Unveiling the Stacking Fault-Driven Phase Transition Delaying Cryogenic Fracture in Fe-Co-Cr-Ni-Mo-C-Based Medium-Entropy Alloy.

In this work, the tensile deformation mechanisms of the Fe55Co17.5Cr12.5Ni10Mo5-xCx-based medium-entropy alloy at room temperature (R.T.), 77 K, and 4.2 K are studied. The formation of micro-defects and martensitic transformation to delay the cryogenic fracture are observed. The results show that FeCoCrNiMo5-xCx-based alloys exhibit outstanding mechanical properties under cryogenic conditions. Under an R.T. condition, the primary contributing mechanism of strain hardening is twinning-induced plasticity (TWIP), whereas at 77 K and 4.2 K, the activation of martensitic transformation-induced plasticity (TRIP) becomes the main strengthening mechanism during cryogenic tensile deformation. Additionally, the carbide precipitation along with increased dislocation density can significantly improve yield and tensile strength. Furthermore, the marked reduction in stacking fault energy (SFE) at cryogenic temperatures can promote mechanisms such as twinning and martensitic transformations, which are pivotal for enhancing ductility under extreme conditions. The Mo4C1 alloy obtains the optimal strength-ductility combination at cryogenic-to-room temperatures. The tensile strength and elongation of the Mo4C1 alloy are 776 MPa and 50.5% at R.T., 1418 MPa and 71.2% in liquid nitrogen 77 K, 1670 MPa and 80.0% in liquid helium 4.2 K, respectively.

Effect of Aging Treatment on the Microstructure and Properties of 2.2 GPa Tungsten-Containing Maraging Steel.

Maraging steel is a prominent category of ultrahigh-strength steel (UHSS) characterized by excellent comprehensive properties, and it finds wide applications in manufacturing load-bearing structural components. In this study, a novel tungsten-containing maraging steel, C-250W, was designed. The effects of aging treatments on the mechanical properties, microstructure, precipitations, and reverted austenite of C-250W steel were investigated. The results revealed that the optimal combination of strength and toughness could be achieved through an aging treatment of C-250W steel carried out for 5 h at 480 °C after solution treatment at 1000 °C for 1 h. As the aging temperature increased, the proportion of dimples in the impact fracture gradually decreased while that of quasi-cleavage increased, leading to a reduction in Charpy impact energy. The boundary of martensitic lath decomposed gradually as the aging temperature increased, and it disappeared entirely at temperatures higher than 550 °C. Moreover, the aging process resulted in the formation of phases, including spherical Fe2M (M represents Mo, W) and thin strip-shaped Ni3N (N represents Mo, Ti) precipitates. These precipitates coarsened from 5 nm to 50-200 nm with increasing aging temperature. Additionally, the content of reverted austenite increased with the aging temperature. Within the temperature range of 400 °C to 500 °C for aging treatment, the content of film-shaped reverted austenite was approximately 3%, primarily distributed at the boundary of martensite lath. When the aging temperature exceeded 550 °C, the content of reverted austenite reached 20.2%, and its morphology changed from film-shaped to block-shaped, resulting in a decline in strength and toughness.

Effect of Cerium on Inclusion Modification in a Secondary-Hardening Steel.

Owing to the continuous increasing of steel strength, mechanical properties including toughness and fatigue performance are becoming increasingly sensitive to inclusions in ultra-high strength steel. Rare-earth treatment is considered as an effective method to reduce the harmful effects of inclusions, but is rarely applied in secondary-hardening steel. In the present study, different amounts of cerium were added in a secondary-hardening steel to investigate the modification effect of Ce on non-metallic inclusions in steel. The characteristics of inclusions were observed experimentally using SEM-EDS and the modification mechanism was analyzed based on thermodynamic calculations. The results indicated that the main inclusions in Ce-free steel are Mg-Al-O + MgS. Thermodynamic calculation indicated that MgAl2O4 is firstly formed in liquid steel and then successively transformed into MgO and MgS during cooling process. When the Ce content is 0.0030%, the typical inclusions in steel were individual Ce2O2S and MgO + Ce2O2S complex inclusions. When the Ce content was increased to 0.0071%, the typical inclusions in steel were individual Ce2O2S- and Mg-containing inclusions. Ce treatment modifies the angular magnesium aluminum spinel inclusions into spherical and ellipsoidal Ce-containing inclusions, thus reducing the harmful effect of inclusion on steel properties.

Design, synthesis and mechanism study of novel natural-derived isoquinoline derivatives as antifungal agents.

