RESUMEN
PURPOSE: To investigate and compare the effect of different heat treatment on the metal- ceramic bonding strength and the interfacial microstructure of the Co-Cr alloy. METHODS: Thirty specimens were made according to ISO 9693,and then divided into 3 groups (n=10) through the measurements .Group A(degassed 60s):degassed and then maintained 60s in 980 degrees centigrade Group B(degassed 60s and preoxidation 60s): degassed and maintained 60s in 980 degrees centigrade, then were maintained continuously for 60s in 980 degrees centigrade after re-gassed,Group C(degassed 120s): degassed and maintained 120s in 980 degrees centigrade. The bonding strengths of the three groups were evaluated through three point bending test. Six specimens divided into 3 group were made in the same method to observe the metal-ceramic interface through scanning electronic microscope(SEM) and energy dispersive spectrum(EDS).The bonding strength data were analyzed using ANOVA and Bonferroni's test by SPSS13.0 software package. RESULTS: The mean value of bonding strength was (39.03±2.70)MPa for group A, (34.43±2.36)MPa for group B, (31.65±1.49)MPa for group C, respectively. There were significant difference between every two groups (P<0.05). SEM demonstrated that the width of interfacial transition layer was 12.3-16.4µm in group A, 15.2-21.8µm in group B and 26.3-32.2µm in group C. CONCLUSIONS: Higher metal-ceramic bonding strength for Co-Cr alloy will be formed under the situation of degassed,and maintained 60s in 980 degrees centigrade ; while extending degassed time, prolonging the heat maintained time and preoxidation after degassing will reduce metal-ceramic bonding strength.