Effect of K+ and Ca2+ Cations on Structural Manganese(IV) Oxide for the Aerobic Oxidation of 5-Hydroxymethylfurfural to 2,5-Furandicarboxylic Acid.

The promising influences of K+ and Ca2+ ions in the development of effective MnO2 for the selective oxidation of 5-hydroxymethylfurfural to 2,5-furandicarboxylic acid (FDCA) were studied for the catalytic performance under a high-pressure reaction of aqueous O2 (0.5 MPa) in a basic system. Various oxidation states of manganese in MnO2 were able to accelerate the oxidation of 5-formyl-2-furancarboxylic acid to FDCA in the rate-determining step. The results were in good agreement that Ca2+ played a key role in the highest FDCA yield up to 85% due to the associated cations on the local coordination to enhance the high surface area and the electronic effect on the manganese ion. Both K-MnO2 and Ca-MnO2 catalysts showed excellent catalytic activities without a significant change in the efficiency in the reusability experiments.

One-pot synthesis of iron oxide - Gamma irradiated chitosan modified SBA-15 mesoporous silica for effective methylene blue dye removal.

The development of adsorption technology and the processing of radiation have both been influenced by chitosan adsorbent (γ-chitosan), a raw material with unique features. The goal of the current work was to improve the synthesis of Fe-SBA-15 utilizing chitosan that has undergone gamma radiation (Fe-γ-CS-SBA-15) in order to investigate the removal of methylene blue dye in a single hydrothermal procedure. High-resolution transmission electron microscopy (HRTEM), High angle annular dark field scanning transmission electron microscopy (HAADF-STEM), small- and wide-angle X-ray powder diffraction (XRD), Fourier transform-infrared spectroscopy (FT-IR) and Energydispersive X-ray spectroscopy (EDS) were used to characterize γ-CS-SBA-15 that had been exposed to Fe. By using N2-physisorption (BET, BJH), the structure of Fe-γ-CS-SBA-15 was investigated. The study parameters also included the effect of solution pH, adsorbent dose and contact time on the methylene blue adsorption. The elimination efficiency of the methylene blue dye was compiled using a UV-VIS spectrophotometer. The results of the characterization show that the Fe-γ-CS-SBA-15 has a substantial pore volume of 504 m2 g-1 and a surface area of 0.88 cm3 g-1. Furthermore, the maximum adsorption capacity (Qmax) of the methylene blue is 176.70 mg/g. The γ-CS can make SBA-15 operate better. It proves that the distribution of Fe and chitosan (the C and N components) in SBA-15 channels is uniform.

Hydrogel-Templated Solid Base Catalysts for Transesterification of Soybean Oil.

A new method for utilization of hydrogel is proposed here for the preparation of solid base catalysts for the transesterification of vegetable oil. When a solution of KF is mixed with a solution of Ca(NO3)2, CaF2 is obtained and inactive as a catalyst in the transesterification of vegetable oils. The catalysts were synthesized by the sequential incorporation of KF and/or Ca(NO3)2 solutions into the hydrogel upon microwave irradiation and then the as-obtained hydrogel was calcined at 800°C for 5 hours to eliminate the template and yield catalysts for the biodiesel productions. The prepared catalysts obtained by the different ways in the incorporation of ions into the hydrogel showed different physical properties and catalytic activities in the transesterification of soybean oil. All catalysts, except the low concentration of Ca(NO3)2, exhibiting the high activity yielding more than 90% FAME after 1 hour at 65°C, using oil to methanol molar ratio of 1:15 and 10 wt% of catalyst amounts.