RESUMEN
OBJECTIVES: To investigate the effect of neutral 10-methacryloyloxydecyl dihydrogen phosphate salt (MDP-Na) on the dentin bond strength and remineralization potential of etch-&-rinse adhesive. METHODS: Two experimental etch-&-rinse adhesives were formulated by incorporating 0 wt% (E0) or 20 wt% (E20) neutral MDP-Na into a basic primer. A commercial adhesive, Adper Single Bond 2 (SB, 3 M ESPE), served as the control. Sixty prepared teeth were randomly allocated into three groups (n = 20) and bonded using either one of the experimental adhesives or SB. Following 24 h of water storage, the bonded specimens were sectioned into resin-dentin sticks, with four resin-dentin sticks obtained from each tooth for microtensile bond strength (MTBS) test. Half of the sticks from each group were immediately subjected to tensile loading using a microtensile tester at a crosshead speed of 1 mm/min, while the other half underwent tensile loading after 6-month incubation in artificial saliva (AS). The degree of conversion (DC) of both the control and experimental adhesives (n = 6 in each group) and the adsorption properties of MDP-Na on the dentin organic matrix (n = 5 in each group) were determined using Fourier-transform infrared spectrometry. Furthermore, the effectiveness of neutral MDP-Na in promoting the mineralization of two-dimensional collagen fibrils and the adhesive-dentin interface was explored using transmission electron microscopy and selected-area electron diffraction. Two- and one-way ANOVA was employed to assess the impact of adhesive type and water storage on dentin bond strength and the DC (α = 0.05). RESULTS: The addition of MDP-Na into the primer increased both the short- and long-term MTBS of the experimental adhesives (p = 0.00). No difference was noted in the DC between the control, E0 and E20 groups (p = 0.366). The MDP-Na remained absorbed on the demineralized dentin even after thorough rinsing. The intra- and extra-fibrillar mineralization of the two-dimensional collagen fibril and dentin bond hybrid layer was confirmed by transmission electron microscopy and selected-area electron diffraction when the primer was added with MDP-Na. CONCLUSIONS: The use of neutral MDP-Na results in high-quality hybrid layer that increase the dentin bond strength of etch-&-rinse adhesive and provides the adhesive with remineralizing capability. This approach may represent a suitable bonding strategy for improving the dentin bond strength and durability of etch-&-rinse adhesive.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Dentina , Metacrilatos , Resistencia a la Tracción , Metacrilatos/química , Humanos , Recubrimiento Dental Adhesivo/métodos , Dentina/ultraestructura , Dentina/efectos de los fármacos , Recubrimientos Dentinarios/química , Remineralización Dental/métodos , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Grabado Ácido Dental/métodos , Análisis del Estrés Dental , Técnicas In Vitro , Cementos de Resina/química , Espectroscopía Infrarroja por Transformada de Fourier , Cementos Dentales/química , Propiedades de SuperficieRESUMEN
OBJECTIVES: To investigate urushiol's potential as a dentin cross-linking agent, promoting remineralization of etched dentin and preventing activation of endogenous proteases causing collagen degradation within the hybrid layer. The goal is to improve bond strength and durability at the resin-dentin interface. METHODS: Urushiol primers with varying concentrations were prepared using ethanol and dimethyl sulfoxide (DMSO) as solvents. Dentin from healthy molars underwent grinding and acid etching for 15 s, followed by a 1min application of urushiol primer. After 14 and 28 days of remineralization incubation and remineralization were used to assess by Attenuated Total Reflection Fourier Transform Infrared spectroscopy (ATR-FTIR), Micro-Raman spectroscopy, X-ray Diffraction (XRD), Atomic Force Microscopy (AFM), Vickers Hardness, Scanning Electron Microscopy (SEM), and Energy X-ray dispersive spectroscopy (EDS). The overall performance of urushiol primers as dentin adhesives was observed by microtensile bond strength (µTBS) testing and nanoleakage assessment. Investigated the inhibitory properties of the urushiol primers on endogenous metalloproteinases (MMPs) utilizing in situ zymography, and the cytotoxicity of the primers was tested. RESULTS: Based on ATR-FTIR, Raman, XRD, EM-EDS and Vickers hardness analyses, the 0.7%-Ethanol group significantly enhanced dentin mineral content and improved mechanical properties the most. Pretreatment notably increased the µTBS of restorations, promoted the stability of the mixed layer, and reduced nanoleakage and MMPs activity after 28 days. SIGNIFICANCE: The urushiol primer facilitates remineralization in demineralized dentin, enhancing remineralization in etched dentin, effectively improving the bonding interface stability, with optimal performance observed at a 0.7 wt% concentration of the urushiol primer.
