RESUMEN
Metal organic chemical vapor deposition was used to grow N-polar In0.63Al0.37N on sapphire substrates. P-doping was provided by a precursor flow of Cp2Mg between 0 and 130 nmol/min, reaching a Cp2Mg/III ratio of 8.3 × 10-3. The grain structure of 360 nm thick InAlN was spoiled by pits after introducing a flow of CP2Mg at 30 nmol/min. The surface quality was improved with a flow of 80 nmol/min; however, detrimental deterioration appeared at 130 nmol/min. This correlated with the XRD shape and determined density of dislocations, indicating a phase separation at the highest flow. Degenerated n-type conduction and a free carrier concentration of ~1019 cm-3 were determined in all samples, with a minor compensation observed at a CP2Mg flow of 30 nmol/min. The room temperature (RT) electron mobility of ~40 cm2/Vs of the undoped sample was reduced to ~6 and ~0.3 cm2/Vs with a CP2Mg flow of 30 and 80 nmol/min, respectively. Scattering at ionized acceptor/donor Mg-related levels is suggested. RT photoluminescence showed a red shift of 0.22 eV from the virgin 1.73 eV peak value with Mg doping. Mobility degradation was found to be the main factor by InAlN resistivity determination, which increased by two orders of magnitude, approaching ~0.5 Ωcm, at the highest Cp2Mg flow.
RESUMEN
Polysiloxanes have shown exquisite properties for fabrication of microstructures for various biomedical and biotechnological applications. Nevertheless, their biocompatibility in terms of cell adhesion and survival ability is controversial. A simple polysiloxane modifying procedure that reproducibly enhances cell adhesion was proposed. Sonication of the hybrid organic-inorganic polymer of polysiloxane type, Ormocomp, in potassium hydroxide (KOH)/ethanol solution enhanced adhesion and subsequent survival of a panel of four cell lines. Characterization of surface properties of untreated and KOH-treated Ormocomp coatings has revealed considerable negative charge of Ormocomp substrates based on measurements of zeta potentials. KOH treatment did not modify surface morphology as visualized by scanning electron microscopy, but it resulted in alteration in both chemical composition according to SIMS analysis and hydrophilicity evaluated by static water contact angles. The results suggest that the failure of the adherent cells to survive on Ormocomp coatings is related to cell adhesion. The negative surface charge of Ormocomp substrates may be one of the influencing factors; however, the modification of surface chemistry mediated by KOH and the resulting increase in hydrophilicity accompanied by modification of protein adsorption are more likely responsible for enhanced cell adhesion and survival on Ormocomp coatings. KOH treatment thus may serve as a simple, cost-effective procedure modifying polysiloxane-type polymers that leads to reproducible enhancement of cell adhesion.