High adsorption capacities for dyes by a pH-responsive sodium alginate/sodium lignosulfonate/carboxylated chitosan/polyethyleneimine adsorbent.

Dyes are indispensable for the rapid development of society, but untreated dye wastewater can threaten human health. In this study, an adsorbent (SA/SL/CCS/PEI@MNPs) was synthesized by one-pot method using magnetic nanoparticles (MNPs), sodium alginate (SA), sodium lignosulfonate (SL), carboxylated chitosan (CCS) and polyethyleneimine (PEI). The adsorbent was mesoporous micrometer-sized particles with pore size of 34.92 nm, which was favorable for dynamic column experiments. SA/SL/CCS/PEI@MNPs possessed pH-responsive performance. Under acidic condition, the maximum adsorption capacities for anionic dyes (tartrazine, reactive black-5, indigo carmine) reached >550 mg/g. Under alkaline condition, those for cationic dyes (methylene blue, methyl violet, neutral red) exceeded 1900 mg/g. The function of the various modifiers was investigated. The results indicated that the incorporation of SL, CCS and PEI was able to provide plenty of sulfonate, carboxylate and amino/imine reactive groups so that adsorption capacities of dyes were improved. The adsorption mechanism was explored by FTIR and XPS. At the same time, the adsorption mechanism was more deeply analyzed using molecular dynamics simulations and radial distribution function. It was demonstrated that the dyes adsorption on the SA/SL/CCS/PEI@MNPs was mainly due to electrostatic attraction and π-π interaction. In addition, the adsorbent had good reusability, and the removal still reached over 90 % after five cycles. In conclusion, the adsorbent displayed a broad prospect for the adsorption of organic dyes.

Selective adsorption of anionic dyes by a macropore magnetic lignin-chitosan adsorbent.

Dyes pollution is well known for their hazardous impacts on human health and the environment. The removal of dyes from wastewater has become an important issue. In this study, magnetic micrometer-sized particles AL-CTS@MNPs were synthesized from alkaline lignin (AL) and chitosan (CTS) by "one-pot method". The adsorbent presented higher selectivity adsorption effect on anionic dyes than amphoteric and cationic dyes, and even no adsorption effect on cationic methylene blue (MB), which showed that the anionic dyes could be better separated from the other two types of dyes. The adsorption isotherms of the dyes were highly consistent with the Langmuir model, and the maximum adsorption capacity was 329.50 mg/g for methyl orange (MO) and 20.00 mg/g for rhodamine B (RhB). AL-CTS@MNPs showed good adsorption of anionic dyes (MO) in the pH range of 3-9. Meanwhile, the adsorbent AL-CTS@MNPs were also characterized, showing rough surface with specific surface areas of 37.38 m2/g, pore diameter of 95.8 nm and porosity of 17.62 %. The particle sizes were ranged from 800 µm to 1300 µm. The electrostatic attraction and π-π* electron donor-acceptor interactions were the main forces between the adsorbent and anionic dyes. While the electrostatic repulsive force between the adsorbent and the cationic dyes resulted in the non-absorption of MB by AL-CTS@MNPs. Subsequently, the adsorbent maintained a removal rate of >95 % after five adsorption-desorption cycles, demonstrating its excellent stability and recoverability. Ultimately, the prepared AL-CTS@MNPs illuminated good prospect on complex components dyes wastewater treatment.