Circular Economy Electrochemistry: Creating Additive Manufacturing Feedstocks for Caffeine Detection from Post-Industrial Coffee Pod Waste.

The recycling of post-industrial waste poly(lactic acid) (PI-PLA) from coffee machine pods into electroanalytical sensors for the detection of caffeine in real tea and coffee samples is reported herein. The PI-PLA is transformed into both nonconductive and conductive filaments to produce full electroanalytical cells, including additively manufactured electrodes (AMEs). The electroanalytical cell was designed utilizing separate prints for the cell body and electrodes to increase the recyclability of the system. The cell body made from nonconductive filament was able to be recycled three times before the feedstock-induced print failure. Three bespoke formulations of conductive filament were produced, with the PI-PLA (61.62 wt %), carbon black (CB, 29.60 wt %), and poly(ethylene succinate) (PES, 8.78 wt %) chosen as the most suitable for use due to its equivalent electrochemical performance, lower material cost, and improved thermal stability compared to the filaments with higher PES loading and ability to be printable. It was shown that this system could detect caffeine with a sensitivity of 0.055 ± 0.001 µA µM-1, a limit of detection of 0.23 µM, a limit of quantification of 0.76 µM, and a relative standard deviation of 3.14% after activation. Interestingly, the nonactivated 8.78% PES electrodes produced significantly better results in this regard than the activated commercial filament toward the detection of caffeine. The activated 8.78% PES electrode was shown to be able to detect the caffeine content in real and spiked Earl Grey tea and Arabica coffee samples with excellent recoveries (96.7-102%). This work reports a paradigm shift in the way AM, electrochemical research, and sustainability can synergize and feed into part of a circular economy, akin to a circular economy electrochemistry.

Adjusting the Connection Length of Additively Manufactured Electrodes Changes the Electrochemical and Electroanalytical Performance.

Changing the connection length of an additively manufactured electrode (AME) has a significant impact on the electrochemical and electroanalytical response of the system. In the literature, many electrochemical platforms have been produced using additive manufacturing with great variations in how the AME itself is described. It is seen that when measuring the near-ideal outer-sphere redox probe hexaamineruthenium (III) chloride (RuHex), decreasing the AME connection length enhances the heterogeneous electrochemical transfer (HET) rate constant (k0) for the system. At slow scan rates, there is a clear change in the peak-to-peak separation (ΔEp) observed in the RuHex voltammograms, with the ΔEp shifting from 118 ± 5 mV to 291 ± 27 mV for the 10 and 100 mm electrodes, respectively. For the electroanalytical determination of dopamine, no significant difference is noticed at low concentrations between 10- and 100-mm connection length AMEs. However, at concentrations of 1 mM dopamine, the peak oxidation is shifted to significantly higher potentials as the AME connection length is increased, with a shift of 150 mV measured. It is recommended that in future work, all AME dimensions, not just the working electrode head size, is reported along with the resistance measured through electrochemical impedance spectroscopy to allow for appropriate comparisons with other reports in the literature. To produce the best additively manufactured electrochemical systems in the future, researchers should endeavor to use the shortest AME connection lengths that are viable for their designs.

Trace manganese detection via differential pulse cathodic stripping voltammetry using disposable electrodes: additively manufactured nanographite electrochemical sensing platforms.

Additive manufacturing is a promising technology for the rapid and economical fabrication of portable electroanalytical devices. In this paper we seek to determine how our bespoke additive manufacturing feedstocks act as the basis of an electrochemical sensing platform towards the sensing of manganese(ii) via differential pulse cathodic stripping voltammetry (DPCSV), despite the electrode comprising only 25 wt% nanographite and 75 wt% plastic (polylactic acid). The Additive Manufactured electrodes (AM-electrodes) are also critically compared to graphite screen-printed macroelectrodes (SPEs) and both are explored in model and real tap-water samples. Using optimized DPCSV conditions at pH 6.0, the analytical outputs using the AM-electrodes are as follows: limit of detection, 1.6 × 10-9 mol L-1 (0.09 µg L-1); analytical sensitivity, 3.4 µA V µmol-1 L; linear range, 9.1 × 10-9 mol L-1 to 2.7 × 10-6 mol L-1 (R2 = 0.998); and RSD 4.9% (N = 10 for 1 µmol L-1). These results are compared to screen-printed macroelectrodes (SPEs) giving comparable results providing confidence that AM-electrodes can provide the basis for useful electrochemical sensing platforms. The proposed electroanalytical method (both AM-electrodes and SPEs) is shown to be successfully applied for the determination of manganese(ii) in tap water samples and in the analysis of a certified material (drinking water). The proposed method is feasible to be applied for in-loco analyses due to the portability of sensing; in addition, the use of AM-printed electrodes is attractive due to their low cost.

Complete Additively Manufactured (3D-Printed) Electrochemical Sensing Platform.

Herein, we report a complete additively manufactured (AM) electrochemical sensing platform. In this approach, a fully AM/3D-printed electrochemical system, using a conventional low-cost 3D printer (fused deposition modeling) fabricating both the conductive electrodes and the nonconductive/chemically inert electrochemical cell is reported. The electrodes (working, counter, and pseudo-reference) are AM using a conductive fused-filament comprised of a mixture of carbon black nanoparticles and polylactic acid (CB/PLA). AM components partially coated with silver ink presented a similar behavior to a conventional Ag/AgCl reference electrode. The performance of the AM working electrode was evaluated after a simple and fast polishing procedure on sandpaper and electrochemical activation in a NaOH solution (0.5 mol L-1). Following the electrochemical activation step, a considerable improvement in the electrochemical behavior (current intensity and voltammetric profile) was obtained for model analytes, such as dopamine, hexaammineruthenium(III) chloride, ferricyanide/ferrocyanide, uric acid, and ascorbic acid. Excellent repeatability (RSD = 0.4%, N = 10) and limit of detection (0.1 µmol L-1) were obtained with the all complete AM electrochemical system for dopamine analysis. The electrochemical performance of the developed system (after simple electrochemical activation of the working electrode) was similar or better than those obtained using commercial glassy carbon and screen-printed carbon electrodes. The results shown here represents a significant advance in AM (3D printing) technology for analytical chemistry.