The influence of a selected desensitizer on marginal microleakage of a class V composite restoration subjected to thermocycles: an in vitro study.

INTRODUCTION: Dentin hypersensitivity is a painful clinical condition. The frequency of its occurrence varies from 8 to 57%, depending on tested group and different methods of investigations. Recommended desensitizing agents have different mechanism of action and effectiveness. We are still looking for solutions that will improve their effectiveness and simultaneously allow for wider use of e.g. as a base material, counteracting postoperative hypersensitivity, reducing marginal microleakage. The aim of the study was to assess the effect of a selected desensitizing agent occluding dentin tubules with calcium hydroxyapatite on marginal microleakage formation of a class V composite restorations subjected to thermocycles. MATERIALS AND METHODS: In study it was used 40 molars and premolars, which were alternately assigned into two groups. In both groups standardized cavities were prepared. In the study group (study group - SG) before application of bonding agent Teethmate Desensitizer (f. Kuraray, Noritake Dental Inc., Okayama, Japan) was used. In the control group (control group - CG) OptiBond All-in-one (f. Kerr, Bioggio, Switzerland) bonding agent was used and cavities were filled using composite material Gradia Direct (f. GC Europe N.V., Leuven, Belgium). After storage in saline, teeth were subjected to 600 thermocycles, passive dye penetration test was done, teeth were cut in the area of filling, according to its long axis. Under light microscope magnification value of microleakage was measured and marginal microleakage rate (M) was counted. The results of the tests were statistically analyzed using the package STATISTICA 12.0 (StatSoft, USA). RESULTS: The average value of M for the SG group was 0.46 (min 0.05, max 0.76, SD 0.226) and for CG was 0.22 (min 0, max 0.74, SD 0.235). The differences between M values were statistically significant (p = 0.0094). CONCLUSION: A reduction in the number of retention sites for the bonding system, facilitates the formation of microleakage in the experimental conditions and reduces the degree of adhesion of the composite material to the hard tissues of the tooth.

Influência do hidróxido de cálcio e do EDTA na marcaçäo da infiltraçäo marginal de azul de metileno em obturaçäo de canais radiculares / Influence of calcium hydroxide and EDTA in the methilene blue marginal infiltration in filling root canal

A influência do curativo de hidróxido de cálcio na marcaçäo da infiltraçäo marginal de corante azul de metileno a 2 por cento em obturaçöes de canais radiculares realizadas com cimentos de óxido de zinco e eugenol ou pasta de hidróxido de cálcio foi avaliada. Foram empregados 188 dentes incisivos centrais superiores humanos extraídos. Oito serviram como controle e após todos serem instrumentados e impermeabilizados, foram divididos em 3 grupos, utilizando-se EDTA e o hidróxido de cálcio em diferentes momentos e situaçöes. Posteriormente, os dentes foram imersos em soluçäo de azul de metileno a 2 por cento por 72 horas, seccionados longitudinalmente e as infiltraçöes medidas com o emprego de um microscópico óptico munido de uma ocular micrométrica. Após análise estatística, chegou-se às seguintes conclusöes: o hidróxido de cálcio, empregado tanto na forma de curativo como pasta obturadora, diminuiu a magnetude da infiltraçäo (p<0,05). Em relaçäo ao EDTA: empregado previamente ao curativo de hidróxido de cálcio, melhorou o selamento das obturaçöes com óxido de zinco e eugenol (p<0,05); o seu emprego antes e após o curativo, promoveu um aumento da infiltraçäo marginal em canais obturados com óxido de zinco e eugenol (p<0,05); em canais obturados com pasta de hidróxido de cálcio, o seu emprego näo promoveu interferências estatisticamente significantes nos resultados (p<0,05)

Efetividade de adesivos dentinários hidrofílicos no controle da microinfiltraçäo marginal / Effectiveness of hydrophilic dentin bonding agents in controlling microleakage

O objetivo deste trabalho foi avaliar qualitativamente, através da penetraçäo de corante, a capacidade de adesivos dentinários hidrofílicos em controlar a infiltraçäo marginal. Apesar dos bons resultados, nenhum dos sistemas testados evitou totalmente a microinfiltraçäo

