Determination of the Color Change of Various Esthetic Monolithic Monochromatic Computer-Aided Design/Computer-Aided Manufacturing Materials.

Dental technology has developed materials for prosthetics that are very similar to natural teeth and offer a good balance between durability and esthetics; however, some of these materials are not very color-stable under the influence of external factors. Therefore, the aim of this study is to determine and compare the color change (∆E00) of different esthetic monolithic monochromatic CAD/CAM materials after they have been thermocycled and treated with staining solutions. The color parameters were determined using a spectrophotometer on a white and black background. Five CAD/CAM materials were used for this study-CAD/CAM nanoceramic (GC Cerasmart270), CAD/CAM lithium disilicate ceramic (IPS e.max CAD), CAD/CAM polymer (Telio CAD), CAD/CAM composite (Tetric CAD) and CAD/CAM polymer-infiltrated ceramic (Vita Enamic). The test specimens produced were divided into groups and were thermocycled in distilled water. They were then stored for four weeks at 37 °C in either distilled water as a control liquid, black tea, instant coffee or red wine. The aim is also to evaluate the color changes as a function of the exposure time of the staining solutions. The results obtained were analyzed statistically. All CAD/CAM materials tend to discolor to varying degrees. Among the factors contributing to discoloration, red wine proved to be the most significant influencing factor. The conclusion from the results is that the color change is influenced by the type of material, the staining solution, the sample thickness, the color background and the aging time.

Microscopic and Mechanical Characterization of Co-Cr Dental Alloys Joined by the TIG Welding Process.

Due to their good mechanical and other properties, cobalt-chromium alloys (Co-Cr) are often used in prosthetic therapy. The metal structures of prosthetic works can be damaged and break, and depending on the extent of the damage, they can be re-joined. Tungsten inert gas welding (TIG) produces a high-quality weld with a composition very close to that of the base material. Therefore, in this work, six commercially available Co-Cr dental alloys were joined by TIG welding, and their mechanical properties were evaluated to determine the quality of the TIG process as a technology for joining metallic dental materials and the suitability of the Co-Cr alloys used for TIG welding. Microscopic observations were made for this purpose. Microhardness was measured using the Vickers method. The flexural strength was determined on a mechanical testing machine. The dynamic tests were carried out on a universal testing machine. The mechanical properties were determined for welded and non-welded specimens, and the results were statistically evaluated. The results show the correlation between the investigated mechanical properties and the process TIG. Indeed, characteristics of the welds have an effect on the measured properties. Considering all the results obtained, the TIG-welded I-BOND NF and Wisil M alloys showed the cleanest and most uniform weld and, accordingly, satisfactory mechanical properties, highlighting that they withstood the maximum number of cycles under dynamic load.

Metal Ions Release from Welded Co-Cr Dental Alloys.

Cobalt-chromium alloys (Co-Cr) are widely used in dentistry due to their excellent mechanical properties and corrosion resistance. Since prosthetic materials must be permanently stable in the oral cavity, it is very important to determine the release of ions from alloys in the oral cavity. In dentistry today, metals and alloys are mainly joined by laser and tungsten inert gas (TIG) welding. Therefore, in this work, the release of metal ions from six different Co-Cr alloys joined by these two welding methods was quantified to determine the effects of the welding method on an ion release. Static immersion tests, atomic absorption spectrometry and statistical analysis were performed for this purpose. The results showed that laser-welded alloys release a lower amount of metal ions compared to TIG-welded alloys.

Roughness of the Surface of Zirconia Reinforced Lithium Disilicate Ceramic Treated by Different Procedures.

Lithium disilicate and zirconia are the two most popular materials for aesthetic and dental prosthetic work; however, due to their limitations, a new material is being researched, namely zirconia-reinforced lithium disilicate, the surface of which is treated with different procedures to achieve the best possible surface properties. In this study, the surface of zirconia-reinforced lithium disilicate glass-ceramic was treated using different methods (conventional and laser) to determine the effects of the treatment procedures on the surface properties and surface roughness to achieve a higher strength of adhesion from the self-adhesive resin cement to zirconia-reinforced lithium disilicate. The treated surfaces were investigated using profilometry, X-ray diffraction and energy dispersive X-ray fluorescence. The results obtained were statistically evaluated. The results show that the surface roughness is highest for the samples treated with Er:YAG (erbium-doped yttrium aluminium garnet laser) and silanisation. Furthermore, the surface treatment procedures applied did not change the composition of the surface.