RESUMO
BACKGROUND Dentin contamination with hemostatic agents before bonding indirect restorations negatively affects the bond strength. However, the consensus on which materials could be used to clean contamination of hemostatic agents has not been explored. The aim of this study was to assess the effect of Katana Cleaner applied on the surface of dentin contaminated with hemostatic agents on the shear bond strength (SBS) of self-adhesive resin cement by comparing it with three other surface cleaners. MATERIAL AND METHODS Ninety dentin specimens were divided into a no contamination group (control) (n=10), 4 groups contaminated with 25% aluminum chloride (Viscostat Clear) (n=40), and 4 groups contaminated with 20% ferric sulfate (Viscostat) (n=40). Subsequently, 4 different cleaners were used for each contamination group (water rinse, phosphoric acid, chlorhexidine, and Katana Cleaner). Then, self-adhesive resin cement was directly bonded to the treated surfaces. All specimens were subjected to 5000 thermal cycles of artificial aging. The shear bond strength was measured using a universal testing machine. RESULTS Two-way analysis of variance showed that the contaminant type as the main factor was statistically non-significant (p=0.655), cleaner type as the main factor was highly significant (p<0.001), and interaction between the contaminant and cleaner was non-significant (p=0.51). The cleaner type was the main factor influencing the bond strength. Phosphoric acid and chlorhexidine showed better performance than Katana Cleaner. CONCLUSIONS Cleaning dentin surface contamination with phosphoric acid and chlorhexidine had better performance than with Katana Cleaner.
Assuntos
Colagem Dentária , Dentina , Hemostáticos , Cimentos de Resina , Resistência ao Cisalhamento , Humanos , Dentina/efeitos dos fármacos , Hemostáticos/farmacologia , Colagem Dentária/métodos , Clorexidina/análogos & derivados , Clorexidina/farmacologia , Teste de Materiais/métodos , Propriedades de Superfície/efeitos dos fármacos , Adesivos Dentinários , Compostos Férricos/químicaRESUMO
BACKGROUND: The stability of resin-dentin interfaces is still highly questionable. The aim of this study was to evaluate the effect of Salvadora persica on resin-dentin bond durability. MATERIALS AND METHODS: Extracted human third molars were used to provide mid-coronal dentin, which was treated with 20% Salvadora persica extract for 1 min after acid-etching. Microtensile bond strength and interfacial nanoleakage were evaluated after 24 h and 6 months. A three-point flexure test was used to measure the stiffness of completely demineralized dentin sticks before and after treatment with Salvadora persica extract. The hydroxyproline release test was also used to measure collagen degradation by endogenous dentin proteases. Statistical analysis was performed using two-way ANOVA followed by post hoc Bonferroni test and unpaired t-test. P-values < 0.05 were considered statistically significant. RESULTS: The use of Salvadora persica as an additional primer with etch-and-rinse adhesive did not affect the immediate bond strengths and nanoleakage (p > 0.05). After 6 months, the bond strength of the control group decreased (p = 0.007), and nanoleakage increased (p = 0.006), while Salvadora persica group showed no significant difference in bond strength and nanoleakage compared to their 24 h groups (p > 0.05). Salvadora persica increased dentin stiffness and decreased collagen degradation (p < 0.001) compared to their controls. CONCLUSION: Salvadora persica extract pretreatment of acid-etched dentin preserved resin-dentin bonded interface for 6 months. CLINICAL SIGNIFICANCE: Durability of resin-dentin bonded interfaces is still highly questionable. Endogenous dentinal matrix metalloproteinases play an important role in degradation of dentinal collagen within such interfaces. Salvadora persica may preserve resin-dentin interfaces for longer periods of time contributing to greater clinical success and longevity of resin composite restorations.
Assuntos
Condicionamento Ácido do Dente , Colagem Dentária , Infiltração Dentária , Dentina , Extratos Vegetais , Salvadoraceae , Resistência à Tração , Humanos , Dentina/efeitos dos fármacos , Extratos Vegetais/farmacologia , Colagem Dentária/métodos , Colágeno , Adesivos Dentinários/química , Teste de Materiais , Hidroxiprolina , Análise do Estresse Dentário , Resinas Compostas/química , Fatores de Tempo , Cimentos de Resina/químicaRESUMO
OBJECTIVES: The aim of the current study was to evaluate the effect of 2% CHX and 2% CHX-methacrylate compared to the resin-dentin bonds created by a two-step etch-and-rinse adhesive system after 24h, 6min and 12min. METHODS: Microtensile bond strengths and interfacial nanoleakage within resin-dentin interfaces created by Adper Single Bond 2, with or without CHX or CHX-methacrylate pre-treatment for 30s on acid-etched dentin surfaces, were evaluated after 24h, 6min and 12min of storage in distilled water at 37°C. RESULTS: Twelve months of storage resulted in a significant decrease in microtensile bond strength in the control group, and significant increases in silver nanoleakage. In contrast, Single Bond 2+CHX, and to a greater extent CHX-methacrylate, significantly reduced the rate of deterioration of resin-dentin interfaces over the 12min water storage period, in terms of bond strength. CONCLUSIONS: Similar to Single Bond 2+CHX, Single Bond+CHX-methacrylates reduced the degradation of resin-bonded interfaces over a 12 month storage period. Thus it can be concluded that Single Bond 2+CHX-methacrylate may be important to improve durability of bonded interfaces and therefore, prolong the life span of adhesive restorations. CLINICAL SIGNIFICANCE: Although CHX primers have been shown to enhance the durability of etch-and-rinse adhesives, that protection is lost after 2h. The use of CHX-methacrylate should last much longer since it may copolymerize with adhesive monomers, unlike CHX.