In-band pumped Kerr-lens mode-locked Tm,Ho-codoped calcium aluminate laser.

We report on a Kerr-lens mode-locked Tm,Ho-codoped calcium aluminate laser with in-band pumping of the Tm ions by a spatially single-mode 1678 nm Raman fiber laser. The structurally disordered CaGdAlO4 host crystal is also codoped also with the passive Lu ion for additional inhomogeneous line broadening. The Tm,Ho,Lu:CaGdAlO4 laser generates soliton pulses as short as 79 fs at a central wavelength of 2073.6 nm via soft-aperture Kerr-lens mode-locking. The corresponding average output power amounts to 91 mW at a pulse repetition rate of ∼86 MHz. The average output power can be scaled to 842 mW at the expense of slightly longer pulses of 155 fs at 2045.9 nm, which corresponds to a peak power of ∼58 kW. To the best of our knowledge, this represents the first demonstration of an in-band pumped Kerr-lens mode-locked Tm,Ho solid-state laser at ∼2 µm.

Diode-pumped mode-locked Yb:Sc2SiO5 laser generating 38 fs pulses.

We report on sub-40 fs pulse generation from a Yb:Sc2SiO5 laser pumped by a spatially single-mode fiber-coupled laser diode at 976 nm. A maximum output power of 545 mW was obtained at 1062.6 nm in the continuous-wave regime, corresponding to a slope efficiency of 64% and a laser threshold of 143 mW. A continuous wavelength tuning across 80 nm (1030 -1110 nm) was also achieved. Implementing a SESAM for starting and stabilizing the mode-locked operation, the Yb:Sc2SiO5 laser delivered soliton pulses as short as 38 fs at 1069.5 nm with an average output power of 76 mW at a pulse repetition rate of ∼79.8 MHz. The maximum output power was scaled to 216 mW for slightly longer pulses of 42 fs, which corresponded to a peak power of 56.6 kW and an optical efficiency of 22.7%. To the best of our knowledge, these results represent the shortest pulses ever achieved with any Yb3+-doped rare-earth oxyorthosilicate crystal.

56-fs diode-pumped SESAM mode-locked Yb:YAl3(BO3)4 laser.

We report on the first sub-60 fs pulse generated from a diode-pumped SESAM mode-locked Yb-laser based on a non-centrosymmetric Yb:YAl3(BO3)4 crystal as a gain medium. In the continuous-wave regime, pumping with a spatially single-mode, fiber-coupled 976 nm InGaAs laser diode, the Yb:YAl3(BO3)4 laser generated 391 mW at 1041.7 nm with a slope efficiency as high as 65.1%, and a wavelength tuning across 59 nm (1019 to 1078 nm) was achieved. By implementing a commercial SESAM to initiate and sustain the soliton type mode-locking, and using only a 1 mm-thick laser crystal, the Yb:YAl3(BO3)4 laser delivered pulses as short as 56 fs at a central wavelength of 1044.6 nm with an average output power of 76 mW at a pulse repetition rate of ∼67.55 MHz. To the best of our knowledge, this result represents the shortest pulses ever achieved from Yb:YAB crystal.

Sub-50 fs diode-pumped SESAM mode-locked Yb:SrF2 laser.

We report on sub-50 fs pulse generation from a passively mode-locked Yb:SrF2 laser pumped with a spatially single-mode, fiber-coupled laser diode at 976 nm. In the continuous-wave regime, the Yb:SrF2 laser generated a maximum output power of 704 mW at 1048 nm with a threshold of 64 mW and a slope efficiency of 77.2%. A continuous wavelength tuning across 89 nm (1006 - 1095 nm) was achieved with a Lyot filter. By implementing a SEmiconductor Saturable Absorber Mirror (SESAM) for initiating and sustaining the mode-locked operation, soliton pulses as short as 49 fs were generated at 1057 nm with an average output power of 117 mW at a pulse repetition rate of ∼75.9 MHz. The maximum average output power of the mode-locked Yb:SrF2 laser was scaled up to 313 mW for slightly longer pulses of 70 fs at 1049.4 nm, corresponding to a peak power of 51.9 kW and an optical efficiency of 34.7%.

Kerr-lens mode-locking of an Yb:CLNGG laser.

We report on a Kerr-lens mode-locked laser based on an Yb3+-doped disordered calcium lithium niobium gallium garnet (Yb:CLNGG) crystal. Pumping by a spatially single-mode Yb fiber laser at 976 nm, the Yb:CLNGG laser delivers soliton pulses as short as 31 fs at 1056.8 nm with an average output power of 66 mW and a pulse repetition rate of ∼77.6 MHz via soft-aperture Kerr-lens mode-locking. The maximum output power of the Kerr-lens mode-locked laser amounted to 203 mW for slightly longer pulses of 37 fs at an absorbed pump power of 0.74 W, which corresponds to a peak power of 62.2 kW and an optical efficiency of 20.3%.

Semiconductor saturable absorber mirror mode-locked Yb:YAP laser.

