Full Selectivity Control over the Catalytic Hydrogenation of Nitroaromatics into Six Products.

A full selectivity control over the catalytic hydrogenation of nitroaromatics leads to the production of six possible products, i.e., nitroso, hydroxylamine, azoxy, azo, hydrazo or aniline compounds, which has however not been achieved in the field of heterogeneous catalysis. Currently, there is no sufficient evidence to support that the catalytic hydrogenation of nitroaromatics with the use of heterogeneous metal catalysts would follow the Haber's mechanistic scheme based on electrochemical reduction. We now demonstrate in this work that it is possible to fully control the catalytic hydrogenation of nitroaromatics into their all six products using a single catalytic system under various conditions. Employing SnO2-supported Pt nanoparticles facilitated by the surface coordination of ethylenediamine and vanadium species enabled this unprecedented selectivity control. Through systematic investigation into the controlled production of all products and their chemical reactivities, we have constructed a detailed reaction network for the catalytic hydrogenation of nitroaromatics. Crucially, the application of oxygen-isolated characterization techniques proved indispensable in identifying unstable compounds such as nitroso, hydroxylamine, hydrazo compounds. The insights gained from this research offer invaluable guidance for selectively transforming nitroaromatics into a wide array of functional N-containing compounds, both advancing fundamental understanding and fostering practical applications in various fields.

Chiroptical Activity Amplification of Chiral Metal Nanoclusters via Surface/Interface Solidification.

It remains a grand challenge to amplify the chiroptical activity of chiral metal nanoclusters (NCs) although it is desirable for fundamental research and practical application. Herein, we report a strategy of surface/interface solidification (SIS) for enhancing the chiroptical activity of gold NCs. Structural analysis of [Au19(2R,4R/2S,4S-BDPP)6Cl2]3+ (BDPP is 2,4-bis(diphenylphosphino)pentane) clusters reveals that one of the interfacial gold atoms is flexible between two sites and large space is present on the surface, thus hampering chirality transfer from surface chiral ligands to metal core and leading to low chiroptical activity. Following SIS by filling the flexible sites and replacing chlorides with thiolate ligands affords another pair of [Au20(2R,4R/2S,4S-BDPP)6(4-F-C6H4S)2]4+, which shows a more compact and organized structure and thus an almost 40-fold enhancement of chiroptical activity. This work not only provides an efficient approach for amplifying the chiroptical activity of metal nanoclusters but also highlights the significance of achiral components in shaping chiral nanostructures.

Optimizing Ionomer Distribution in Anode Catalyst Layer for Stable Proton Exchange Membrane Water Electrolysis.

The high cost of proton exchange membrane water electrolysis (PEMWE) originates from the usage of precious materials, insufficient efficiency, and lifetime. In this work, an important degradation mechanism of PEMWE caused by dynamics of ionomers over time in anode catalyst layer (ACL), which is a purely mechanical degradation of microstructure, is identified. Contrary to conventional understanding that the microstructure of ACL is static, the micropores are inclined to be occupied by ionomers due to the localized swelling/creep/migration, especially near the ACL/PTL (porous transport layer) interface, where they form transport channels of reactant/product couples. Consequently, the ACL with increased ionomers at PTL/ACL interface exhibit rapid and continuous degradation. In addition, a close correlation between the microstructure of ACL and the catalyst ink is discovered. Specifically, if more ionomers migrate to the top layer of the ink, more ionomers accumulate at the ACL/PEM interface, leaving fewer ionomers at the ACL/PTL interface. Therefore, the ionomer distribution in ACL is successfully optimized, which exhibits reduced ionomers at the ACL/PTL interface and enriches ionomers at the ACL/PEM interface, reducing the decay rate by a factor of three when operated at 2.0 A cm-2 and 80 °C. The findings provide a general way to achieve low-cost hydrogen production.

Redox-Sensitive NiOx Stabilizing Perovskite Films for High-Performance Photovoltaics.