Asunto(s)
Dentina , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Solventes , Resistencia a la Tracción , Remineralización Dental , Humanos , Espectroscopía Infrarroja por Transformada de Fourier , Dentina/efectos de los fármacos , Remineralización Dental/métodos , Solventes/química , Difracción de Rayos X , Recubrimientos Dentinarios/química , Espectrometría Raman , Propiedades de Superficie , Recubrimiento Dental Adhesivo/métodos , Microscopía de Fuerza Atómica , Técnicas In Vitro , Grabado Ácido Dental , Espectrometría por Rayos X , Diente Molar , Reactivos de Enlaces Cruzados/química , DurezaRESUMEN
AIM: The objective of the present study was to evaluate the influence of different adhesive strategies regarding shear bond strength (SBS) of provisional resin--based materials bonded to the enamel surface as well as on the enamel surface roughness. MATERIALS AND METHODS: Bovine incisors were randomly divided into six groups (n = 10) according to the adhesive strategy used: BRControl (bis-acrylic resin); Spot-etch+BR (spot-etch + bis-acrylic resin); Spot--etchSB2+BR (spot-etch + adhesive + bis-acrylic resin); Spot-etchZ350Flow+BR (spot-etch + flowable composite resin + bis-acrylic resin); SBU+BR (universal adhesive + bis-acrylic resin); Spot-etchSBMP+Z350 (spot-etch + adhesive + composite resin). The enamel surface roughness was determined by a surface profil-ometer. An SBS test was performed in a universal testing machine, and failure modes were classified under magnification. The SBS data were analyzed by one-way analysis of variance (ANOVA). A paired t test was used for enamel surface roughness intragroup comparisons, and the Friedman one-way repeated meas-ures analysis of variance by ranks was used for differences in enamel surface roughness between groups, with the Tukey post hoc test (a = 0.05). RESULTS: BRControl had the lowest SBS values (MPa), with a significant difference (P ≤ 0.001) from the other groups. Spot-etch+BR had the highest SBS values but with no significant differences from the other groups in which the spot-etch technique was also used. Adhesive failure mode was predominant for all groups. BRControl had the lowest surface roughness difference, significantly different (P = 0.001) from all the other groups. CONCLUSIONS: Spot-etch and other adhesive strategies could be applied to increase the SBS values of provisional restorations to enamel compared with no surface pretreatment. However, the adhesive strategy may change the enamel surface roughness, revealing the importance of cleaning the tooth surface.
Asunto(s)
Resinas Compuestas , Recubrimiento Dental Adhesivo , Esmalte Dental , Coronas con Frente Estético , Resistencia al Corte , Propiedades de Superficie , Animales , Bovinos , Resinas Compuestas/química , Recubrimiento Dental Adhesivo/métodos , Grabado Ácido Dental/métodos , Análisis del Estrés Dental , Resinas Acrílicas/química , Ensayo de Materiales , Distribución AleatoriaRESUMEN
PURPOSE: The primary objective of this study was to determine which single-shade composite surface yielded clinically acceptable shear bond strength (SBS) to metal orthodontics brackets. The secondary objectives were to identify the best composite surface treatment to enhance SBS and determine which surface treatment produced the least surface damage at debond. METHODS: Forty dental composite samples were selected from four different manufacturers (n=160) and grouped by manufacturer, one standard multi-shade dental system (FilTek™ Supreme Ultra) and three single-shade dental composites systems (OmniChroma®, SimpliShade™ and Venus® Diamond One). Each group of forty samples was randomly divided into four sub-groups (n=10). Each sub-group was identified by the surface treatment used, hydrofluoric acid (HFA), micro-etching (MIC), or phosphoric acid (PA). Shear bond strength testing and adhesive remnant index (ARI) were performed. Statistical analyses included Kruskal-Wallis, Wilcoxon rank-sum, and two-factorial ANOVA. RESULTS: OmniChroma® had statistically significant lower shear bond strength than the other composite materials tested. The control groups had statistically significant lower shear bond strength than Group 1/HFA (P<0.001) and Group 2/MIC (P<0.001). Group 1/HFA had the lowest distribution ARI score overall, while MIC had the highest ARI score distributions. CONCLUSIONS: The results of this in-vitro study found that all tested composite materials achieved clinically acceptable shear bond strengths. The utilization of micro-etching produced higher SBS. Significant Adhesive Remnant Index scores (< 0.001) were only found for OmniChroma® without any surface preparation.