In screening for natural fungicidal leads, two series of novel 3-aryl-isoquinoline derivatives 8 and 9 were designed and synthesized based on sanguinarine, chelerythrine and berberine. Their structures were confirmed by 1D, 2D NMR and HRMS. Most of the title compounds showed medium to excellent antifungal activity in vitro at 50 mg/L, which were much more active than the lead of sanguinarine. Especially, 9f possessed the best effective against Alternaria solani (80.4%), Alternaria alternata (88.2%) and Physalospora piricola (93.8%). Furthermore, the EC50 of 9f (3.651 mg/L) against P. piricola was marginally better than chlorothalonil (3.869 mg/L). In vivo antifungal activity of 9f against P. piricola was studied on apples. The curative and protection results at the dosage of 50 and 100 mg/L showed as 70.45 ~ 81.67% and 64.96 ~ 80.34%, respectively, which were equal to that of chlorothalonil (80.30 ~ 86.67%, 73.08 ~ 76.92%). Molecular electrostatic potential and molecular docking analysis revealed that 9f was fully covered by positive potential contour, which was easier to interact with the negative amino acid resides of succinate dehydrogenase than 8f. 9f could be used as a novel antifungal lead compound for further study. Two series of novel isoquinoline derivatives 8, 9 containing 3-aryl were rational designed and synthesized based on quaternary isoquinoline alkaloids. The bioassay and interaction mechanism studies indicated that 9f should be considered as potential antifungal lead.

[Familial male-limited precocious puberty due to Asp578His mutations in the LHCGR gene: clinical characteristics and gene analysis in an infant].

The aim of the study was to provide a descriptive analysis of familial male-limited precocious puberty (FMPP), which is a rare inherited disease caused by heterozygous constitutively activating mutations of the luteinizing hormone/choriogonadotropin receptor gene (LHCGR). The patient was a ten-month-old boy, presenting with penile enlargement, pubic hair formation, and spontaneous erections. Based on the clinical manifestations and laboratory data, including sexual characteristics, serum testosterone levels, GnRH stimulation test, and bone age, this boy was diagnosed with peripheral precocious puberty. Subsequently the precocious puberty-related genes were analyzed by direct DNA sequencing of amplified PCR products from the patient and his parents. Genetic analysis revealed a novel heterozygous missense mutation c.1732G>C (Asp578His) of the LHCGR gene exon11 in the patient, which had never been reported. His parents had no mutations. After combined treatment with aromatase inhibitor letrozole and anti-androgen spironolactone for six months, the patient's symptoms were controlled. The findings in this study expand the mutation spectrum of the LHCGR gene, and provide molecular evidence for the etiologic diagnosis as well as for the genetic counseling and prenatal diagnosis in the family.

[Analyzing crude/processed root of Polygonum multiflorum from different habitats by UPLC fingerprint and mode identification methods].

To establish a content determination method for 2,3,5,4'-tetrahydroxy stilbene-2-O-ß-D-glucoside (TSG) of the crude/processed root of Polygonum multiflorum from different habitats in China and set up the fingerprint by using UPLC. Various samples were pretreated by macro-porous resin. Then UPLC analysis was performed on Waters ACQUITY UPLC@BEH C18 chromatographic column (2.1 mm×50 mm, 1.7 µm) at (25±5) ℃. A binary gradient elution system was composed of acetonitrile (phase A) and 0.5% acetic acid solution (phase B). Detection was performed at the wavelength of 254 nm, and the mobile flow rate was set at 0.3 mL•min⁻¹. Results showed that the yield of extraction of the 2,3,5,4'-tetrahydroxy stilbene-2-O-ß-D-glucoside from root of P. multiflorum was all over 25.0% after macro-porous resin separation; an exclusive UPLC fingerprint method of the crude/processed root of P. multiflorum from different habitats was successfully set up and 17 chromatographic peaks were calibrated. Cluster analysis can not entirely distinguish the crude one from the processed one, while principal component analysis absolutely can. 2,3,5,4'-tetrahydroxy stilbene-2-O-ß-D-glucoside is the composition that has largest differences in variable importance in projection (VIP) between crude and processed root of P. multiflorum. The separating method can gain high-purity 2,3,5,4'-tetrahydroxy stilbene-2-O-ß-D-glucoside, and the determination method is simple, sensitive, reliable and can be used in fast identifying the crude/processed root of P. multiflorum or as a method for overall quality control of root of P. multiflorum.