Metal halide perovskite materials inherently possess imperfections, particularly under nonequilibrium conditions, such as exposure to light or heat. To tackle this challenge, we introduced stearate ligand-capped nickel oxide (NiOx), a redox-sensitive metal oxide with variable valence, into perovskite intermediate films. The integration of NiOx improved the efficiency and stability of perovskite solar cells (PSCs) by offering multifunctional roles: (1) chemical passivation for ongoing defect repair, (2) energetic passivation to bolster defect tolerance, and (3) field-effect passivation to mitigate charge accumulation. Employing a synergistic approach that tailored these three passivation mechanisms led to a substantial increase in the devices' efficiencies. The target cell (0.12 cm2) and module (18 cm2) exhibited efficiencies of 24.0 and 22.9%, respectively. Notably, the encapsulated modules maintained almost 100 and 87% of the initial efficiencies after operating for 1100 h at the maximum power point (60 °C, 50% RH) and 2000 h of damp-heat testing (85 °C, 85% RH), respectively. Outdoor real-time tests further validated the commercial viability of the NiOx-assisted PSMs. The proposed passivation strategy provides a practical and uncomplicated approach for fabricating high-efficiency and stable photovoltaics.

Efficient and Stable Proton Exchange Membrane Water Electrolysis Enabled by Stress Optimization.

Proton exchange membrane water electrolysis (PEMWE) is a promising solution for the conversion and storage of fluctuating renewable energy sources. Although tremendously efficient materials have been developed, commercial PEMWE products still cannot fulfill industrial demands regarding efficiency and stability. In this work, we demonstrate that the stress distribution, a purely mechanical parameter in electrolyzer assembly, plays a critical role in overall efficiency and stability. The conventional cell structure, which usually adopts a serpentine flow channel (S-FC) to deliver and distribute reactants and products, resulted in highly uneven stress distribution. Consequently, the anode catalyst layer (ACL) under the high stress region was severely deformed, whereas the low stress region was not as active due to poor electrical contact. To address these issues, we proposed a Ti mesh flow channel (TM-FC) with gradient pores to reduce the stress inhomogeneity. Consequently, the ACL with TM-FC exhibited 27 mV lower voltage initially and an 8-fold reduction in voltage degradation rate compared to that with S-FC at 2.0 A/cm2. Additionally, the applicability of the TM-FC was demonstrated in cross-scale electrolyzers up to 100 kW, showing a voltage increase of only 20 mV (accounting for less than 2% of overall voltage) after three orders of magnitude scaleup.

A Versatile Strategy for the Controlled Synthesis of Atomically Precise Palladium Nanoclusters.

The study of the structures, applications, and structure-property relationships of atomically precise metal nanoclusters relies heavily on their controlled synthesis. Although great progress has been made in the controlled synthesis of Group 11 (Cu, Ag, Au) metal nanoclusters, the preparation of Pd nanoclusters remains a grand challenge. Herein, a new, simple, and versatile synthetic strategy for the controlled synthesis of Pd nanoclusters is reported with tailorable structures and functions. The synthesis strategy involves the controllable transformations of Pd4(CO)4(CH3COO)4 in air, allowing the discovery of a family of Pd nanoclusters with well-defined structure and high yield. For example, by treating the Pd4(CO)4(CH3COO)4 with 2,2-dipyridine ligands, two clusters of Pd4 and Pd10 whose metal framework describes the growth of vertex-sharing tetrahedra have been selectively isolated. Interestingly, chiral Pd4 nanoclusters can be gained by virtue of customized chiral pyridine-imine ligands, thus representing a pioneering example to shed light on the hierarchical chiral nanostructures of Pd. This synthetic methodology also tolerates a wide variety of ligands and affords phosphine-ligated Pd nanoclusters in a simple way. It is believed that the successful exploration of the synthetic strategy would simulate the research enthusiasm on both the synthesis and application of atomically precise Pd nanoclusters.

