RESUMO
Cu-doping contents in the TiO2 lattice structure were studied to show the effects on the crystal structure, morphology, and photocatalytic activity of TiO2 nanoparticles and thus composite cellulosic nanofibrous membranes. Pristine and copper-doped TiO2 nanoparticles were synthesized using the sol-gel technique, a wet chemical method with the advantages of low synthesizing temperature, uniform nanosize distribution, and purity. The as-synthesized semiconductor nanoparticles were first tested with the dye removal process and then impregnated onto electrospun cellulose nanofibers (CL nanofibers) to acquire modified nanofibers with self-cleaning properties. The as-prepared composite CL nanofibers consisting of doped and undoped TiO2 nanoparticles were characterized by various techniques, such as field emission scanning electron microscopy, transmission electron microscopy, UV-vis, X-ray diffraction, Fourier transform infrared spectroscopy, and tensile tests. The copper-doped TiO2 molar ratio in the nanocomposite was found to possess a pronounced impact on the dye removal and self-cleaning effects under the visible light spectrum, whereas TiO2 is highly effective under specific UV-light irradiation. Optical measurements and dye decomposition showed that the Cu-doped TiO2 nanocomposite was optimized at a 1% molar ratio by the copper-doping concentration regarding dye removal and self-cleaning applications under the visible light range.
RESUMO
A series of MnO2-Co3O4-CeO2 catalysts with different ceria loading (0.75, 1.26 and 1.88 Ce/Mn molar ratio) were synthesized by a co-precipitation technique and the catalytic activity was tested for selective catalytic reduction of NOx by C3H6 or NH3. The catalysts were characterized by various physicochemical techniques to examine the effect of ceria loading on the properties of catalysts, such as crystallinity of metal species, surface area, porosity, and acidity using physical adsorption analysis, SEM-EDX, H2-TPR, XRD, NH3-TPD and in-situ FTIR spectroscopy. Ceria loading had a significant effect on the reduction of NOx, with the catalyst having low amount of ceria loading (Ce/Mn = 0.75) showing excellent performance at low-temperature conditions, but the activity declined at higher temperature. The high ceria loading (Ce/Mn = 1.88) catalyst showed poor activity compared to the counterparts owing to the lower number of acid sites and the resulting lower adsorption capacity.
RESUMO
This paper compares different coating methods (in situ solid combustion, hybrid deposition, secondary growth on seed, suspension, double deposition of wet impregnation and suspension) to deposit Ce0.2Zr0.8O2 mixed oxides on cordierite substrates, for use as a three way catalyst. Among them, the double deposition was proven to be the most efficient one. The coated sample shows a BET (Brunauer-Emmett-Teller) surface area of 25 m²/g, combined with a dense and crack free surface. The catalyst with a layer of MnO2-NiO-Co3O4 mixed oxides on top of the Ce0.2Zr0.8O2/cordierite substrate prepared by this method exhibits good activity for the treatment of CO, NO and C3H6 in exhaust gases (CO conversion of 100% at 250 °C, C3H6 conversion of 100% at 400 °C and NO conversion of 40% at 400 °C).