Asunto(s)
Resinas Compuestas , Recubrimiento Dental Adhesivo , Ensayo de Materiales , Soportes Ortodóncicos , Resistencia al Corte , Propiedades de Superficie , Resinas Compuestas/química , Recubrimiento Dental Adhesivo/métodos , Grabado Ácido Dental , Ácidos Fosfóricos/química , Análisis del Estrés Dental , Humanos , Ácido Fluorhídrico/química , Grabado Dental/métodos , Cementos de Resina/químicaRESUMEN
OBJECTIVES: To assess the impact of various organic and inorganic acids on the roughness, demineralization, and collagen secondary structures of human dentin and to compare these effects with those of traditional agents, specifically phosphoric acid (PA) and ethylenediaminetetraacetic acid (EDTA). METHODS: Coronal dentin discs (n = 10) were examined by optical profilometry (roughness) and ATR-FTIR before and after conditioning with 32 % PA, 3 % nitric acid (NA), 20 % citric acid (CA), 20 % phytic acid (IP6) or 17 % EDTA. Spectra data were processed to quantify dentin demineralization (DM%) and percentage area of amide I curve-fitted components of ß-turns, 310-helix, α-helix, random coils, ß-sheets, and collagen maturation index. Statistical analysis was performed by one-way ANOVA or Kruskal-Wallis for DM% and roughness parameters, and paired t-test/Wilcoxon test for amide I components at significance level set at α = 0.05. RESULTS: All treatments resulted in increased roughness parameters, with the most significant changes occurring primarily with PA, while EDTA exhibited the least changes. DM% was NA>PA>IP6>CA>EDTA in a descending order. Regarding amide I components, NA demonstrated a significant reduction in ß-turns, 310-helices, and α-helices and it increased ß-sheets and random coils. PA resulted in reduction in ß-turns and α-helices while it increased ß-sheets. CA and EDTA did not cause significant changes. The collagen maturation index significantly increased only after IP6 treatment. CONCLUSIONS: The effect on dentin roughness parameters, demineralization, and collagen secondary structures varied based on the type of dentin surface treatment. CLINICAL SIGNIFICANCE: Understanding the impact of acids on the intrinsic properties of dentin is clinically essential for gaining insights into how these effects influence adhesion to dentin, the long-term stability of resin-based restorations, and the success of remineralization therapies.
Asunto(s)
Ácido Cítrico , Colágeno , Dentina , Ácido Edético , Ácidos Fosfóricos , Propiedades de Superficie , Desmineralización Dental , Dentina/efectos de los fármacos , Humanos , Ácido Edético/farmacología , Ácido Edético/química , Ácido Cítrico/farmacología , Ácido Cítrico/química , Ácidos Fosfóricos/química , Ácidos Fosfóricos/farmacología , Espectroscopía Infrarroja por Transformada de Fourier , Ácido Fítico/farmacología , Ácido Fítico/química , Estructura Secundaria de Proteína , Grabado Ácido Dental , Ensayo de Materiales , Conformación Proteica en Hélice alfaRESUMEN
OBJECTIVE: To investigate the effect of decontamination procedures on the microshear bond strength (µSBS) of blood-contaminated resin-modified glass ionomer cement (RMGIC) bonded to resin composite (RC). METHODS: Eighty RMGIC disc specimens were allocated into 5 groups (n=16). All groups except Group 2 were contaminated with blood. Group 1 had no decontamination procedure, Group 3 was decontaminated by rinsing, Group 4 was decontaminated by 34% phosphoric acid etching, and Group 5 was decontaminated by 5% sodium hypochlorite application. RMGIC specimens were subsequently bonded with RC using a universal adhesive in self-etch mode. µSBS tests were conducted using a universal testing machine at a crosshead speed of 1 mm/min. Failure mode analysis was conducted on RMGIC fracture surfaces under a scanning electron microscope. RESULTS: µSBS results indicated that Group 4 had the highest mean µSBS value of 6.22 ± 2.14 MPa, while Group 1 had the lowest mean µSBS value of 3.53 ±1.67 MPa. Significant differences were observed in the µSBS of Group 2 with no contamination (p=0.023) and Group 4 with decontamination by phosphoric acid-etching (p=0.003) when compared to Group 1 with blood contamination. No statistically significant differences (p>0.05) were observed between all other groups' µSBS. For all groups, the predominant mode of failure was adhesive failure between the RMGIC-RC interface, with a few mixed failures in RMGIC for Groups 2-5. CONCLUSIONS: Blood contamination before adhesive application significantly reduced the µSBS between RMGIC and RC. Phosphoric acid etching was the most effective blood decontamination procedure to improve the µSBS.