Frustrated Lewis pairs on pentacoordinated Al3+-enriched Al2O3 promote heterolytic hydrogen activation and hydrogenation.

As an emerging class of metal-free catalysts, frustrated Lewis pairs (FLPs) catalysts have been greatly constructed and applied in many fields. Homogeneous FLPs have witnessed significant development, while limited heterogeneous FLPs catalysts are available. Herein, we report that heterogeneous FLPs on pentacoordinated Al3+-enriched Al2O3 readily promote the heterolytic activation of H2 and thus hydrogenation catalysis. The defect-rich Al2O3 was prepared by simple calcination of a carboxylate-containing Al precursor. Combinatorial studies confirmed the presence of rich FLPs on the surface of the defective Al2O3. In contrast to conventional alumina (γ-Al2O3), the FLP-containing Al2O3 can activate H2 in the absence of any transition metal species. More importantly, H2 was activated by surface FLPs in a heterolytic pathway, leading to the hydrogenation of styrene in a stepwise process. This work paves the way for the exploration of more underlying heterogeneous FLPs catalysts and further understanding of accurate active sites and catalytic mechanisms of heterogeneous FLPs at the molecular level.

Constructing Robust 3D Ionomer Networks in the Catalyst Layer to Achieve Stable Water Electrolysis for Green Hydrogen Production.

The widespread application of proton exchange membrane water electrolyzers (PEMWEs) is hampered by insufficient lifetime caused by degradation of the anode catalyst layer (ACL). Here, an important degradation mechanism has been identified, attributed to poor mechanical stability causing the mass transfer channels to be blocked by ionomers under operating conditions. By using liquid-phase atomic force microscopy, we directly observed that the ionomers were randomly distributed (RD) in the ACL, which occupied the mass transfer channels due to swelling, creeping, and migration properties. Interestingly, we found that alternating treatments of the ACL in different water/temperature environments resulted in forming three-dimensional ionomer networks (3D INs) in the ACL, which increased the mechanical strength of microstructures by 3 times. Benefitting from the efficient and stable mass transfer channels, the lifetime was improved by 19 times. A low degradation rate of approximately 3.0 µV/h at 80 °C and a high current density of 2.0 A/cm2 was achieved on a 50 cm2 electrolyzer. These data demonstrated a forecasted lifetime of 80 000 h, approaching the 2026 DOE lifetime target. This work emphasizes the importance of the mechanical stability of the ACL and offers a general strategy for designing and developing a durable PEMWE.

Hydride-doped Ag17Cu10 nanoclusters as high-performance electrocatalysts for CO2 reduction.

The atomically precise metal electrocatalysts for driving CO2 reduction reactions are eagerly pursued as they are model systems to identify the active sites, understand the reaction mechanism, and further guide the exploration of efficient and practical metal nanocatalysts. Reported herein is a nanocluster-based electrocatalyst for CO2 reduction, which features a clear geometric and electronic structure, and more importantly excellent performance. The nanocatalysts with the molecular formula of [Ag17Cu10(dppm)4(PhC≡C)20H4]3+ have been obtained in a facile way. The unique metal framework of the cluster, with silver, copper, and hydride included, and dedicated surface structure, with strong (dppm) and labile (alkynyl) ligands coordinated, endow the cluster with excellent performance in electrochemical CO2 reduction reaction to CO. With the atomically precise electrocatalysts in hand, not only high reactivity and selectivity (Faradaic efficiency for CO up to 91.6%) but also long-term stability (24 h), are achieved.

Interfacial Property Tuning Enables Copper Electrodes in High-Performance n-i-p Perovskite Solar Cells.

