RESUMO
Poly(glycolic acid) (PGA) is a biodegradable polymer with high gas barrier properties, mechanical strength, and heat deflection temperature. However, PGA's brittleness severely limits its application in packaging, creating a need to develop PGA-based copolymers with improved elasticity that maintain its barrier properties and hydrolytic degradability. In this work, a series of PGBAT (poly(glycolic acid-co-butylene) adipate-co-butylene terephthalate) copolymers containing 21-92% glycolic acid (nGA) with Mw values of 46,700-50,600 g mol-1 were synthesized via melt polycondensation, and the effects of altering the nGA on PGBAT's thermomechanical properties and hydrolysis rate were investigated. Poly(glycolic acid-co-butylene succinate) (PGBS) and poly(glycolic acid-co-butylene terephthalate) (PGBT) copolymers with high nGA were synthesized for comparison. DSC analysis revealed that PGBAT21 (nGA = 21%) and PGBAT92 were semicrystalline, melting between 102.8 and 163.3 °C, while PGBAT44, PGBAT86-89, PGBT80, and PGBS90 were amorphous, with Tg values from -19.0 to 23.7 °C. These high nGA copolymers showed similar rates of hydrolysis to PGA, whereas those containing <50% GA showed almost no mass loss over the testing period. Their mechanical properties were highly dependent upon their crystallinity and improved significantly after annealing. Of the high nGA copolymers, annealed PGBS90 (Mw 97,000 g mol-1) possessed excellent mechanical properties with a modulus of 588 MPa, tensile strength of 30.0 MPa, and elongation at break of 171%, a significant improvement on PGA's elongation at break of 3%. This work demonstrates the potential of enhancing PGA's flexibility by introducing minor amounts of low-cost diols and diacids into its synthesis.
RESUMO
The rise in demand for biodegradable plastic packaging with high barrier properties has spurred interest in poly(lactic acid-co-glycolic acid) (PLGA) copolymers with a relatively high glycolide content. In this work, we examined how reaction conditions affect the synthesis of PLGA25 (L:G 25:75) through the ring-opening polymerisation of d-l-lactide (L) and glycolide (G), using tin 2-ethylhexanoate (Sn(Oct)2) as the catalyst and 1-dodecanol as the initiator. The effects of varying the initiator concentration, catalyst concentration, reaction time, and temperature on the molecular weight, monomer conversion, and thermal properties of PLGA25 were investigated. Increasing the reaction temperature from 130 to 205 °C significantly reduced the time required for high monomer conversions but caused greater polymer discolouration. Whilst increasing the [M]:[C] from 6500:1 to 50,000:1 reduced polymer discolouration, it also resulted in longer reaction times and higher reaction temperatures being required to achieve high conversions. High Mn and Mw values of 136,000 and 399,000 g mol-1 were achieved when polymerisations were performed in the solid state at 150 °C using low initiator concentrations. These copolymers were analysed using high temperature SEC at 80 °C, employing DMSO instead of HFIP as the eluent.
RESUMO
Furandioate-adipate copolyesters are an emerging class of bio-based biodegradable polymers with great potential to replace fossil-derived terephthalic acid-based copolyesters such as poly(butylene adipate-co-terephthalate) (PBAT). Furandioate-adipate polyesters have almost exclusively been prepared with conventional primary (1°) alcohol diols, while secondary (2°) alcohol diol monomers have largely been overlooked until now, despite preliminary observations that using methyl-branched diols increases the T g of the resultant polyesters. Little is known of what impact the use of 2° alcohol diols has on other properties such as material strength, hydrophobicity, and rate of enzymatic hydrolysis-all key parameters for performance and end-of-life. To ascertain the effects of using 2° diols on the properties of furandioate-adipate copolyesters, a series of polymers from diethyl adipate (DEA) and 2,5-furandicarboxylic acid diethyl ester (FDEE) using different 1° and 2° alcohol diols was prepared. Longer transesterification times and greater excesses of diol (diol/diester molar ratio of 2:1) were found to be necessary to achieve M ws > 20 kDa using 2° alcohol diols. All copolyesters from 2° diols were entirely amorphous and exhibited higher T gs than their linear equivalents from 1° diols. Compared to linear poly(1,4-butyleneadipate-co-1,4-butylenefurandioate), methyl-branched, poly(2,5-hexamethyleneadipate-co-2,5-hexamethylenefurandioate) (0:7:0.3 furandioate/adipate ratio) displayed both higher modulus (67.8 vs 19.1 MPa) and higher extension at break (89.7 vs 44.5 mm). All other methyl-branched copolyesters displayed lower modulus but retained higher extension at break compared with their linear analogues. Enzymatic hydrolysis studies using Humicola insolens cutinase revealed that copolyesters from 2° alcohol diols have significantly decreased rates of biodegradation than their linear equivalents synthesized using 1° alcohol diols, allowing for fine-tuning of polymer stability. Hydrophobicity, as revealed by water contact angles, was also found to generally increase through the introduction of methyl branching, demonstrating potential for these materials in coatings applications.