Análise "in vitro" da infiltraçäo marginal apical do corante azul-de-metileno, quando da obturaçäo do canal radicular diante da variaçäo dos métodos de secagem / Anals \"in vitro\" of the dental leakage with methylene blue colors, in root canal obturation in dry methods variation

A secagem do canal radicular, imediatamente antes da inserçäo dos materiais obturadores, pode ser obtida pelo emprego da aspiraçäo do conteúdo líquido do canal radicular ou pelo uso de cones de papel absorvente, ou ainda, pela associaçäo de ambos recursos. Remover líquidos da luz do canal radicular e, da própria intimidade do tecido dentinário, propicia melhor aderência entre os materiais obturadores e as paredes dentinárias. Empregando-se dentes humanos extraídos, avaliou-se, com o auxílio do corante azul-de-metileno e leituras lineares efetivas em um projetor de perfil, os níveis de infiltraçäo marginal apical que decorrem, diante da adoçäo de diferentes formas de secagem do canal radicular. O tratamento estatítistico dos resultados apurados tornou evidente que, quanto maior for o índice de remoçäo da umidade do interior do canal e da própria intimidade do tecido dentinário, de qualidade mais significativa, será a impermeabilizaçäo marginal apical da obturaçäo endodôntica. Assim, foi possível demonstrar que, associando-se à aspiraçäo do canal radicular, o emprego de cânulas caracterizadas por calibres decrescentes e aplicadas nos níveis cervical, médio e apical e complementando-se a secagem do canal radicular com cones de papel absorvente, é possível obter-se melhor coaptaçäo do material obturador às paredes dentinárias do que, em condiçöes outras, nas quais, recursos de menor efetividade de secagem do canal forem adotados

Obturaçäo retrógrada: avaliaçäo da adaptaçäo às paredes das cavidades e infiltraçäo marginal, em funçäo dos materiais obturadores e de agentes de limpeza / Retrograde obturation: evaluation of adaptation to cavities wall and marginal leakage, in function of the filling materials and of cleansing solutions

Na execuçäo deste trabalho foram utilizados 180 caninos humanos extraídos, armazenados em H²O destilada e formol a 10 por cento, que após a eliminaçäo da parte coronária tiveram seus ápices biselados a 2 mm, numa inclinaçäo de 45º segundo a técnica de NICHOLLS (97). A seguir os canais radiculares foram preparados, instrumentados, irrigados com soluçäo salina e obturados com guta-percha e cimento de óxido de zinco e eugenol pela técnica da condensaçäo lateral; as amostras foram na sequência impermeabilizadas com exceçäo do ápice biselado onde seriam feitas as retrobturaçöes. Cavidades com broca esférica n§ 2 foram preparadas após a distribuiçäo aleatória dos 18 grupos que receberam durante o preparo, irrigaçöes com soluçäo fisiológica, hipoclorito de sódio a 1 por cento e soluçäo fisiológica, após aplicaçäo prévia do E.D.T.A. por 3 minutos...

Avaliaçäo "in vitro" da influência do cimento adesivo Panavia EX na infiltraçäo marginal de restauraçöes de amálgama de prata / \"In vitro\" evaluation of the influence of the adhesive resin cement lining Panavia EX in marginal leakage of silver amalgam restorations

O objetivo deste trabalho foi avaliar "in vitro" o efeito do cimento adesivo Panavia EX na microinfiltraçäo de restauraçöes de amálgama. Trinta dentes humanos com cavidades Classe V foram divididos em 3 grupos e restaurados da seguinte forma: no grupo A todas as cavidades foram restauradas apenas com amálgama; no grupo B uma camada de Panavia EX foi aplicada às paredes cavitárias antes da restauraçäo e no grupo C, o esmalte do contorno da cavidade foi condicionado com ácido, as paredes da cavidade protegidas com Panavia EX e entäo restauradas com amálgama. Os dentes foram imersos numa soluçäo de azul de metileno e os resultados indicaram que: a) todas as restauraçöes de amálgama sem Panavia EX mostraram infiltraçäo severa e moderada; b) as restauraçöes forradas com Panavia EX tiveram reduzida infiltraçäo quando comparadas com o controle (Grupo A); e, c) näo houve influência do condicionamento ácido quanto à infiltraçäo marginal