a low-frequency shift, broadening, and a decrease in the intensity of the Raman signal. The stability of the AD-Si QDs and the complete dissolution of the SCD-Si QDs during 24 hours of incubation with cells have been demonstrated. This might explain the apparent lower cytotoxicity observed for SCD-Si QDs.