Asunto(s)
Resinas Compuestas , Descontaminación , Recubrimiento Dental Adhesivo , Cementos de Ionómero Vítreo , Resistencia al Corte , Resinas Compuestas/uso terapéutico , Resinas Compuestas/química , Descontaminación/métodos , Cementos de Ionómero Vítreo/uso terapéutico , Recubrimiento Dental Adhesivo/métodos , Humanos , Ensayo de Materiales , Análisis del Estrés Dental , Sangre , Grabado Ácido Dental/métodos , Ácidos Fosfóricos , Microscopía Electrónica de Rastreo , Cementos de Resina/uso terapéuticoRESUMEN
The aim of this study was to evaluate the influence of implant macrodesign and surface hydrophilicity on osteoclast (OC) differentiation, activation, and survival in vitro. Titanium disks were produced with a sandblasted, dual acid-etched surface, with or without additional chemical modification for increasing hydrophilicity (SAE-HD and SAE, respectively) and different macrodesign comprising trapezoidal (HLX) or triangular threads (TMX). This study evaluated 7 groups in total, 4 of which were experimental: HLX/SAE-HD, HLX-SAE, TMX/SAE-HD, and TMX/SAE; and 3 control groups comprising OC differentiated on polystyrene plates (CCPC): a positive CCPC (+), a negative CCPC (-), and a lipopolysaccharide-stimulated assay positive control group, CCPC-LPS. Murine macrophage RAW264.7 cells were seeded on the disks, differentiated to OC (RAW-OC) by receptor activator of nuclear factor-κB ligand (RANKL) treatment and cultured for 5 days. Osteoclast differentiation and cell viability were respectively assessed by specific enzymatic Tartrate-Resistant Acid Phosphatase (TRAP) activity and MTT assays. Expression levels of various OC-related genes were measured at the mRNA level by quantitative polymerase chain reaction (qPCR). HLX/SAE-HD, TMX/SAE-HD, and HLX/SAE significantly suppressed OC differentiation when compared to CCPC (+). Cell viability was significantly increased in TMX/SAE and reduced in HLX/SAE-HD. In addition, the expression of Interleukin (IL)-6 and Tumour Necrosis Factor (TNF)-α was upregulated in TMX/SAE-HD compared to CCPC (+). Hydrophilic surfaces negatively modulate macrophage/osteoclast viability. Specifically, SAE-HD with double triangular threads increases the cellular pro-inflammatory status, while surface hydrophilicity and macrodesign do not seem to have a distinct impact on osteoclast differentiation, activation, or survival.
Asunto(s)
Diferenciación Celular , Supervivencia Celular , Interacciones Hidrofóbicas e Hidrofílicas , Osteoclastos , Propiedades de Superficie , Titanio , Titanio/química , Osteoclastos/efectos de los fármacos , Diferenciación Celular/efectos de los fármacos , Animales , Supervivencia Celular/efectos de los fármacos , Ratones , Factores de Tiempo , Grabado Ácido Dental , Osteogénesis/efectos de los fármacos , Osteogénesis/fisiología , Ensayo de Materiales , Reproducibilidad de los Resultados , Fosfatasa Ácida Tartratorresistente/análisis , Análisis de Varianza , Ligando RANK/análisis , Reacción en Cadena en Tiempo Real de la Polimerasa , Células RAW 264.7 , Valores de Referencia , Macrófagos/efectos de los fármacosRESUMEN
Aims - to compare the color changes, the surface roughness and morphology of the enamel bleached with two different bleaching solutions (chemical and laser activated), preceded or not with acid etching. Thirty teeth of bovine prepared and haphazardly assigned to 2 groups (n=15) depending on bleaching technique. Each group subdivided to 3 subgroup (n=5) consistent with acid etching by 37% phosphoric acid. Atomic force microscopy and VITA easy shade spectrophotometer were performed twice for all the specimens before and after bleaching. ANOVA, the Paired sample t-test, and the independent sample t-test used for statistical analysis. As for the color changes, the groups that were bleached by the chemical method, the difference among the three subgroups was statistically significant. This also applies to the groups bleached with the laser method. When comparing the results of the chemical bleaching subgroups with the laser bleaching ones, the difference was not significant. Roughness results showed significant differences between certain subgroups and non-significant differences among others. However, the difference was statistically significant between the chemical and laser groups, laser technique resulted in less surface roughness than the chemical one. Acid etching before bleaching produced better colour change in both the chemical and laser assisted bleaching. In chemical bleaching, surface roughness was higher when acid etching was used. This was also true for laser bleaching technique. In general, laser assisted bleaching produced less surface roughness than chemical bleaching.
