RESUMO
The solution-derived non-stoichiometric nickel oxide (NiOx) is a promising hole-injecting material for stable quantum dot light-emitting diodes (QLEDs). However, the carrier imbalance due to the misalignment of energy levels between the NiOx and polymeric hole-transporting layers (HTLs) curtails the device efficiency. In this study, the modification of the NiOx surface is investigated using either 3-cyanobenzoic acid (3-CN-BA) or 4-cyanobenzoic acid (4-CN-BA) in the QLED fabrication. Morphological and electrical analyses revealed that both 4-CN-BA and 3-CN-BA can enhance the work function of NiOx, reduce the oxygen vacancies on the NiOx surface, and facilitate a uniform morphology for subsequent HTL layers. Moreover, it is found that the binding configurations of dipole molecules as a function of the substitution position of the tail group significantly impact the work function of underlying layers. When integrated in QLEDs, the modification layers resulted in a significant improvement in the electroluminescent efficiency due to the enhancement of energy level alignment and charge balance within the devices. Specifically, QLEDs incorporating 4-CN-BA achieved a champion external quantum efficiency (EQE) of 20.34%, which is a 1.8X improvement in comparison with that of the devices utilizing unmodified NiOx (7.28%). Moreover, QLEDs with 4-CN-BA and 3-CN-BA modifications exhibited prolonged operational lifetimes, indicating potential for practical applications.
RESUMO
The growing demand for wearable and attachable displays has sparked significant interest in flexible quantum-dot light-emitting diodes (QLEDs). However, the challenges of fabricating and operating QLEDs on flexible substrates persist due to the lack of stable and low-temperature processable charge-injection/-transporting layers with aligned energy levels. In this study, we utilized NiOx nanoparticles that are compatible with flexible substrates as a hole-injection layer (HIL). To enhance the work function of the NiOx HIL, we introduced a self-assembled dipole modifier called 4-(trifluoromethyl)benzoic acid (4-CF3-BA) onto the surface of the NiOx nanoparticles. The incorporation of the dipole molecules through adsorption treatment has significantly changed the wettability and electronic characteristics of NiOx nanoparticles, resulting in the formation of NiO(OH) at the interface and a shift in vacuum level. The alteration of surface electronic states of the NiOx nanoparticles not only improves the carrier balance by reducing the hole injection barrier but also prevents exciton quenching by passivating defects in the film. Consequently, the NiOx-based red QLEDs with interfacial modification demonstrate a maximum current efficiency of 16.1 cd/A and a peak external quantum efficiency of 10.3%. This represents a nearly twofold efficiency enhancement compared to control devices. The mild fabrication requirements and low annealing temperatures suggest potential applications of dipole molecule-modified NiOx nanoparticles in flexible optoelectronic devices.