Interaction between Hexametaphosphate, Other Active Ingredients of Toothpastes, and Erosion-Abrasion in Enamel in vitro.

Sodium hexametaphosphate (HMP) as toothpaste additive is claimed to reduce erosive tooth wear and to stabilize stannous ions. However, little is known about the impact of concentration and its interactions with fluoride (F) or stannous+fluoride ions (F/Sn) on enamel erosion and erosion-abrasion. In a 10 day cyclic in vitro erosion-abrasion model, 320 flat human enamel specimens were divided into ten groups (n = 32 each) and daily subjected to six erosive challenges (0.5% citric acid, 2 min) and two toothpaste suspension applications (2 min, 1:3 F-free toothpaste:mineral-salt solution, 0.23% sodium gluconate). Half of specimens per group were additionally brushed twice/day (200 g, 15 s) during suspension immersion. Nine suspensions contained HMP (0.25%, 1.75%, 3.25%), either on its own or combined with F (373 ppm F-) or F/Sn (800 ppm Sn2+, 373 ppm F-). One suspension contained sodium gluconate only (NegContr). After 10 days, specimens' surfaces were analysed with profilometry, energy dispersive X-ray spectroscopy, and scanning electron microscopy. Tissue loss (µm, mean ± standard deviation) in NegContr was 10.9 ± 2.0 (erosion), 22.2 ± 1.6 (erosion-abrasion). Under erosive conditions, only 0.25% HMP in any combination and 1.75% HMP with F/Sn reduced loss significantly (-28% to -54%); 3.25% HMP without F and F/Sn increased loss significantly (+35%). With additional abrasion, no suspension reduced loss significantly compared to NegContr, instead, in groups without F and F/Sn or with 3.25% HMP loss was increased (+15% to +30%). Conclusively, at higher concentrations, HMP increased erosive tooth wear and seemed to reduce anti-erosive effects of fluoride and stannous ions.

Impact of mucin on the anti-erosive/anti-abrasive efficacy of chitosan and/or F/Sn in enamel in vitro.

The application of stannous ions in combination with fluoride (F/Sn) is one of the central strategies in reducing erosive tooth wear. F/Sn efficacy can be enhanced by adding chitosan, a positively charged biopolymer. For patients with low saliva flow, this efficacy, however, is not sufficient, making further improvement desirable. This could be achieved by combining chitosan with other molecules like mucin, which together might form multilayers. This in-vitro study aimed to investigate the effect of chitosan, mucin, F/Sn and combinations thereof on enamel erosion and erosion-abrasion. Human enamel samples (n = 448, 28 groups) were cyclically eroded or eroded-abraded (10 days; 6 × 2 min erosion and 2 × 15 s/200 g abrasion per day). Samples were treated 2 × 2 min/day with solutions containing either, chitosan (50 or 500 mPas), porcine gastric mucin, F/Sn or combinations thereof after abrasive challenge. Tissue loss was measured profilometrically, interaction between hard tissue and active agents was assessed with energy dispersive spectroscopy and scanning electron microscopy. Chitosan and F/Sn showed the expected effect in reducing tissue loss under erosive and under erosive-abrasive conditions. Neither mucin alone nor the combinations with mucin showed any additional beneficial effect.