Asunto(s)
Grabado Ácido Dental , Esmalte Dental , Propiedades de Superficie , Blanqueamiento de Dientes , Esmalte Dental/efectos de los fármacos , Esmalte Dental/química , Bovinos , Animales , Blanqueamiento de Dientes/métodos , Propiedades de Superficie/efectos de los fármacos , Color , Ácidos Fosfóricos/química , Ácidos Fosfóricos/farmacología , Microscopía de Fuerza Atómica , Blanqueadores Dentales/química , Blanqueadores Dentales/farmacología , Espectrofotometría , Rayos LáserRESUMEN
This study investigated the impact of adding hydroxyapatite nanoparticles to implant surfaces treated with zirconia blasting and acid etching (ZiHa), focusing on structural changes and bone healing parameters in low-density bone sites. The topographical characterization of titanium discs with a ZiHa surface and a commercially modified zirconia-blasted and acid-etched surface (Zi) was performed using scanning electron microscopy, profilometry, and surface-free energy. For the in vivo assessment, 22 female rats were ovariectomized and kept for 90 days, after which one implant from each group was randomly placed in each tibial metaphysis of the animals. Histological and immunohistochemical analyses were performed at 14 and 28 days postoperatively (decalcified lab processing), reverse torque testing was performed at 28 days, and histometry from calcified lab processing was performed at 60 days The group ZiHa promoted changes in surface morphology, forming evenly distributed pores. For bone healing, ZiHa showed a greater reverse torque, newly formed bone area, and bone/implant contact values compared to group Zi (p < 0.05; t-test). Qualitative histological and immunohistochemical analyses showed higher features of bone maturation for ZiHa on days 14 and 28. This preclinical study demonstrated that adding hydroxyapatite to zirconia-blasted and acid-etched surfaces enhanced peri-implant bone healing in ovariectomized rats. These findings support the potential for improving osseointegration of dental implants, especially in patients with compromised bone metabolism.
Asunto(s)
Durapatita , Nanopartículas , Oseointegración , Propiedades de Superficie , Circonio , Circonio/química , Animales , Durapatita/química , Durapatita/farmacología , Femenino , Ratas , Nanopartículas/química , Oseointegración/efectos de los fármacos , Implantes Dentales , Titanio/química , Tibia/efectos de los fármacos , Tibia/cirugía , Grabado Ácido DentalRESUMEN
Background: The aim of this study was threefold. Firstly, it aimed to introduce and detail a novel method for chemically etching the bases of stainless-steel orthodontic brackets. Secondly, the study sought to investigate the structural alterations within the brackets' microstructure following chemical etching compared to those with sandblasted bases, using electron microscopy analysis. Lastly, the study aimed to evaluate and compare the long-term durability and survivability of orthodontic brackets with chemically etched bases versus those with sandblasted bases, both bonded using the conventional acid etch technique with Transbond XT adhesive, over an 18-month follow-up period. Methods: The study was a randomized clinical control trial with triple blinding and split-mouth study design and consisted of two groups. The brackets in the sandblasted group were prepared by sandblasting the intaglio surface of the base of the bracket with 50 µm SiO2 particles. Hydrofluoric acid was used to roughen the base in the acid-etched group. The bases of the brackets were viewed under an electron microscope to analyze the topographical changes. Results: A total of 5,803 brackets (3,006 acid-etch, 2,797 sandblasted) in 310 patients were bonded, in a split-mouth design by the same operator. The patients were followed for 18 months. The failure rate of 2.59% and 2.7% was noted in an acid-etched and sandblasted group, respectively. There was a close approximation of curves in the Kaplan-Meier plot, and the survival distribution of the two groups in the log-rank (Mantel-Cox) test was insignificant; x2 = 0.062 (P value = 0.804). Conclusion: Acid etching if the bases of the brackets can be used as an alternative to sandblasting furthermore acid etching can be performed on the chair side.
Asunto(s)
Grabado Ácido Dental , Recubrimiento Dental Adhesivo , Microscopía Electrónica de Rastreo , Soportes Ortodóncicos , Humanos , Grabado Ácido Dental/métodos , Femenino , Masculino , Recubrimiento Dental Adhesivo/métodos , Adolescente , Propiedades de Superficie , Adulto , Cementos de Resina/química , Adulto Joven , Acero Inoxidable/química , Grabado Dental/métodosRESUMEN
The glass infiltration technique was employed for surface modification of zirconia implants in this study. The prepared glass-infiltrated zirconia with low infiltrating temperature showed excellent mechanical properties and enough infiltrating layer. The zirconia substrate was pre-sintered at 1,200°C and the glass infiltration depth reached 400 µm after infiltrating at 1,200°C for 10 h. The infiltrating glass has good wetting ability, thermal expansion match and good chemical compatibility with the zirconia substrate. Indentation fracture toughness and flexural strength of the dense sintered glass-infiltrated zirconia composite are respectively 5.37±0.45 MPaâ¢m1/2 and 841.03±89.31 MPa. Its elasticity modulus is 163.99±7.6 GPa and has about 500 µm infiltrating layer. The glass-infiltrated zirconia can be acid etched to a medium roughness (1.29±0.09 µm) with a flexural strength of 823.65±87.46 MPa, which promotes cell proliferation and has potential for dental implants.