Developing cost-effective metal electrodes is essential for reducing the overall cost of perovskite solar cells (PSCs). Although copper is highly conductive and economical, it is rarely used as a positive electrode in efficient n-i-p PSCs due to its unmatched Fermi level and low oxidation threshold. We report herein that modification for the inner surface of electrodes using mercaptopyridine-based molecules readily tunes the electronic and chemical properties of copper, which has been achieved by fine-tuning the substituents of mercaptopyridines. The systematic adjustment for the Fermi level and oxidation potential of copper facilitates interfacial hole extraction and enhances the oxidation resistance of copper electrodes, which enables pure copper electrodes to be used in high-performance n-i-p PSCs with different hole transport materials. The resulting PSCs with copper electrodes display excellent power conversion efficiency and long-term stability, even comparable to those of the gold electrodes, showing great potential in the manufacturing and commercialization of PSCs.

Mechanism of Particle-Mediated Inhibition of Demetalation for Single-Atom Catalytic Sites in Acidic Electrochemical Environments.

Demetalation, caused by the electrochemical dissolution of metal atoms, poses a significant challenge to the practical application of single-atom catalytic sites (SACSs) in proton exchange membrane-based energy technologies. One promising approach to inhibit SACS demetalation is the use of metallic particles to interact with SACSs. However, the mechanism underlying this stabilization remains unclear. In this study, we propose and validate a unified mechanism by which metal particles can inhibit the demetalation of Fe SACSs. Metal particles act as electron donors, decreasing the Fe oxidation state by increasing the electron density at the FeN4 position, thereby strengthening the Fe-N bond, and inhibiting electrochemical Fe dissolution. Different types, forms, and contents of metal particles increase the Fe-N bond strength to varying extents. A linear correlation between the Fe oxidation state, Fe-N bond strength, and electrochemical Fe dissolution amount supports this mechanism. Our screening of a particle-assisted Fe SACS led to a 78% reduction in Fe dissolution, enabling continuous operation for up to 430 h in a fuel cell. These findings contribute to the development of stable SACSs for energy applications.

Hydrogen Bond Network Induced by Surface Ligands Shifts the Semi-hydrogenation Selectivity over Palladium Catalysts.

Tuning the metal-ligand interfaces of heterogeneous catalysts has emerged as an effective strategy to optimize their catalytic performance. However, improving the selectivity via organic modification remains a challenge so far. In this work, we demonstrate a simple ligand modification by preparing cysteamine-coated ultrathin palladium nanosheets. The as-prepared catalyst exhibits excellent selectivity with durability during catalytic hydrogenation of terminal alkynes, superior to most previously reported ligand-protected palladium catalysts. Further study reveals that a zwitterionic transformation occurs on the palladium interface under the H2 conditions, generating a rigid hydrogen bond network. Such an unexpected effect beyond the traditional steric effect derived from van der Waals interactions makes the catalytic surface favor the hydrogenation of alkynes over alkenes without significantly sacrificing the catalytic activity. These results not only provide a unique steric effect concept for surface coordination chemistry but also provide a practical application to improve the selectivity and activity comprehensively.

Atom-Precise Heteroatom Core-Tailoring of Nanoclusters for Enhanced Solar Hydrogen Generation.

While core-shell nanomaterials are highly desirable for realizing enhanced optical and catalytic properties, their synthesis with atomic-level control is challenging. Here, the synthesis and crystal structure of [Au12 Ag32 (SePh)30 ]4- , the first example of selenolated Au-Ag core-shell nanoclusters, comprising a gold icosahedron core trapped in a silver dodecahedron, which is protected by an Ag12 (SePh)30 shell, is presented. The gold core strongly modifies the overall electronic structure and induces synergistic effects, resulting in high enhancements in the stability and near-infrared-II photoluminescence. The Au12 Ag32 and its homometal analog Ag44 , show strong interactions with oxygen vacancies of TiO2 , facilitating the interfacial charge transfer for photocatalysis. Indeed, the Au12 Ag32 /TiO2 exhibits remarkable solar H2 production (6810 µmol g-1  h-1 ), which is ≈6.2 and ≈37.8 times higher than that of Ag44 /TiO2 and TiO2 , respectively. Good stability and recyclability with minimal catalytic activity loss are additional features of Au12 Ag32 /TiO2 . The experimental and computational results reveal that the Au12 Ag32 acts as an efficient cocatalyst by possessing a favorable electronic structure that aligns well with the TiO2 bands for the enhanced separation of photoinduced charge carriers due to the relatively negatively charged Au12 core. These atomistic insights will motivate uncovering of the structure-catalytic activity relationships of other nanoclusters.

