Rice Husk-Based Adsorbents for Removal of Metals from Aqueous Solutions.

Adsorption is one of the main methods of water purification. Novel advanced, eco-friendly, cost-effective adsorbents with high adsorption capacity and selectivity are required to remove pollutants from aqueous solutions. Plant polymers are viewed as both prospective adsorbents and as raw materials to produce them instead of conventional adsorption materials. There is widespread interest in using rice husk as a universal sorbent to remove different contaminants from aqueous media because of its surplus availability, low cost, and high content of oxygen containing functional and silanol groups as active sites for adsorptive extraction. Different methods of heat and chemical treatments have been developed to improve the sorption properties of raw rice husk. Unmodified rice husk and rice-husk-based sorbents have been tested to uptake non-ferrous, ferrous, minor, precious, rare, and rare-earth metals and radionuclides from artificial and industrial solutions, natural contaminated water, and industrial wastewater. This review summarizes the results of numerous studies and characterizes the current state of work in this area, with recommendations for further development.

Rice Husk Cellulose-Based Adsorbent to Extract Rare Metals: Preparing and Properties.

Adsorption is one of the common stages in the hydrometallurgy of rare metals. Its efficiency is largely determined by the quality of the sorbent used. The purpose of this work was to create an activated sorbent based on rice husk cellulose for the extraction of rhenium from aqueous solutions. Two types of cellulose were obtained by treating rice husk with a 1.5% NaOH solution (alkaline cellulose) and a nitric acid solution in ethyl alcohol (Kürschner and Hoffer cellulose). They were tested by IR, SEM, TA, TPD-MS, and XRD methods. It was found that Kürschner and Hoffer cellulose does not contain lignin and retains structural order to a greater extent. By means of this cellulose carbonization at 600 °C and activation by physical, chemical, and combined methods, a series of sorbents were prepared and studied by different methods. It was determined that the sorbent KHC4-600VA obtained by combined activation of cellulose carbonizate by water vapor at 850 °C, followed by an alkaline treatment, has the best textural characteristics: S-~1200 m2·g-1, V-1.22 cm3·g-1, and R-2.05 nm. KHC4-600VA provides 90% recovery of Re (VII) ions from aqueous solutions. According to the Freundlich model, sorption proceeds favorably on the sorbent's heterogeneous surface.

Rice Husk Research: From Environmental Pollutant to a Promising Source of Organo-Mineral Raw Materials.

Rice husk is a large-tonnage waste left from rice production. It is not subject to humification and therefore becomes a serious environmental pollutant. Due to the presence of two essential elements-carbon and silicon-in its composition, rice husk is a promising organo-mineral raw material. The known methods for processing of rice husk are associated with the formation of even more aggressive waste. The creation of a waste-free technology for processing this plant material requires a detailed study. Rice husk of yzylorda oblast was studied using IR, SEM, TA, TPD-MS, EPR, and TEM methods. It was determined that under a temperature up to 500 °C, the ligno-carbohydrate component of rice husk decomposes almost completely. Three main peaks are recorded during the decomposition: hemicellulose at 200 °C, cellulose at 265 °C, and lignin at 350-360 °C. This process is endothermic. However, above of 300 °C the exothermic reactions associated with the formation of new substances and condensation processes in the solid residue begin to prevail. This explains the increase in the concentration of paramagnetic centers (PMCs) in products of rice husk carbonization in the range of up to 450 °C. Further increase in temperature leads to a decrease in the number of PMCs as a result of carbon graphite-like structures formation. The silicon-carbon product of rice husk carbonization (nanocomposite) is formed by interconnected nanoscale particles of carbon and silicon dioxide, the modification of which depends on the temperature of carbonization. The obtained data allow management of the rice husk utilization process while manufacturing products in demand based on ecofriendly technologies.

Rice Husk Hydrolytic Lignin Transformation in Carbonization Process.

Lignin processing products have an extensive using range. Because products properties depend on lignin precursor quality it was interesting to study lignin isolated from rice husk being a large tonnage waste of rice production and its structural transformations during carbonization. Lignin isolated by the thermal hydrolysis method with H2SO4 1 wt % solution and its carbonized products prepared under different carbonization conditions were characterized using elemental analysis, IR, TPD-MS, XRD, TEM, and EPR. It was shown lignin degradation takes place over the wide (220-520 °C) temperature range. Silica presenting in lignin affects the thermal destruction of this polymer. Due to the strong chemical bond with phenolic hydroxylic group it decreases an evaporation of volatile compounds and as a result increases the temperature range of the lignin degradation. Rice husk hydrolytic lignin transformations during carbonization occur with generation of free radicals. Their concentration is decreased after condensation of aromatic rings with carbon polycycles formation, i.e., the graphite-like structure. Quantity and X-ray diffraction characteristics of the graphite-like phase depend on carbonization conditions. Morphology of the lignin-based carbonized products is represented by carbon fibers, carbon and silica nanoparticles, and together with another structure characteristics provides prospective performance properties of lignin-based end products.