Asunto(s)
Implantes Dentales , Resistencia Flexional , Vidrio , Ensayo de Materiales , Propiedades de Superficie , Circonio , Circonio/química , Vidrio/química , Módulo de Elasticidad , Temperatura , Materiales Dentales/química , Grabado Ácido DentalRESUMEN
This study aimed to evaluate the microleakage of light-cured and self-cured adhesives on enamel surfaces selectively etched with Er, Cr: YSGG laser or 35% phosphoric acid. A total of 60 class V cavities were prepared 1 mm above the cemento-enamel junction (CEJ). The specimens were randomly divided into six groups. Group 1: Clearfil SE Bond with no conditioning, Group 2: Tokuyama Universal Bond with no conditioning, Group 3: Clearfil SE Bond conditioned with 35% phosphoric acid, Group 4: Tokuyama Universal Bond conditioned with 35% phosphoric acid, Group 5: Clearfil SE Bond conditioned with Er, Cr: YSGG laser and Group 6: Tokuyama Universal Bond conditioned with Er, Cr: YSGG laser. Microleakage was evaluated qualitatively (visually) and quantitatively (ImageJ). The data were analyzed using IBM SPSS V23 and submitted to Kruskal-Wallis and Wilcoxon tests. The significance level was set at p < 0.05. In all evaluation methods, the microleakage scores exhibit significant differences (p*<0.001). Group 1 and Group 3 exhibited similar and lower microleakage values than the Group 5. In the occlusal margin, the microleakage values were similar in Group 2, Group 4, and Group 6, whereas in the gingival margin Group 4 showed significantly lower leakage compared to Group 2. Regardless of the etching protocols and adhesive systems used, less microleakage was observed on the occlusal surface than on the gingival surface. Phosphoric acid etching provides better results than laser etching for enamel surface treatment on both occlusal and gingival surfaces.
Asunto(s)
Grabado Ácido Dental , Esmalte Dental , Filtración Dental , Láseres de Estado Sólido , Humanos , Esmalte Dental/efectos de la radiación , Esmalte Dental/efectos de los fármacos , Láseres de Estado Sólido/uso terapéutico , Cementos de Resina/química , Ácidos Fosfóricos/química , Cementos Dentales/química , Técnicas In VitroRESUMEN
PURPOSE: This study evaluated the implant stability, volumetric changes, and patient-reported outcome measures (PROMs) of hydroxyapatite (HA) nano-coated sandblasted/acid-etched (SLA) implants compared to uncoated SLA implants. METHODS: Forty patients were recruited and randomly allocated to HA nano-coated SLA group (test, n = 20) and uncoated SLA group (control, n = 20) using single-blinded/block randomization. Implants were immediately placed in maxillary posterior region using a digital surgical guide. Insertion torque and implant stability quotient (ISQ) were measured at implant surgery and 1, 2, 3, and 4 months postoperatively. Intraoral scans, PROMs and soft tissue inflammation data were collected, and multivariable linear regression analysis of ISQ was performed. RESULTS: In total, 48 implants (test; n = 24, control; n = 24) in 37 patients (test; n = 19, control; n = 18) were analyzed. Despite no significant between-group difference at surgery, the test group showed higher ISQ values than the control group at 2 (76.53 ± 4.17 vs. 71.32 ± 4.79, p < 0.01), 3 (77.45 ± 4.41 vs. 73.85 ± 4.69, p < 0.05), and 4 months (79.08 ± 2.96 vs. 73.43 ± 3.52, p < 0.0001) postoperatively. There were no significant differences in linear and volumetric changes, PROMs, and soft tissue inflammation analysis between two groups. The ISQ at implant surgery was influenced by age and diabetes mellitus (DM) at the implant level and DM and predicted total bone-to-implant contact area at the patient level. CONCLUSION: HA nano-coated SLA implants promoted favorable immediate implants stability during early osseointegration phase compared to uncoated SLA implants, but displayed similar dimensional changes, PROMs, and soft tissue inflammation outcomes. TRIAL REGISTRATION: Clinical Research Information Service (CRIS), KCT0006364. Registered 21 July 2021, https://cris.nih.go.kr/cris/search/detailSearch.do?seq=24221&search_page=L .
