Impregnation of Silica Gel with Choline Chloride-MEA as an eco-friendly adsorbent for CO2 capture.

Deep eutectic solvents (DES) are a generation of ionic liquids that benefit from low cost, good stability, and environmental-friendly features. In this research, a porous silica gel was impregnated with a eutectic Choline Chloride-Monoethanolamine solvent (ChCl-MEA) to greatly improve its CO2 capture performance. In the impregnation, the weight percentages of ChCl-MEA were used in the range of 10-60 wt% at a temperature of 25 °C. The effect of ChCl-MEA loading on the structural properties of the DES-modified silica samples was studied by BET, FTIR, and TGA analyses. Investigation of the CO2 adsorption performance at different operational conditions showed that the modified silica gel with 50 wt% ChCl-MEA (Silica-CM50) presents the highest CO2 capture capacity of 89.32 mg/g. In the kinetic modeling, the fractional order model with a correlation coefficient of 0.998 resulted in the best fit with the experimental data. In addition, the isotherm data for Silica-CM50 were well-fitted with the Dual site Langmuir isotherm model with a correlation coefficient of 0.999, representing two distinct sites for the adsorption process. Moreover, the thermodynamic parameters including Enthalpy, Entropy, and Gibbs free energy at 25 °C were obtained to be - 2.770, - 0.005 and - 1.162, respectively. The results showed the exothermic, spontaneous and feasibility of the adsorption process.

Facile synthesis of Persian gum-graphene oxide composite as a novel adsorbent for CO2 capture: characterization and optimization.

Burning fossil fuels releases toxic gases into the environment and has negative effects on it. In this study, Persian gum@Graphene oxide (Pg@GO) was synthesized and used as a novel adsorbent for CO2 capture. The characterization of materials was determined through XRD, FTIR, FE-SEM, and TGA analysis. The operating parameters including temperature, Pressure, and adsorbent weight were studied and optimized by response surface methodology via Box-Behnken design (RSM-BBD). The highest amount of CO2 adsorption capacity was 4.80 mmol/g, achieved at 300 K and 7.8 bar and 0.4 g of adsorbent weight. To identify the behavior and performance of the Pg@GO, various isotherm and kinetic models were used to fit with the highest correlation coefficient (R2) amounts of 0.955 and 0.986, respectively. The results proved that the adsorption of CO2 molecules on the adsorbent surface is heterogeneous. Based on thermodynamic results, as the value of ΔG° is - 8.169 at 300 K, the CO2 adsorption process is exothermic, and spontaneous.