Biocorrosion and Cytotoxicity Studies on Biodegradable Mg-Based Multicomponent Alloys.

Magnesium-based multicomponent alloys with different compositions, namely Mg60Al20Zn5Cu10Mn5 (Mg60 alloy), Mg70Al15Zn5Cu5Mn5 (Mg70 alloy), and Mg80Al5Cu5Mn5Zn5 (Mg 80) alloys, were prepared using the disintegrated melt deposition technique. The DMD technique is a distinctive method that merges the benefits from gravity die casting and spray forming. This approach facilitates high solidification rates, process yields, and reduced metal wastage, resulting in materials with a fine microstructure and minimal porosity. Their potential as biodegradable materials was assessed through corrosion in different simulated body fluids (SBFs), microstructure, and cytotoxicity tests. It was observed that the Mg60 alloy exhibited low corrosion rates (~× 10-5 mm/year) in all SBF solutions, with a minor amount of corrosive products, and cracks were observed. This can be attributed to the formation of the Mg32(AlZn)49 phase and to its stability due to Mg(OH)2 film, leading to excellent corrosion resistance when compared to the Mg70 and M80 alloys. Conversely, the Mg80 alloy exhibited high corrosion rates, along with more surface degradation and cracks, due to active intermetallic phases, such as Al6Mn, Al2CuMg, and Al2Cu phases. The order of corrosion resistance for the Mg alloy was found to be ASS > HBSS > ABP > PBS. Further, in vitro cytotoxicity studies were carried out using MDA-MB-231 tumor cells. By comparing all three alloys, in terms of proliferation and vitality, the Mg80 alloy emerged as a promising material for implants, with potential antitumor activity.

Development of Novel Lightweight Metastable Metal-(Metal + Ceramic) Composites Using a New Powder Metallurgy Approach.

In the current study, metal-(metal + ceramic) composites composed of biocompatible elements, magnesium (Mg), zinc (Zn), calcium (Ca) and manganese (Mn) were synthesized using a sinter-less powder metallurgy method. The composite has a composition of Mg49Zn49Ca1Mn1 (wt.%) in which the compositional ratio between Mg and Zn was chosen to be near eutectic Mg-Zn composition. The synthesis method was designed to avoid/minimize intermetallic formation by using processing temperatures lower than the Mg-Zn binary eutectic temperature (~ 340 °C). The synthesis process involved extrusion of green compacts at two different temperatures, 150 °C and 200 °C, without sintering. Extrusion was performed directly on the green compacts as well as on the compacts soaked at temperatures of 150 °C and 200 °C, respectively. Microstructure and mechanical properties of the materials synthesized under various processing conditions were investigated. Effect of extrusion temperature as well as soaking temperature on the materials' properties were also evaluated in details and different properties showed an optimum under different conditions. All the synthesized materials showed no evidence of intermetallic formation which was confirmed by SEM/EDS, XRD, and Differential Scanning Calorimetry (DSC) techniques. The study establishes development of unconventional metal-(metal + ceramic) eco-friendly composites and provides important insight into realizing certain properties without using sintering step thus to minimize the energy consumption of the process. The study also highlights the use of magnesium turnings (recyclability) to develop advanced materials.

Tensile and Compressive Responses of Ceramic and Metallic Nanoparticle Reinforced Mg Composites.

In the present study, room temperature mechanical properties of pure magnesium, Mg/ZrO2 and Mg/(ZrO2 + Cu) composites with various compositions are investigated. Results revealed that the use of hybrid (ZrO2 + Cu) reinforcements in Mg led to enhanced mechanical properties when compared to that of single reinforcement (ZrO2). Marginal reduction in mechanical properties of Mg/ZrO2 composites were observed mainly due to clustering of ZrO2 particles in Mg matrix and lack of matrix grain refinement. Addition of hybrid reinforcements led to grain size reduction and uniform distribution of hybrid reinforcements, globally and locally, in the hybrid composites. Macro- and micro- hardness, tensile strengths and compressive strengths were all significantly increased in the hybrid composites. With respect to unreinforced magnesium, failure strain was almost unchanged under tensile loading while it was reduced under compressive loading for both Mg/ZrO2 and Mg/(ZrO2 + Cu) composites.

Synthesis and Characterization of Nano Boron Nitride Reinforced Magnesium Composites Produced by the Microwave Sintering Method.

In this study, magnesium composites with nano-size boron nitride (BN) particulates of varying contents were synthesized using the powder metallurgy (PM) technique incorporating microwave-assisted two-directional sintering followed by hot extrusion. The effect of nano-BN addition on the microstructural and the mechanical behavior of the developed Mg/BN composites were studied in comparison with pure Mg using the structure-property correlation. Microstructural characterization revealed uniform distribution of nano-BN particulates and marginal grain refinement. The coefficient of thermal expansion (CTE) value of the magnesium matrix was improved with the addition of nano-sized BN particulates. The results of XRD studies indicate basal texture weakening with an increase in nano-BN addition. The composites showed improved mechanical properties measured under micro-indentation, tension and compression loading. While the tensile yield strength improvement was marginal, a significant increase in compressive yield strength was observed. This resulted in the reduction of tension-compression yield asymmetry and can be attributed to the weakening of the strong basal texture.