Asunto(s)
Durapatita , Humanos , Masculino , Femenino , Persona de Mediana Edad , Método Simple Ciego , Implantes Dentales , Carga Inmediata del Implante Dental/métodos , Adulto , Materiales Biocompatibles Revestidos/química , Grabado Ácido Dental , Anciano , Medición de Resultados Informados por el Paciente , Oseointegración , Propiedades de SuperficieRESUMEN
BACKGROUND: To investigate the effect of a 50% ascorbic acid with 50% citric acid solution on the immediate shear bond strength (SBS) of metallic brackets after tooth bleaching. The enamel etching pattern and the required quantity of these combined acids as antioxidants following 35% hydrogen peroxide (HP) bleaching were also determined. METHODS: The stability of the solution at room temperature was assessed at various time intervals. Fifty teeth were randomly divided into five groups: non-bleached (G1), bleached then acid etched (G2), bleached followed by a 10-minute treatment with 10% sodium ascorbate and acid etched (G3), 5-minute treatment with 50% ascorbic acid (G4), and 5-minute treatment with a combination of 50% ascorbic acid and 50% citric acid (G5). Groups G2, G3, G4 and G5 were bleached by 35% HP gel for a total of 32 min. Acid etching in groups G1, G2, and G3 was performed using 37% phosphoric acid (Ormco®, Orange, CA, USA) for 15 s. In all groups, metal brackets were immediately bonded using Transbond™ XT primer and Transbond™ PLUS adhesive, with light curing for 40 s. The SBS was tested with a universal testing machine, and statistical analysis was conducted using one-way ANOVA followed by Tukey's HSD test. The level of significance was set at p < 0.05 for all statistical tests. RESULTS: Stability tests demonstrated that the combined acids remained effective for up to 21 days. Group G5 significantly increased the SBS of bleached teeth to the level of G1 (p < 0.05), while G3 did not achieve the same increase in SBS (p > 0.05). SEM analysis revealed enamel etching patterns similar to those of both control groups (G1 and G2). Kinetic studies at 6 min indicated that the antioxidation in G5 reacted 0.2 mmole lower than in G3 and G4. CONCLUSION: 5-minute application of the combined acids enhanced the SBS of bleached teeth comparable to unbleached teeth. The combined acids remain stable over two weeks, presenting a time-efficient, single-step solution for antioxidant application and enamel etching in orthodontic bracket bonding.
Asunto(s)
Ácido Ascórbico , Ácido Cítrico , Recubrimiento Dental Adhesivo , Esmalte Dental , Soportes Ortodóncicos , Resistencia al Corte , Blanqueamiento de Dientes , Ácido Ascórbico/farmacología , Ácido Cítrico/farmacología , Ácido Cítrico/química , Blanqueamiento de Dientes/métodos , Humanos , Proyectos Piloto , Esmalte Dental/efectos de los fármacos , Recubrimiento Dental Adhesivo/métodos , Grabado Ácido Dental , Antioxidantes/farmacología , Propiedades de Superficie , Factores de Tiempo , Peróxido de Hidrógeno/química , Blanqueadores Dentales/química , Ácidos Fosfóricos , Análisis del Estrés DentalRESUMEN
OBJECTIVE: This study aimed to evaluate the effect of ultrasonic activation of etch-and-rinse and self-etch adhesive systems on the bond strength of resin cement to irradiated root dentin. MATERIALS AND METHODS: Eighty human maxillary anterior teeth were distributed into 8 groups (n = 10), according to the type of adhesive system used (etch-and-rinse and self-etch), the ultrasonic activation of the adhesive systems, and the dentin condition (irradiated or non-irradiated - 70 Gy). Endodontic treatment was performed followed by fiberglass post-space preparation. After fiberglass posts' luting, the roots were transversely sectioned on dentin discs and submitted to the push-out bond strength test (0.5 mm/min). The fractured specimens were analyzed under a stereomicroscope and Scanning Electron Microscope (SEM) for failure mode classification. One of the dentin discs was analyzed under SEM to evaluate the characteristics of the adhesive interface. RESULTS: Irradiated specimens had lower bond strength than non-irradiated specimens (P < 0.0001). Ultrasonic activation of both adhesive systems increased the bond strength of the resin cement to irradiated dentin (P < 0.0001). Radiotherapy significantly affected the failure mode in the middle (P = 0.024) and apical thirds (P = 0.032) (adhesive failure). CONCLUSION: Non-irradiated specimens had a more homogeneous adhesive interface. When ultrasonically activated, both adhesive systems showed a greater number of resinous tags, regardless of the dentin condition. CLINICAL RELEVANCE: Ultrasonic activation of adhesive systems is a feasible strategy to enhance fiberglass posts retention in oncological patients.
