RESUMEN
Monitoring high-temperature strain on curved components in harsh environments is a challenge for a wide range of applications, including in aircraft engines, gas turbines, and hypersonic vehicles. Although there are significant improvements in the preparation of high-temperature piezoresistive film on planar surfaces using 3D printing methods, there are still difficulties with poor surface compatibility and high-temperature strain testing on curved surfaces. Herein, a conformal direct ink writing (CDIW) system coupled with an error feedback regulation strategy was used to fabricate high-precision, thick films on curved surfaces. This strategy enabled the maximum amount of error in the distance between the needle and the substrate on a curved surface to be regulated from 155 to 4 µm. A conformal Pt thick-film strain gauge (CPTFSG) with a room-temperature strain coefficient of 1.7 was created on a curved metallic substrate for the first time. The resistance drift rate at 800 °C for 1 h was 1.1%, which demonstrated the excellent stability and oxidation resistance of the CPTFSG. High-temperature dynamic strain tests up to 769 °C revealed that the sensor had excellent high-temperature strain test performance. Furthermore, the CPTFSG was conformally deposited on an aero-engine turbine blade to perform in situ tensile and compressive strain testing at room temperature. High-temperature strain tests were conducted at 100 and 200 °C for 600 and 580 µÎµ, respectively, demonstrating a high steady-state response consistent with the commercial high-temperature strain transducer. In addition, steady-state strain tests at high temperatures up to 496 °C were tested. The CDIW error modulation strategy provides a highly promising approach for the high-precision fabrication of Pt thick films on complex surfaces and driving in situ sensing of high-temperature parameters on curved components toward practical applications.