Upgrading heterogeneous Ni catalysts with thiol modification.

Precious metal catalysts are the cornerstone of many industrial processes. Replacing precious metal catalysts with earth-abundant metals is one of key challenges for the green and sustainable development of chemical industry. We report in this work a surprisingly effective strategy toward the development of cost-effective, air-stable, and efficient Ni catalysts by simple surface modification with thiols. The as-prepared catalysts exhibit unprecedentedly high activity and selectivity in the reductive amination of aldehydes/ketones. The thiol modification can not only prevent the deep oxidation of Ni surface to endow the catalyst with long shelf life in air but can also allow the reductive amination to proceed via a non-contact mechanism to selectively produce primary amines. The catalytic performance is far superior to that of precious and non-precious metal catalysts reported in the literature. The wide application scope and high catalytic performance of the developed Ni catalysts make them highly promising for the low-cost, green production of high-value amines in chemical industry.

Heterogeneous Hydrogenation with Hydrogen Spillover Enabled by Nitrogen Vacancies on Boron Nitride-Supported Pd Nanoparticles.

Heterogeneous hydrogenation with hydrogen spillover has been demonstrated as an effective route to achieve high selectivity towards target products. More effort should be paid to understand the complicated correlation between the nature of supports and hydrogenation involving hydrogen spillover. Herein, we report the development of the hydrogenation system of hexagonal boron nitride (h-BN)-supported Pd nanoparticles for the hydrogenation of aldehydes/ketones to alcohols with hydrogen spillover. Nitrogen vacancies in h-BN determine the feasibility of hydrogen spillover from Pd to h-BN. The hydrogenation of aldehydes/ketones with hydrogen spillover from Pd proceeds on nitrogen vacancies on h-BN. The weak adsorption of alcohols to h-BN inhibits the deep hydrogenation of aldehydes/ketones, thus leading to high catalytic selectivity to alcohols. Moreover, the hydrogen spillover-based hydrogenation mechanism makes the catalyst system exhibit a high tolerance to CO poisoning.

Surface and Interface Coordination Chemistry Learned from Model Heterogeneous Metal Nanocatalysts: From Atomically Dispersed Catalysts to Atomically Precise Clusters.

The surface and interface coordination structures of heterogeneous metal catalysts are crucial to their catalytic performance. However, the complicated surface and interface structures of heterogeneous catalysts make it challenging to identify the molecular-level structure of their active sites and thus precisely control their performance. To address this challenge, atomically dispersed metal catalysts (ADMCs) and ligand-protected atomically precise metal clusters (APMCs) have been emerging as two important classes of model heterogeneous catalysts in recent years, helping to build bridge between homogeneous and heterogeneous catalysis. This review illustrates how the surface and interface coordination chemistry of these two types of model catalysts determines the catalytic performance from multiple dimensions. The section of ADMCs starts with the local coordination structure of metal sites at the metal-support interface, and then focuses on the effects of coordinating atoms, including their basicity and hardness/softness. Studies are also summarized to discuss the cooperativity achieved by dual metal sites and remote effects. In the section of APMCs, the roles of surface ligands and supports in determining the catalytic activity, selectivity, and stability of APMCs are illustrated. Finally, some personal perspectives on the further development of surface coordination and interface chemistry for model heterogeneous metal catalysts are presented.