RESUMO
This study demonstrates the preparation of SiO2/ZnO core-shell nanoparticles with controllable shell size and their optical properties. A facile ultrasonication method was utilized to prepare the core-shell particles in the absence of surfactant materials. The synthesis duration was 75% shorter than that required for the common sol-gel method, which favours its potential applicability in the future for mass production. Tetraethyl orthosilicate (TEOS) was used as the silica source, while the core material was prepared using zinc acetate dihydrate. The outer shell size could easily be controlled by changing the molar ratio of silica from 0.25 to 1.00. The experimental results show that increasing the silica ratio was effective in suppressing the self-agglomeration of ZnO and, further, in obtaining agglomeration-free particles. The investigation of the photoluminescence (PL) properties of nanometre-sized ZnO revealed several emission peaks in the ultraviolet (UV) wavelength range, indicating variations in bandgap energy. This did not appear in the spectrum of micrometre-sized ZnO particles. The core-shell particles produced with higher amounts of silica showed higher UV-A and UV-B absorption. In addition, the presence of silica reduced the photocatalytic activity of ZnO by 65% and reduced the PL intensity. The obtained emission peaks, intensity changes, and spectral characteristics open new avenues for further research on tailoring the properties of SiO2/ZnO core-shell structures for specific technological advancements. These advancements hold promising applications in UV attenuation materials, LED technologies, lenses, and solar cells within the realm of optical devices.
RESUMO
Background: Breast cancer is one of the main causes of death in women. Uncaria gambir is an Indonesian herbal plant that can be used as an anti-cancer. However, herbal medicines have low bioavailability, which affects their bioactivity. Nanoencapsulation can increase bioavailability and stability of bioactive compounds in herbal medicines. Purpose: This recent finding tried to unravel anti-cancer and chemopreventive of U. gambir nano-encapsulated by Na-alginate. Study Design: U. gambir bioactive compounds were isolated and characterized using UV-Vis spectrometer, FTIR, NMR and HR-MS. U. gambir extract was nanoencapsulated using Na-alginate. Anti-cancer effect was assessed by MTT assay towards T47D cell. Meanwhile, a chemopreventive analysis was carried out in breast cancer mice-induced benzo[α]pyrene. The healthy mice were divided into 8 groups comprising control and treatment. Results: Elucidation of U. gambir ethyl acetate extract confirmed high catechin content, 89.34% (w/w). Successful nanoencapsulation of U. gambir (G-NPs) was indicated. The particle size of G-NPs was 78.40 ± 12.25 nm. Loading efficiency (LE) and loading amount (LA) of G-NPs were 97.56 ± 0.04% and 32.52 ± 0.01%, respectively. G-NPs had an EC50 value of 10.39 ± 3.50 µg/mL, which was more toxic than the EC50 value of extract towards the T47D cell line. Administration of 200 mg/kg BW G-NPs to mice induced by benzo[α]pyrene exhibited SOD and GSH levels of 13.69 ng/mL and 455.6 ng/mL. In addition, the lowest TNF-α level was 27.96 ng/mL. A dose of 100 mg/kg BW G-NPs could best increase CAT levels by 7.18 ng/mL. There was no damage or histological abnormalities found in histological analysis of the breast tissue in the group given 200 mg/kg BW G-NPs.
