RESUMO
Potassium-ion hybrid capacitors (PIHC) are considered as ideal large-scale rechargeable energy storage devices due to their low-cost, high-power density and environmental protection. However, a low energy density is the main factor restricting the practical application of PIHC. The interface is formed on the surface of electrode material of PIHC through strong correlation to construct heterojunction, which can significantly improve the performance of ion energy storage. However, how to reveal the influence of the interfacial state of the heterojunction on the adsorption and electron transmission of energy storage ions at the atomic level is still one of the key scientific problems in this field. In this work, metal ion intercalation and microwave-assisted in-situ etching are used to construct the Hexagon MXene Ti3C2 heterojunction with TiOHO strong correlation. At the interface of heterojunction, TiOHO highway for electron transmission is developed to improve the rate performance of PIHC. Through experimental and theoretical calculation, the optimum adsorption position and maximum adsorption amount of potassium-ion at the single interface of heterojunction are obtained, and the specific energy density of PIHC is increased. This lays a foundation for the practical application of high-performance soft-package PIHC.