Asunto(s)
Recubrimiento Dental Adhesivo , Dentina , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Técnica de Perno Muñón , Cementos de Resina , Humanos , Cementos de Resina/química , Recubrimiento Dental Adhesivo/métodos , Dentina/efectos de la radiación , Técnicas In Vitro , Recubrimientos Dentinarios/química , Análisis del Estrés Dental , Propiedades de Superficie , Raíz del Diente/efectos de la radiación , Ultrasonido , Grabado Ácido Dental , Incisivo , Vidrio/químicaRESUMEN
The surface treatment of glass-ceramic-based materials, namely, lithium disilicate glass (IPS e.max CAD), feldspar porcelain (VITABLOCS Mark II), and a polymer-infiltrated ceramic network (VITA ENAMIC), using aqueous fluoride solutions and their influence on luting agent bonding were investigated. Six experimental aqueous fluoride solutions were applied to these materials, and their effects were assessed by surface topological analysis. The obtained results were compared using non-parametric statistical analyses. Ammonium hydrogen fluoride (AHF) etchant demonstrated the greatest etching effect. Subsequent experiments focused on evaluating different concentrations of the AHF etchant for the bonding pretreatment of glass-ceramic-based materials with a luting agent (PANAVIA V5). AHF, particularly at concentrations above 5 wt%, effectively roughened the surfaces of the materials and improved the bonding performance. Notably, AHF at a concentration of 30 wt% exhibited a more pronounced effect on both etching and bonding capabilities compared to hydrofluoric acid.
Asunto(s)
Cerámica , Diseño Asistido por Computadora , Porcelana Dental , Fluoruros , Ácido Fluorhídrico , Ensayo de Materiales , Propiedades de Superficie , Fluoruros/química , Cerámica/química , Porcelana Dental/química , Ácido Fluorhídrico/química , Recubrimiento Dental Adhesivo/métodos , Grabado Ácido Dental , Silicatos de Aluminio/química , Compuestos de Potasio/química , Compuestos de Amonio/químicaRESUMEN
The aim of this study was to evaluate the effects of the application of universal adhesive in the etch-and-rinse (ER) strategy with a manual brush (MB) or rotary brush (RB) in adhesion to dentin impregnated (WB) or not (NB) with bioceramic sealer, at 24 h and 1 year. Eighty-eight crowns of bovine incisors were divided into four groups (n=22): WB-MB, WB-RB, NB-MB, NB-RB. After the restorative protocol, dentin penetrability was evaluated by confocal microscopy. Bond strength was evaluated by microtensile test. Data were analyzed using one-way ANOVA/Tukey tests (α=0.05). NB-RB and WB-RB exhibited greater extensions of resin tags in dentin. At 24 h, WB-RB and NB-MB showed the highest and lowest values of bond strength, respectively. At 1 year, WB-MB and WB-RB demonstrated the highest bond strength values. The RB increases the formation of resin tags and residues of bioceramic sealer provides higher bond strength in the ER strategy.
Asunto(s)
Recubrimiento Dental Adhesivo , Animales , Bovinos , Recubrimiento Dental Adhesivo/métodos , Resistencia a la Tracción , Cerámica/química , Ensayo de Materiales , Microscopía Confocal , Recubrimientos Dentinarios/química , Dentina/química , Grabado Ácido DentalRESUMEN
Adhesive dentistry is an essential component in the delivery of direct and indirect restorations. Ongoing discussions among scientists and clinicians have focused on whether or not current self-etch and universal adhesives adequately prepare enamel surfaces to achieve optimal bond strengths. To address these concerns, a selective enamel etch technique has been recommended. The definition of a selective enamel etch technique is as its name suggests. The clinician selectively etches the enamel of a cavity preparation by applying phosphoric acid etchant to the enamel surfaces of the preparation while refraining from applying the etchant to the dentin. This article explores the current research to help guide clinicians to achieve ideal outcomes when using dental adhesives. With few exceptions, the current scientific evidence recommends a selective enamel etch technique in conjunction with the clinician's adhesive system of choice.
Asunto(s)
Grabado Ácido Dental , Recubrimiento Dental Adhesivo , Esmalte Dental , Humanos , Esmalte Dental/efectos de los fármacos , Grabado Ácido Dental/métodos , Recubrimiento Dental Adhesivo/métodos , Ácidos Fosfóricos/química , Preparación de la Cavidad Dental/métodosRESUMEN
This study evaluated bond strength of glass fiber posts to root dentin using push-out (PO) and diametral compression (DC), testing glycolic acid as a conditioner and varying dentin moisture. An additional aim was to test whether DC can be an alternative test to PO for bond strength assessment. Eighty bovine teeth were divided into eight groups (n = 10) defined by the use of either 37% glycolic acid or 37% phosphoric acid (PA) on moist or wet dentin before bonding with either Adapter SingleBond/RelyX ARC or One Step Plus/Duo-Link Bisco. Each tooth provided discs with an internal diameter of 2 mm, external diameter of 5 mm, and height of 2 mm, which underwent PO and DC. Finite element analysis (FEA) was carried out on 3D models. When analyzing PO results through linear regression, the highest values of bond strength were observed using glycolic acid on wet dentin in the cervical and middle thirds of the teeth. Analyzing DC results, the only statistical influence on values was the dental thirds. The scatterplot of the DC results and the PO bond strength values indicated no relationship between the results of the two tests (r = 0.03; p = 0.64). PO test detected more sensitive changes in bond strength values than DC.