We report on sub-30 fs pulse generation from a semiconductor saturable absorber mirror mode-locked Yb:YAP laser. Pumping by a spatially single-mode Yb fiber laser at 979 nm, soliton pulses as short as 29 fs were generated at 1091 nm with an average output power of 156 mW and a pulse repetition rate of 85.1 MHz. The maximum output power of the mode-locked Yb:YAP laser amounted to 320 mW for slightly longer pulses (32 fs) at an incident pump power of 1.52 W, corresponding to a peak power of 103 kW and an optical efficiency of 20.5%. To the best of our knowledge, this result represents the shortest pulses ever achieved from any solid-state Yb laser mode-locked by a slow, i.e., physical saturable absorber.

Kerr-lens mode-locked Yb:YAlO3 laser generating 24-fs pulses at 1085 nm.

We report on a Kerr-lens mode-locked Yb:YAlO3 laser generating soliton pulses as short as 24 fs at 1085 nm with an average output power of 186 mW and a pulse repetition rate of 87.5 MHz, representing the shortest pulses ever achieved from any mode-locked laser based on Yb3+-doped structurally ordered crystal. Optimized for power-scalable operation, the Yb:YAlO3 laser delivers 1.9 W at 1060 nm at the expense of a longer pulse duration of 44 fs, corresponding to a peak power of 462 kW and an optical efficiency of 43.2%.

Kerr-lens mode-locked ytterbium-activated orthoaluminate laser.

We report on the first, to the best of our knowledge, Kerr-lens mode-locked laser based on an Yb3+-doped perovskite-type orthoaluminate crystal exploiting two different principal light polarizations. The Yb:(Y,Gd)AlO3 laser delivers soliton pulses as short as 32 fs at 1067 nm with an average output power of 328 mW and a pulse repetition rate of ∼84.6 MHz for E || a polarization. For the orthogonal E || b polarization, 33-fs pulses are generated at 1057 nm with an average output power of 305 mW. Power scaling to a maximum average output power reaching 2.07 W is achieved at the expense of longer pulse duration (72 fs for E || b), corresponding to an optical efficiency of 43.9% and a peak power of 303 kW.

Diode-pumped SESAM mode-locked Yb:(Y,Gd)AlO3 laser.

We report on the continuous-wave (CW) and mode-locked (ML) laser performance of an Yb3+-doped yttrium-gadolinium orthoaluminate crystal, Yb:(Y,Gd)AlO3. Pumping by a single-transverse-mode fiber-coupled 976 nm InGaAs laser diode, the maximum output power in the CW regime amounted to 429 mW at 1041.8 nm corresponding to a slope efficiency of 51.1% and a continuous wavelength tuning across 84 nm (1011-1095 nm) was achieved. The self-starting ML operation of the Yb:(Y,Gd)AlO3 laser was stabilized by a semiconductor saturable absorber mirror. Soliton pulses as short as 43 fs were generated at 1052.3 nm with an average output power of 103 mW and a pulse repetition rate of ∼70.8 MHz. To the best of our knowledge, our result represents the first report on the passively mode-locked operation of a Yb:(Y,Gd)AlO3 laser, and the shortest pulse duration ever achieved from any Yb3+-doped orthorhombic perovskite aluminate crystals.

Soliton mode-locked Yb:Ca3Gd2(BO3)4 laser.

We report on a soliton mode-locked Yb:Ca3Gd2(BO3)4 laser at ∼1.06 µm stabilized by a semiconductor saturable absorber mirror. Pumping with a single-transverse mode, fiber-coupled laser diode at 976 nm, the Yb:Ca3Gd2(BO3)4 laser delivers soliton pulses as short as 39 fs at a central wavelength of 1059.2 nm with an average output power of 70 mW and a pulse repetition rate of ∼67.3 MHz.

SESAM mode-locked Yb:Sr3Y2(BO3)4 laser.

We demonstrate the first sub-40 fs soliton pulse generation from a diode-pumped Yb:Sr3Y2(BO3)4 laser passively mode-locked by a semiconductor saturable absorber mirror. Pulses as short as 38 fs at a central wavelength of 1051.7 nm were achieved with an average output power of 115 mW and a pulse repetition rate of 67.7 MHz. The maximum average output power reached 303 mW at 1057.8 nm with a slightly longer pulse duration of 52 fs, which corresponded to a peak power of 76.9 kW and an optical efficiency of 25.3%.

Diode-pumped mode-locked Yb:BaF2 laser.

We report on a continuous-wave (CW) and passively mode-locked operation of a fluorite-type Yb:BaF2 crystal. Pumped with a spatially single-mode, fiber-coupled InGaAs laser diode at 976 nm, the Yb:BaF2 laser generated a maximum CW output power of 512 mW at 1054.4 nm, corresponding to a laser threshold of 36.5 mW and a slope efficiency of 65.0%. A continuous wavelength tuning across 85 nm (1007-1092 nm) was achieved. By implementing a semiconductor saturable absorber mirror for initiating and sustaining the soliton pulse shaping, near Fourier-transform-limited pulses as short as 52 fs were generated at 1058.2 nm with an average output power of 129 mW at a pulse repetition rate of ∼79.5 MHz. To the best of our knowledge, this is the first report on the passively mode-locked operation of the Yb:BaF2 crystal.